PERILAKU KOROSI TITANIUM DALAM LARUTAN MODIFIKASI SALIVA BUATAN UNTUK APLIKASI ORTODONTIK | Ardhy | Jurnal MEKANIKAL 5264 17239 1 PB
Bebas
9
0
0
Teks penuh
Gambar
![Gambar 2. Spesimen dimasukkan ke dalam larutan saliva buatan (pH asam)](https://thumb-ap.123doks.com/thumbv2/123dok/883230.823908/4.595.367.478.504.693/gambar-spesimen-dimasukkan-larutan-saliva-buatan-ph-asam.webp)
![Tabel 3. Laju korosi spesimen uji (mm/y)](https://thumb-ap.123doks.com/thumbv2/123dok/883230.823908/5.595.104.267.608.730/tabel-laju-korosi-spesimen-uji-mm-y.webp)
![Tabel 5. Perbandingan nilai kekerasan (HVN)](https://thumb-ap.123doks.com/thumbv2/123dok/883230.823908/6.595.321.544.68.333/tabel-perbandingan-nilai-kekerasan-hvn.webp)
![Gambar 8. Struktur mikro Cp Ti; 0 jam, 1 jam, 10 ja, 100 jam, 1000 jam.](https://thumb-ap.123doks.com/thumbv2/123dok/883230.823908/7.595.331.526.371.546/gambar-struktur-mikro-cp-ti-jam-jam-jam.webp)