These results refer only to the materials received for testing purposes. They do not imply any warranty. Usage should be suited to local conditions and the materials employed. Any proprietary rights should be respected. All rights reserved.
TEST REPORT
PT Wacker Chemicals Indonesia KawasanPergudangan Taman Tekno BSD CitySektor XIUnit H-3 No. 28 B, Tangerang Selatan
Indonesia
Sample Plaster
Customer
PT Sumber Inti Perkasa Pembangunan Komplek pergudangan dan industry Safe n Lock. Block V2 no. 3318 Sidoarjo-Indonesia
Date 2nd March 2022
Tested by Jakarta Technical Center
1. Introduction
• Plaster samples received from Eco Mortar (PT Sumber Inti Perkasa Pembangunan) was tested per EN 1015-11 and EN 1015-12. The tests results were summarizedin thetablegiven below.
2. Test Results
Project no
Customer Name PT Sumber Inti Perkasa Pembangunan
Sample Name Plaster
Notes
Sample Plaster 100
Walocel 40000 PFV As informed by cus-
tomer
Vinnapas 4115 N As informed by cus-
tomer
Water Demand 18
Workability Good
(Standard Plaster)
Tensile Adhesion Strength According to EN 1015-12 - 2 mm thickness
Standard Condition 28d SC
Mean value (N/mm2) 0.22 Standard deviation
(N/mm2) 0.06
Failure pattern CFA
Heat Ageing
14d SC + 14d 70deg C + 1d SC
Mean value (N/mm2) 0.22 Standard deviation
(N/mm2) 0.06
Failure pattern CFA
Page 2 of 3
These results refer only to the materials received for testing purposes. They do not imply any warranty. Usage should be suited to local conditions and the materials employed. Any proprietary rights should be respected. All rights reserved.
Project no JAKTC 0145
Customer Name PT Sumber Inti Perkasa Pembangunan
Sample Name Plaster
Flexural and Compressive, According to EN 1015-11 - 28d S.C
Flexural Strength 40x40x160 mm
Mean value (N/mm2) 1.73 Standard deviation
(N/mm2) 0.19
Compressive Strength 40x40 mm
Mean value (N/mm2) 2.82 Standard deviation
(N/mm2) 0.12
SC: 23°C, 50 % Relative humidity, d = days
3. Pictures
4. Comments
• The workability of Eco Mortar Plaster at the water demand of 18% was found to be good.
• Tensile adhesion strength after 28d Standard Condition (SC) (SC: 23°C, 50% relative humidity) was found to be 0.22 N/mm2.
• Tensile adhesion strength after heat ageing (14d SC+14d 70ºC+1d SC) was found to be 0.22 N/mm2.
Standard Condition Heat Ageing Condition
Page 3 of 3
These results refer only to the materials received for testing purposes. They do not imply any warranty. Usage should be suited to local conditions and the materials employed. Any proprietary rights should be respected. All rights reserved.
• Flexural and compressive strength was found to be 1.73 N/mm2 and 2.82 N/mm2 re- spectively.