CNT/GT was dispersed in the binder and deposited on the SS sheet substrate using the doctor blade method and drying at a certain temperature. CNT/GT (mass composition 1:1) was dispersed in the binder with a stirrer for 10 min. The XRD patterns of the CNT/GT and CNT/GT/ZnO-300 composites can be found in Figure 1 .
Figure 1(b) shows the XRD pattern of the CNT/GT/ZnO composite with ZnO coating temperature of 300°C. SEM images of surface morphology and cross section of (a) CNT/GT and (b) CNT/GT/ZnO-300 composites on SS sheet substrate. It can be attributed to the overlap between CNT/GT and 4 μm thick ZnO layers.
Thickness of the ZnO over CNT/GT increases leading to the formation of clusters that block the pores in the electrode [17]. However, there is a decrease in capacitance of the CNT/GT/ZnO-300 sample in the scan rate from 20 to 200 mV/s. Overall, the addition of ZnO increases the capacitance value which was the highest value achieved in CNT/GT/ZnO-300.
The relatively higher capacitance in the CNT/GT/ZnO-300 sample was caused by the effect of the small crystallite size of ZnO. The temperature of 300 °C is the best temperature for drying ZnO material on the surface of CNT/GT. The performance of CNT/GT/ZnO electrodes was found to be dependent on the drying temperature of the ZnO material.
Materials Science Forum
SJR is a size-independent prestige indicator that ranks journals according to their 'average prestige per article'. SJR is a measure of journal scientific impact that takes into account both the number of citations a journal receives and the importance or reputation of the journals from which those citations come. It measures the scientific impact of the average journal article. expresses how central to the global This indicator counts the number of citations received by papers from a journal and divides them by the total number of papers published in that journal.
The graph shows the evolution of the average number of times that documents published in a journal in the past two, three and four years have been cited in the current year. Evolution of the total number of journal citations and self-citations received by a journal's published papers over the previous three years. Journal Self-citation is defined as the number of citations from a journal citing an article to articles published in the same journal.
Development of the number of total citations per document and external citations per document (ie, self-citations from journal removed) received by a journal's published documents during the previous three years. External citations are calculated by subtracting the number of self-citations from the total number of citations received by the journal's documents. International Collaboration stands for the articles produced by researchers from several countries.
The graph shows the proportion of a journal's documents signed by researchers from more than one country; it includes more than one country address. Not every article in a journal is considered primary research and therefore "citable". This graph shows the ratio of a journal's articles including substantial research (research articles, conference papers and reviews) in three year windows vs. Proportion of a journal's items, grouped over three-year windows, that were cited at least once vs.
Main Themes
Advanced Materials Research QiR 15
Abstract: To obtain specific properties in commercial and engineering applications, PP materials are often combined with additives. Health state estimation of lithium-ion batteries based on combination of Gaussian distribution data and least squares support vector machine regression. Abstract: Microwave absorption characteristics of a bilayer of barium hexaferrite attached to silica by a composition based on ..more.
E ect of the rare earth oxide impurities on the physical and thermal properties of CeGdO (GDC) composite. Authors: Jarot Raharjo, Damisih, Masmui, Ade Utami Hapsari, Asep Riswoko, Mochamad Setyadji, Suyanti, Maria Veronica Purwani Abstract: Observation of the effects of rare earth impurities on the properties of Ce Gd O (GDC) composite electrolyte has been . .more. Abstract: A simple method has been developed to fabricate carbon nanotube/graphite/zinc oxide (CNT/GT/ZnO) composite on SS foil ...more.
Hydrogen recovery from hydrogen-methane gas mixture using Palm Shell-based bioadsorbing activated carbon. Abstract: The purpose of the study is to obtain a suitable adsorbent to be used for the purification of hydrogen from hydrogen-methane gas ... more. E ect of Sub Zero treatment on microstructures, mechanical properties and dimensional stability of AISI D2 cold tool steel.
Abstract: AISI D2 tool steel has become an important material in industry, especially for mold and die makers, and is also used for cutting tools.
ISSN: 1662-9752
Periodicals
University of Newcastle, PRC for Geotechnical Science and Engineering, School of Engineering; University Drive, Callaghan, Australia, NSW 2308;. Hong Kong University of Science and Technology, Department of Chemical and Biomolecular Engineering, Clear Water Bay; Kowloon, China;. AGH University of Science and Technology, Faculty of Materials Science and Ceramics, Department of Physical Chemistry and Modeling of Processes and Surface Engineering; already
2 684 Cahyo Budiyantoro Influence of Nano Fillers on Thermal and Mechanical Properties of PP. An analysis of the effect of the electrolyte resistivity on the geometric properties (i.e., pore diameter and pore density) of anodic alumina (AAO) films prepared by single-step anodization. The role of Sr and TiB on mechanical properties of aluminum 6061 composite produced through stir casting method.
Mechanical Properties of Al2O3 Reinforced Aluminum A356 with Grain Refiner Al-5Ti-1B, Manufactured by Stir Casting Method. Effect of cold rolling and annealing temperature on the recrystallization and mechanical properties of Al-4.7Zn-1.8Mg (wt%) alloy produced by pinch casting. Effect of casting temperature, T4 and T6 heat treatment on tensile strength of Al-5.9Cu-1.9Mg alloy.
Flux Coating Effect of SMAW 308L Electrode on Its Mechanical Properties and Corrosion Resistance for Cryogenic Application. Effect of sub-zero treatment on microstructures, mechanical properties and dimensional stability of AISI D2 cold work tool steel. Optimization of the substrate preheating process to the mechanical properties of cobalt-based alloy coating on alloy and carbon steel with high velocity oxygen fuel (HVOF) method.
Raman Spectroscopy Study, Magnetic and Microwave Absorbing Properties of Modified Barium Strontium Monoferrite Ba(1-x)Sr(x)Fe2O4. Effect of structural transition on magnetic properties of doped LaMnO3 nanopowders characterized by Raman spectroscopy. Effect of SiC and sintering temperature variations on the characterization of Fe-clad MgB2 supergel wires.
Effect of different precursors and solvents on the characteristics of fluorine-doped tin oxide (FTO) conducting glass fabricated by ultrasonic spray pyrolysis. Effect of rare earth oxide impurities on physical and thermal properties of Ce1-yGd1-xO2-1 (GDC) IT-SOFC composite electrolytes.