PENGARUH TEKANAN DAN PENAMBAHAN Cu
TERHADAP KEKERASAN HASIL CORAN ALUMINIUM PADUAN PADA PROSES SQUEEZE CASTING
SKRIPSI Diajukan Kepada :
UNIVERSITAS MUHAMMADIYAH MALANG
Untuk Memenuhi Syarat Memperoleh Gelar Sarjana (S1) Teknik Mesin Program Strata Satu (S-1) Jurusan Teknik Mesin
AHMAD THOLABA ILMI NIM: 201110120311060
JURUSAN TEKNIK MESIN FAKULTAS TEKNIK
UNIVERSITAS MUHAMMADIYAH MALANG 2016
LEMBAR PENGESAHAN SKRIPSI
Pengaruh Tekanan dan Penambahan Cu Terhadap Kekerasan Hasil
Coran Aluminium Paduan Pada Proses Squeeze Casting
Diajukan Kepada :
UNIVERSITAS MUHAMMADIYAH MALANG
Memenuhi Syarat Memperoleh Gelar Sarjana (S1) Teknik Mesin
Program Strata Satu (S-1) Jurusan Teknik Mesin
Oleh:
Ahmad Tholaba Ilmi
201110120311060
Diterima dan Disetujui pada tanggal 22 Juli 2016 Dosen Pembimbing I
Iis Siti A., ST., MT., PhD
NIP.108.1503.0572
Dosen Pembimbing II
Drs. Moh. Jufri ST., MT
NIP.196311101990101001
Mengetahui,
Ketua Jurusan Teknik Mesin Universitas Muhammdiyha Malang
Ir. Daryono, MT NIP.108.8909.0124
UNIVERSITAS MUHAMMADIYAH MALANG FAKULTAS TEKNIK JURUSAN TEKNIK MESIN
Jl. Raya Tlogomas No. 246 Telp. (0341) 464318 – 21 Psw. 127 Fax. (0341) 460782 Malang 65144
LEMBAR KONSULTASI / ASISTENSI
Nama : AHMAD THOLABA ILMI
No. Induk : 201110120311060
Terhadap Kekerasan Hasil Coran Aluminium Paduan Pada Proses Squeeze Casting
Pembimbing I : Iis Siti A., ST., MT., PhD. Pembimbing II : Drs. Moh. Jufri ST., MT
NO Tanggal URAIAN ASISTENSI TTD
1 15-10-2015 PENGAJUAN JUDUL SKRIPSI 2 15-10-2015 ACC JUDUL SKRIPSI
3 19-10-2015 KONSULTASI BAB I 4 22-10-2015 ACC BAB I
5 23-10-2015 KONSULTASI BAB II 6 05-11-2015 ACC BAB II
7 09-11-2015 KONSULTASI BAB III 8 27-11-2015 ACC BAB III
9 03-11-2015 KONSULTASI BAB IV
10 07-01-2016 ACC BAB IV DAN SEMINAR HASIL Mengetahui,
Ketua Jurusan Teknik Mesin
Ir. Daryono, MT NIP.108.8909.0124
Malang, 22 Januari 2016
Dosen Pembimbing I
Iis Siti A., ST., MT., PhD NIP.108.1503.0572
UNIVERSITAS MUHAMMADIYAH MALANG FAKULTAS TEKNIK JURUSAN TEKNIK MESIN
Jl. Raya Tlogomas No. 246 Telp. (0341) 464318 – 21 Psw. 127 Fax. (0341) 460782 Malang 65144
LEMBAR KONSULTASI / ASISTENSI
Nama : AHMAD THOLABA ILMI
No. Induk : 201110120311060
Judul : Pengaruh Tekanan dan Penambahan Cu
Terhadap Kekerasan Hasil Coran Aluminium Paduan Pada Proses Squeeze Casting
Pembimbing I : Iis Siti A., ST., MT., PhD. Pembimbing II : Drs. Moh. Jufri ST., MT.
NO Tanggal URAIAN ASISTENSI TTD
1 15-10-2015 PENGAJUAN JUDUL SKRIPSI 2 15-10-2015 ACC JUDUL SKRIPSI
3 19-10-2015 KONSULTASI BAB I 4 22-10-2015 ACC BAB I
5 23-10-2015 KONSULTASI BAB II 6 05-11-2015 ACC BAB II
7 09-11-2015 KONSULTASI BAB III 8 27-11-2015 ACC BAB III
9 03-11-2015 KONSULTASI BAB IV
10 07-01-2016 ACC BAB IV DAN SEMINAR HASIL
Mengetahui,
Ketua Jurusan Teknik Mesin
Ir. Daryono, MT NIP.108.8909.0124 Malang, 22 Januari 2016 Dosen Pembimbing II Drs. Moh. Jufri ST., MT NIP.196311101990101001 1
2 LEMBAR PERNYATAAN Yang bertanda tangan di bawah :
Nama : Ahmad Tholaba Ilmi
Nim : 201110120311060
Tempat / Tanggal Lahir : Gresik /16 Juni 1992
Jurusan : Teknik Mesin
Fakultas : Teknik
Instansi : Universitas Muhammadiyah Malang
Dengan ini menyatakan dengan sebenar-benarnya bahwa :
1. Tugas Akhir dengan Judul :
“Pengaruh Tekanan dan Penambahan Cu Terhadap Kekerasan Hasil Coran Aluminium Paduan Pada Proses Squeeze Casting “
Adalah hasil karya saya, dan dalam naskah tugas akhir ini tidak terdapat karya ilmiah yang pernah diajukan oleh orang lain untuk memperoleh gelar
akademik disuatu perguruan tinggi, dan tidak terdapat karya atau pendapat yang pernah ditulis atau diterbitkan oleh orang lain, baik sebagian atau keseluruhan, kecuali yang secara tertulis dikutip dalam naskah ini dan disebutkan dalam sumber kutipan dan daftar pustaka.
2. Apabila ternyata didalam naskah tugas akhir inbi dapat dibuktikan terdapat
unsur-unsur “PLAGIASI”, saya bersedia “TUGAS AKHIR INI DIGUGURKAN” dan “GELAR AKADEMIK YANG TELAH SAYA PEROLEH DIBATALKAN”,serta diproses sesuai ketentuan yang berlaku. Demikian surat pernyataan ini dibuat dengan sebenarnya untuk digunakan
sebagaimana mestinya.22 Januari 2016
Hormat,
ABSTRAK
Salah satu metode dalam proses pengecoran adalah pengecoran Squeeze
casting yang memanfaatkan keuntungan-keuntungan proses forging dan casting.
Berbagai produk komponen kendaraan dapat dihasilkan dari proses pengecoran ini,
seperti: steering, brake, Bagian-bagian suspense roda (velg), dan sebagainya.
Pengaruh tekanan pada proses ini menyebabkan butiran yang menjadi kecil, selain itu pengaruh penambahan Cu akan mengurangi penyerapan gas dan memperbaiki sifat mekaniknya. Oleh karena itu perlu diteliti lebih lanjut tentang pengaruh variasi tekanan dan penambahan Cu terhadap kekerasan hasil coran aluminium paduan. Variasi tekanan yang dipilih sebesar 100, 200, 300, 400 Bar. Sedangkan variasi kadar
Cu yang dipilih sebesar 2, 4, 6, 8 %, dengan temperature penuangan 7500C dan
temperature cetakan 4500C.
Percobaan dilakukan dengan melihat hasil uji kekerasan yang didapatkan pada setiap variasi tekanan dan variasi penambahan Cu. Selanjutnya dapat dilakukan pembahasan mengenai hubungan tekanan dan penambahan Cu serta interaksi terhadap angka kekerasan setiap variasi tersebut.
Dari hasil analisa dapat diketahui bahwa peningkatan variasi tekanan dan penambahan Cu berpengaruh terhadap kekerasan hasil coran aluminium paduan pada
proses squeeze casting. Kekerasan rata-rata tertinggi dapat pada tekanan 400 Bar dan
penambahan kadar Cu 8%, yaitu sbesar 205,31 VHN. Kata kunci : Tekanan, unsur Cu, Squeeze casting
ABSTRACK
Either the methods in the process of casting is the squeeze casting that utilizes the advantages of forging and casting process. Various vehicle components products can be produced from this casting process, such as: steering, brake, portions suspension, wheels (rims), etc. The effect of pressure on this process causes the grain that happens to be small, but it will reduce the effect of adding Cu gas absorption and improve its mechanical properties. Therefore, it needs to be studied further about the influence of pressure variations and additions to violence Cu aluminum alloy casting product. Preferred pressure variation of 100, 200, 300, 400 Bar. While the variation of Cu content is selected by 2, 4, 6, 8%, with temperature casting mold temperature of 750 0C and 450 0C.
The researh can by looking at the hardness test results obtained at each pressure variations and variations addition of Cu. Further discussion can be conducted regarding the relationship of pressure and the addition of Cu and interaction on any variation of the levels of violence.
From the analysis it can be seen that the increase of pressure variations and
the addition of Cu affect the hardness of aluminum alloy casting product on a squeeze casting process. Violence highest average can be at a pressure of 400 bar and the addition of Cu content of 8%, which is sbesar 205.31 VHN.
3 KATA PENGANTAR
Dengan memanjatkan puji dan syukur kehadirat Allah SWT, yang telah melimpahkan rohmat, taufik dan hidayah-nya pada penyusun sehingga dapat menyelasaikan Tugas akhir ini.
Didalam penyusun tugas akhir ini sering mengalami kesulitan dan hambatan, namun berkat bantuan dari semua pihak segala kesulitan itu bias dihadapi dan teratasi. Oleh karena itu sangat tepatlah bila penyusun pada kesempatan kali ini untuk menyampaikan terima kasih atas jasa baik yang selama ini penyusun terima, baik nasehat, petunjuk serta bimbingan dan saran yang berupa apapun sehingga penyusun dapat menyelesaikan Tugas akhir ini. Rasa terima kasih ini penyusun sampaikan kepada :
1. Bapak Sudarman, Ir. MT. Selaku Dekan Fakultas Teknik Universitas Muhammadiyah
Malang.
2. Bapak Ir. Daryono, MT. Selaku Ketua Jurusan Teknik Mesin Fakultas Teknik
Universitas Muhammadiyah Malang.
3. Bapak Iis Siti A., ST., MT., PhD. Selaku Dosen Pembimbing I yang telah
memberikan bimbingan serta arahan secara intensif selama penyusunan skripsi ini dilakukan.
4. Bapak Drs. Moh. Jufri ST., MT. Selaku Dosen Pembimbing II yang telah
memberikan masukan ide serta saran sehingga terselesaikannya skripsi ini.
5. Bapak Irkham ST., MT. Yang telah memberikan masukan ide dan saran selama
penyusunan skripsi ini dilakukan
6. Bapak/Ibu Dosen yang telah bersedia memberikan bantuan berupa bimbingan teoritis
secara langsung maupun tidak langsung.
7. Serta kedua orang tua yang selalu memberikan bantuan materi maupun non materi,
mendo`akan, mengingatkan akan pesan-pesannya yang tak akan terlupakan.
9. Ninin Krisinda yang selalu mendo’akan dan memberikan masukan selama pengerjaan skrips ini
10.Serta semua pihak yang belum tersebutkan, terima kasih banyak
Dalam penyusunan tugas akhir ini, penyusun menyadari bahwa masih banyak kekurangan dan kelemahan baik dalam penyusunan data maupun dalam pembahasannya. Oleh karena itu segala kritik dan saran yang sifatnya membangun sangat penyusun harapkan demi sempurnanya Tugas akhir ini.
Semoga Allah SWT memberikan balasan kepada semua pihak yang tersebut diatas dan penyusun berharap semoga Tugas akhir bermanfaat bagi penyusun dan pembaca.
Malang, 22 Januari 2016 Hormat.
DAFTAR ISI DAFTAR ISI
COVER ...
LEMBAR PENGESAHAN ... i
BERITA ACARA TUGAS AKHIR ... ii
LEMBAR PERNYATAAN ... iv
ABSTRAK ... v
KATA PENGANTAR ... vii
DAFTAR ISI ... ix
DAFTAR GAMBAR ... xi
DAFTAR TABEL ... xii
BAB I PENDAHULUAN ... 1 1.1 Latar Belakang ... 1 1.2 Rumusan Masalah ... 2 1.3 Batasan Masalah... 2 1.4 Tujuan Penelitian ... 3 1.5 Manfaat Penelitian ... 3
BAB II TINJAUAN PUSTAKA ... 4
2.1 Penelitian Sebelumnya ... 4
2.2 Pengecoran Logam ... 4
2.2.1 Pengecoran Dengan Cetakan Logam ... 5
2.2.2 Squeeze Casting ... 6
2.3 Peroses Pembekuan logam ... 8
2.3.1 Pertumbuhan Kristal ... 10
2.3.2 Pembekuan Logam Paduan... 12
2.3.3 Kurva Pendingin ... 13
2.3.4 Waktu Pembekuan ... 15
2.4 Aluminium ... 16
2.4.1 Aluminium Paduan ... 16
2.4.3 Sifat Umum Dari Berbagai Jenis Padan Aluminum ... 20
2.5 Tekanan ... 21
2.6 Kekerasan Bahan ... 22
2.7 Hipotesis ... 22
BAB III METODOLOGI PENELITIAN ... 23
3.1 Metode Penelitian... 23
3.2 Bahan Yang Digunakan ... 23
3.3 Alat Yang Digunakan ... 23
3.4 Variabel Pnelitian ... 24
3.5 Prosedur Penelitian... 24
3.7 Rancangan Penelitian ... 25
3.8 Diagram Alir Penelitan ... 27
BAB IV ANALISA DATA DAN PEMBAHASAN ... 28
4.1 Data Hasil Pengujian ... 28
4.2 Pembahasan ... 30
4.2.1 Pengaruh Tekanan Terhadap Kekerasan Terhadap Kekerasan ... 31
4.2.2 Pengaruh Kadar Cu Terhadap Kekerasan ... 32
4.2.3 Implementation Diagram(Deployment Diagram)... 34
BAB V PENUTUP ... 35
5.1 Kesimpulan ... 35
5.2 Saran ... 35
DAFTAR PUSTAKA ... 36 LAMPIRAN
DAFTAR GAMBAR
Gambar 2.1 Proses Squeeze Casting ... 7
Gambar 2.2 Ilustrasi Skematis Dari Permukaan Logam ... 9
Gambar 2.3 Ilustrasi Skematis Pembekuan Logam Pada Cetakan Bujur Sangkar .... 12
Gambar 2.4 Skematis Pendinginan dan Distribusi Temperatur Logam Paduan ... 13
Gambar 2.5 Kurva Pendingnan Logam Murni Atau Paduan Eutectoid ... 14
Gambar 2.6 Kurva Pendinginan Untuk Logam Paduan ... 15
Gambar 2.7 Diagram Fase Binary Al-Cu ... 21
Gambar 3.8 Diagram Alir Penelitian ... 27
Gambar 4.1 Hubungan tekanan terhadap kekerasan ... 29
DAFTAR TABEL
DAFTAR PUSTAKA
De Garmo, E. Paul, 1988. Materials and Processes in Manufacturing. Macmillan
Publishing Company: New York.
Vimala, Andi (2004) meneliti pengaruh temperatur penuangan dan penambahan
unsur Cu pada proses squeeze casting terhadap kekerasan coran aluminium
paduan.
Herman, Gita Novian (2014) meneliti pengaruh Komposisi Cu dan Variasi Tekanan Kompaksi Terhadap Densitas dan Kekerasan.
Kalpakjian, S., 1990. Manfacturing Engineering and Technology. Addison-Wesley
Publish Company: Massachusetts.
Sudia, Tata, 1995, Pengetahuan Bahan Teknik, P.T Pradnya Paramita: Jakarta