ORIGINAL PAPER
https://doi.org/10.1007/s10924-022-02595-y
fire retardant film, medical bag, safety glass/optically clear film and surface protection film [2].
With the aim to overcome the environmental concerns on the release of organic solvents from the utilization of traditional solvent borne polyurethane, the aqueous based counterpart, waterborne polyurethane (WPU) has been developed. There are several features that make WPU attractive. The most important features that offered by WPU is non-toxic and less pollution to the environment compared to the traditional solvent borne polyurethane due to the relatively lower volatile organic compound (VOC) content.
Moreover, WPU also possesses good adhesion and excel- lent rheological properties. Other features such as non-flam- mable, absence of external emulsifier and good behavior at low temperature further increase the comparability of WPU [3, 4]. Nonetheless, WPU is inferior to its solvent-based counterpart in terms of surface properties and chemical resistance, poor wettability and limited thermal, mechanical and electrolytic stability [3, 5, 6].
1. Introduction
Global plastic film market outlook shows increasing trend in recent year. According to the latest market research, the global plastic film and sheets market is forecasted to reach USD 157.5 billion by the year 2025 [1]. Among the poly- meric materials, polyurethane is one of the potential can- didates that can be used as the raw material for the plastic films. Few examples of the applications of polyurethane film are wound dressing (medical), adhesive coated product,
Jiun Hor Low jiunhor@gmail.com
1 School of Engineering, Faculty of Innovation and Technology, Taylor’s University, Lakeside Campus, No.1, Jalan Taylor’s, 47500 Subang Jaya, Selangor, Malaysia
2 Department of Polymer and Textile Engineering, Faculty of Engineering, Nnamdi Azikiwe University, Awka, Anambra
Abstract
With the aim to enhance the tensile properties and thermal stability of waterborne polyurethane (WPU) film, a comparative study was conducted to investigate the use of unfunctionalized lignin and 3-aminopropyltriethoxy silane functionalized lignin as natural reinforcing filler. The ultimate tensile strength of the WPU film that filled with 0.5 wt% functionalized lignin was found elevated by 9% compared to the unfunctionalized lignin, which was only increased by 0.3%. The func- tionalized lignin-filled WPU films also becomes more flexible and possess higher deformation resistance (lower Young’s modulus and higher elongation at break) compared to the one filled with unfunctionalized lignin. In addition, the func- tionalized lignin is proven to reinforce the fabricated bio-composite films without significantly compromising their thermal stability, since the initial degradation temperature (296.79 °C) is comparable to the pristine WPU film (297.40 °C). The Fourier-transform infrared and morphological analyses confirm the formation of extra carbamate, urea and hydrogen bonds between the functionalized lignin and WPU is the main reason for the functionalized lignin to reinforce the fabricated films without significantly compromising their thermal stability. Ultimately, the current findings and proposed chemical reaction between the functionalized lignin and WPU, also serve as a guideline to facilitate the future design and development of other functionalized lignin-based products.
Keywords Bio-composite film · Waterborne polyurethane · Lignin · 3-aminopropyltriethoxy silane · Properties enhancement
Accepted: 12 September 2022
© The Author(s), under exclusive licence to Springer Science+Business Media, LLC, part of Springer Nature 2022
Properties Enhancement of Waterborne Polyurethane Bio-composite Films with 3-aminopropyltriethoxy Silane Functionalized Lignin
Qi Yuan Ng1 · Jiun Hor Low1 · Ming Meng Pang1 · Christopher Igwe Idumah2
Filler incorporation is one of the methods which can be applied to tackle the shortcomings of WPU to produce the end-products with the desired specifications. The utiliza- tion of green plant-derived bio-polymers as filler has gained much attention due to the environmental and economic rea- sons. For instance, rice straw [7, 8], kenaf fiber [9], sago waste [10, 11], corn starch [12], durian skin fiber [13], pine- apple leaf fiber [14], microcrystalline cellulose [15], corn waste [16], wood chips [17], kapok [18], tree pruning waste [19] and oil palm mesocarp [20], these green plant-derived bio-polymers have demonstrated their potential to reinforce the properties of the developed polymer bio-composites with or without subjecting to the functionalization process by using a coupling agent. Some of these bio-polymers have even been proven can be used as the substituents to produce different eco-friendly end-products, for instance, tree-free papers [21–25], soil cover [26], textile [27] and nanowires [28]. Lignin is the second most abundant green plant-derived bio-polymer on Earth which is exceeded only by cellulose [29]. Lignin can be extracted through lignocellulose separa- tion process. One of the biggest producers of lignin is paper and pulp industry whereby approximately 50 million ton of lignin is being produced annually [30, 31]. Owing to its low cost and ample natural availability, lignin is recognized as a suitable adsorbent material for adsorption process to remove pollutants [32]. In fact, lignin is a macromolecule which is made up of three different types of cinnamyl alco- hols (monolignols), namely p-coumaryl alcohol, coniferyl alcohol and sinapyl alcohol. Thus, the abundant functional groups that can be found in these components have made lignin to be a reactive bio-polymer which is not only can be used for the development of derma products, drug delivery systems, engineering devices [33], but also holds potential to reinforce the fabricated polymer bio-composites without the use of coupling agent. It is even to be expected that the reinforcing effect can be intensified when the lignin is fur- ther functionalized by using the adaptive coupling agent.
With the aforementioned, the main aim of this study is to investigate and report the potential use of lignin as a reinforcing filler for the development of WPU films with enhanced tensile properties without compromising their thermal stability. Lignin recovered from the Kraft pulping process, which is also known as Kraft lignin, was utilized in this study since the Kraft process is the most common pulping method and it contributes 85% of the total lignin production in the world [34, 35]. A comparative study was conducted to discuss the reinforcing effect of lignin, with and without subjecting to the functionalization process by using 3-aminopropyltriethoxy silane (APTES) as the functional- izing agent, on the performance of the fabricated WPU bio- composite films. In the present study, APTES was selected as the functionalizing agent since it was expected that the
interaction between the hydroxyl groups of APTES (upon hydrolysis) and lignin would provide an extra functional group (amino group) to the lignin, which makes the lignin becomes more compatible with WPU, and thus, the per- formance of the fabricated bio-composite films. Moreover, the investigation of the tensile properties, thermal stability, Fourier-transform infrared spectroscopy (FTIR) and surface morphology was also expected to provide insight into the extent of lignin and functionalized lignin on the properties enhancement of WPU films. These findings are not only fill- ing up the knowledge gaps, but also serve as a guideline for the development of lignin-based green products.
2. Materials and Methods
2.1 MaterialsThe aliphatic WPU dispersion, which was utilized as the polymer matrix of the fabricated films, was synthesized based on the use of a proprietary method. Kraft lignin with an average particle size of 29.45 μm (CAS number: 8068- 05-1) was purchased from Sigma Aldrich 3-aminopropyl- triethoxy silane 99% (APTES, CAS number: 919-30-2) was purchased from Fisher Scientific.
2.2 Functionalization of Lignin
To prepare the medium of functionalization process, 2 wt% of APTES was hydrolyzed by using 100 mL of dis- tilled water. Afterwards, the lignin powder was added into the medium and stirred at 200 rpm (room temperature) for 40 min. The functionalized lignin was then filtered through a filter paper and fully dried in an oven at 80 °C. The dried and functionalized lignin was then grounded by using a mortar and pestle before storing. The APTES functional- ized lignin is termed as functionalized lignin throughout the works.
2.3 Fabrication of WPU Films
The prepared WPU dispersion was mixed with lignin or functionalized lignin at different proportion (0, 0.5, 1.0, 1.5 and 2.0 wt%) under magnetic stirring condition at a speed of 850 rpm for 30 min. The mixing process was carried out at room temperature without external heating. After the mixing process, small amount of the stirred solution was immediately poured onto a piece of release paper with the dimension of 28.5 cm x 22 cm. A 100 μm coating bar was used to spread the mixture on the release paper. After the spreading process, the mixture was air dried at room tem- perature to produce the WPU films.
2.4 Tensile Properties
The tensile properties (ultimate tensile strength, Young’s modulus and elongation at break) of the pristine WPU film, lignin-filled WPU bio-composite films and functionalized lignin-filled WPU bio-composite films were determined based on the ASTM D 882. The evaluation was conducted by using a universal tensile machine (Instron Model 5969).
According to ASTM D 882, the rectangular shaped samples with dimension 100 mm x 10 mm x 0.1 mm and gauge length of 50 mm were tested under a crosshead speed of 500 mm/
min at room temperature. The average value of 5 horizontal cut samples and 5 vertical cut samples was reported for each formulation.
2.5 Thermal Stability
The thermal stability of lignin, functionalized lignin, pris- tine WPU film, lignin-filled WPU bio-composite films and functionalized lignin-filled WPU bio-composite films were investigated by using a thermogravimetric analyzer (Model TGA 8000 from Perkin Elmer). The sample with a mass of 5 mg was placed in a ceramic crucible of the thermo- gravimetric analyzer and heated from room temperature to 700 °C at a heating rate of 10 °C/min with nitrogen purging at 20 mL/min.
2.6 Fourier-transform Infrared Spectroscopy (FTIR) FTIR spectroscopy was carried out by using an attenuated total reflectance (ATR)-FTIR spectrometer (Model Spec- trum 100 from Perkin Elmer) to identify the chemical inter- action between the lignin or functionalized lignin with the WPU. The spectra were obtained in the frequency range of 4000 cm− 1 to 525 cm− 1 at a resolution of 4 cm− 1 and accu- mulations 16 scans. The peak assignments were done based on the works reported by other scholars [36–41].
2.7 Scanning Electron Microscopy
Scanning electron microscopy was adopted to examine the dispersion of lignin and functionalized lignin in the fabri- cated WPU bio-composite films. The samples were coated with a thin layer of platinum using an auto fine coater (Model Q150R S from Quorum) before the surface exami- nation. After that, the surface morphology of the samples was examined by using a variable pressure scanning elec- tron microscope (Model S-3400 N from Hitachi) at 30X, 200X, 1000X and 2000X magnification with a voltage of 10 kV and pressure of 90 Pa.
3. Results and Discussion
3.1 Tensile PropertiesFigure 1 shows the ultimate tensile strength of WPU films filled with lignin or functionalized lignin. As depicted in Fig. 1, the ultimate tensile strength of pristine WPU is 8.05 MPa, which is mainly contributed by the polyurethane backbones through the combination of polyisocyanates and polyols in the films. With the incorporation of lignin, the highest ultimate tensile strength (8.07 MPa) is achieved when 0.5 wt% of lignin was incorporated into WPU film. In other words, the ultimate tensile strength of the WPU film is increased by 20 kPa. However, beyond that, adverse effect on the ultimate tensile strength of the bio-composite films is observed. These observations indicate that the ultimate tensile strength of the WPU films can be enhanced through the incorporation of lignin, up to 0.5 wt%. The increase in ultimate tensile strength might be due to the formation of the lignin-WPU interaction. Beyond 0.5 wt%, the ulti- mate tensile strength of the bio-composite film decreases with the increase in lignin loading. This phenomenon can be explained by the agglomeration of lignin particles at
Fig. 1 Ultimate tensile strength of lignin and functionalized lignin- filled WPU films
and fabrication process, the reinforcing effect of the func- tionalized lignin in this work is slightly higher compared to the polylactic acid composites fabricated by Zhu and co- workers [42], whereby the tensile strength is increased by 3.2% using the similar APTES-functionalized lignin.
Based on Fig. 2, an increase in Young’s modulus of WPU films is observed with the incorporation of lignin as natu- ral reinforcing filler. The increase in Young’s modulus is mainly attributed to the complex structure of lignin, which restrict the mobility of WPU polymer chains and provide greater stiffness to the bio-composite films. The ability of lignin in providing greater stiffness is further supported by the decrease in elongation at break (Fig. 3). Similar observa- tion is also observed by the scholars in Thailand [43], where the kraft lignin acted as stiffener in thermoplastic starch polymer matrix.
In contrast, the functionalized lignin-filled WPU bio- composite film has lower Young’s modulus (Fig. 2) and higher elongation at break (Fig. 3) compared to the lignin- filled WPU bio-composite film. The improvement in the interfacial adhesion contributes to the enhancement in the elongation at break. Better interfacial adhesion result in the reduction of stress concentration, which leads to the increase in the elongation of the fabricated bio-composite high loading amount. The agglomeration of lignin particle
decreases the total surface area of the filler which resulted in the reduction of tensile strength due to the less efficient stress transfer mechanism. This argument can be supported by the measurement of filler size, which would be discussed in Sect. 3.4 (scanning electron microscopic analysis).
On the other hand, the ultimate tensile strength of the WPU bio-composite films that filled with the functionalized lignin is higher than those reinforced with unfunctionalized lignin, regardless of the lignin loading. The enhancement in the ultimate tensile strength is attributed to the function- alization process, which confers the additional capabilities by changing the surface chemistry of the lignin to improve the surface interaction, and thus, the interfacial adhesion and contact with WPU. This argument can be supported by the FTIR spectroscopic analysis and scanning electron micrographic analysis in Sect. 3.3 and 3.4. A better interfa- cial adhesion helps to achieve better stress distribution on the bio-composite films when the external force is applied, which then leads to the increase in ultimate tensile strength.
With the incorporation of 0.5 wt% of functionalized lignin, the resulting bio-composite film is able to achieve 9% higher in ultimate tensile strength compared to the pristine WPU films (8.05 MPa). By ignoring the different functionalization
Fig. 3 Elongation at break of lignin and functionalized lignin- filled WPU films
Fig. 2 Young’s modulus of lignin and functionalized lignin-filled WPU films
between the tensile properties of vertical and horizontal cut samples have given rise to the broad standard deviation for the reported findings.
3.2 Thermal Stability
The thermal stability of lignin, functionalized lignin as well as the WPU films filled with lignin or functionalized lignin was investigated by using a thermogravimetric ana- lyzer. Based on the TGA thermograms, the initial degrada- tion temperature is identified and tabulated in Tables 1 and 2. As shown, the thermal stability of the WPU films filled with lignin is found to be lower than the pristine one. It is observed that the initial degradation temperature of the fabricated bio-composite films decreases with the increase in lignin loading. This is attributed to the lignin has lower initial degradation temperature (253.94 °C) as compared to WPU (297.40 °C). Owing to this reason, the addition of lignin weakens the thermal stability of the WPU film. On the other hand, the functionalized lignin filled-WPU bio- composite films exhibit better thermal stability compared to the one filled with the unfunctionalized lignin. This phe- nomenon is attributed to the improved surface interaction and bonding formation between the APTES functional- ized lignin and WPU. Theoretically, the APTES serves as a coupling agent to promote the interaction between the lignin and WPU through the formation of carbamate, urea and hydrogen bonds. These intermolecular bonds increase the amount of thermal energy required to break the bonds, and thus, enhance the thermal stability of the fabricated bio-composite films. Moreover, the improved surface inter- action between the lignin and WPU through the APTES functionalization process also reduces the voids in the bio- composite films to hinder the heat diffusion, and thus, delay the thermal degradation. For this reason, the incorporation of APTES functionalized lignin can reinforce the fabricated bio-composite films without significantly decreasing their thermal stability. These arguments are supported by the temperature at the maximum degradation rate (Tmax) of the fabricated films (Table 2). Basically, the Tmax of the func- tionalized lignin filled-WPU bio-composite films is higher than the one prepared with unfunctionalized lignin. The ele- vation of the Tmax further confirms the massive weight loss of the bio-composite films took place at higher temperature.
These phenomena imply that the functionalization process is not only enhance the ultimate tensile strength and flexibil- ity of the resulting films, but it also improves their thermal stability and make them only slightly lower compared to the pristine WPU films.
film. In other words, the WPU films exhibit better deforma- tion when functionalized lignin is used as the reinforcing filler. The characteristic is in line with the works reported by Lv and co-workers [44], since the similar observation was observed when the bio-composite was prepared based on the functionalized wood flour.
As shown in Figs. 1 and 2., the standard deviation reflects the fluctuation range of the ultimate tensile strength and Young’s modulus of the bio-composite films is broad. This phenomenon can be rationalized by the polymer chains ori- entation in the films during the fabrication process. Although the casting method was adopted in this research, but the WPU was manually spread over the release papers with the aid of a coating bar to form the bio-composite films. Owing to the force applied during the manual spreading process, the WPU was stretched top-down over the release papers in one direction. Consequently, the WPU polymer chains were aligned in that direction to give rise to the anisotro- pic behavior in the fabricated films. According to Spragg [45], the mechanical properties of polymer films depend strongly on the orientation of the polymer chains. Basically, the mechanical properties are greater in a direction paral- lel to the polymer chains than in directions normal to them.
Owing to the tensile properties of the WPU bio-composite films were evaluated based on the method recommended by ASTM D 882, the average value of 5 vertical cut samples (parallel to the principal axis of anisotropy) and 5 horizontal cut samples (normal to the principal axis of anisotropy) is used as the representative to represent the performance of each formulation. For this reason, the pronounced difference
Table 1 Initial degradation temperature of lignin and functionalized lignin
Initial Degradation
Temperature (°C) Temperature at the maxi- mum degrada- tion rate (°C)
Lignin 253.94 337.10
Functionalized Lignin 262.71 357.97
Table 2 Initial degradation temperature of lignin and functionalized lignin-filled WPU films
Lignin-filled
WPU Films Functionalized Lignin-filled WPU Films
Lignin Loading (wt%)
Initial Degradation Temperature (°C)
Tempera- ture at the maximum degrada- tion rate (°C)
Initial Degrada- tion Temperature (°C)
Tempera- ture at the maximum degrada- tion rate (°C)
0 297.40 386.96 297.40 386.96
0.5 292.45 357.39 296.79 365.22
1.0 291.86 355.94 294.19 360.87
1.5 290.95 355.07 291.62 363.57
2.0 285.59 356.52 289.23 354.49
rise to the absorption at the frequencies of 1234.9 cm− 1 (Si-CH2CH2CH2), 1170.5 cm− 1 (Si-O-C), 1034.4 cm− 1 (Si-O-C) and 778.3 cm− 1 (C-O of Si-O-C). The detec- tion of Si-O-C confirms that extra carbamate bonds were formed in the fabricated film via the chemical reaction between the hydroxyl groups (Si-OH) of silane and iso- cyanate (N = C = O) of WPU. In addition, the interaction between the amine group (-NH2) of silane and isocyanate (N = C = O) of WPU is also observed through the forma- tion of urea bond (N-C-N) at frequency of 1461.1 cm− 1. The formation of extra carbamate and urea bonds are sup- ported by the increasing peak intensity at 1531.0 cm− 1 and 1310.0 cm− 1, which are attributed to the -C(= O)-NHR bend and stretching, since the -C(= O)-NHR can only be found in carbamate and urea bonds. On the other hand, the increase in the peak intensity at 3303.8 cm− 1 also suggests that the functionalized lignin has improved the formation of hydro- gen bonding with the WPU polymer chains, which in turns, accompanied by the reduction in absorption band of the free and unassociated hydroxyl groups (-OH) at 3781 cm− 1. In other words, the Fourier-transform infrared spectroscopic analysis has confirmed that the functionalized lignin possess higher reactivity to interact with the WPU. The functional- ized lignin promotes the formation of carbamate, urea, and hydrogen bonds, which increase the thermal stability as well as to facilitate the stress distribution on the bio-composite film, as reflected by the increase of initial degradation tem- perature and ultimate tensile strength reported in Sect. 3.2 and 3.1.
The identified chemical bonding that involve among the lignin, APTES and WPU in the bio-composite film has also enabled the coupling reaction to be proposed, as shown in Fig. 5.
3.4 Scanning Electron Microscopic Analysis
The surface morphology of the lignin, functionalized lignin, pristine WPU film as well as the bio-composite films was examined and discussed in this section. The microstructure of lignin is affected after the APTES functionalization pro- cess, as shown in Fig. 6. The surface of the functionalized lignin (Fig. 6(b)) is rougher compared to the unfunctional- ized one (Fig. 6(a)) due to the interaction with the APTES in the functionalization process. This observation further supports that the lignin particles is successfully activated by using APTES, and thus, improve the surface interaction with the WPU.
As shown in Fig. 7 (a), the surface morphology of the pristine WPU film is homogenous which indicates the good surface interaction between hard segments and soft seg- ments of the WPU. Based on Fig. 7 (b) and (c), it can be observed that the dispersion of lignin in 0.5 wt% lignin-filled 3.3 Fourier-transform Infrared Spectroscopic
Analysis
Figure 4 shows the Fourier-transform infrared spectra for the pristine WPU film as well as the films filled with lig- nin and functionalized lignin. As reflected by the spectra, the C-H stretching and C-O-C stretching of the WPU poly- mer chains were recorded at 2942.9 cm− 1 and 1234.9 cm− 1, respectively. For the pristine WPU film and lignin-filled WPU bio-composite film, the formation of carbamate (ure- thane) bond can be observed through the absorption peak at 1711.2 cm− 1 and 1531.0 cm− 1. These absorption peaks are attributed to the carbonyl group (C = O) and N-H of carbamate bond via the polymerization between the isocya- nate and hydroxyl groups (O-H) of WPU dispersion. More- over, the formation of intermolecular hydrogen bonds via the interaction between the (i) hydroxyls groups (O-H) of polyols and N-H of carbamate bonds, (ii) hydroxyls groups (O-H) among the polyols, and (iii) N-H among the carba- mate bonds in the WPU, was also recorded at 3303.8 cm− 1. These carbamate bond and hydrogen bond are important to confer the intrinsic strength to the WPU films to withstand the applied external force. Even so, the spectrum of pristine WPU film has similar absorption peaks and intensity with the one filled with lignin. This phenomenon implies that the incorporation of unfunctionalized lignin may not reactive enough to reinforce the WPU. The observation is even in line with the ultimate tensile strength reported in Sect. 3.1, whereby the strength is only increased by 0.3% when 0.5 wt% of lignin was incorporated into the WPU film.
In contrast, the functionalization process has improved the interaction between the lignin and WPU, which can be observed through the spectrum of functionalized lig- nin-filled WPU bio-composite film. As recorded, the APTES that utilized in the functionalization process gives
Fig. 4 FTIR spectra of pristine WPU film, 0.5 wt% lignin-filled WPU bio-composite film and 0.5 wt% functionalized lignin-filled WPU bio- composite film
hydroxyl groups react with each other and form hydrogen bonds. In contrast, the hydrophobicity of the functionalized lignin is lower than the unfunctionalized lignin due to the presence of amino group by using APTES as the function- alizing agent. The functionalized lignin is more soluble in the mixture and tend to react with WPU during the mixing process, and thus, better surface interaction. Meanwhile, the functionalization process also makes the functionalized lig- nin become more reactive compared to the unfunctionalized lignin. In other words, the lignin can react with each other and agglomerate readily during the mixing process. Conse- quently, the size of functionalized lignin is larger than the one prepared by using unfunctionalized lignin.
Figure 8 illustrates the interaction between lignin/func- tionalized lignin and WPU in the fabricated bio-composite films. As shown in the micrographs, unlike the surface mor- phology of lignin-filled WPU bio-composite film (Fig. 8 WPU bio-composite film is better than 2.0 wt% lignin-filled
WPU bio-composite film. Besides that, it is also discovered that the average lignin particle size in 2.0 wt% lignin-filled WPU bio-composite film is significantly larger than the one in 0.5 wt% lignin-filled WPU bio-composite film. This indi- cates that the lignin agglomerate with each other to form bigger size when the lignin loading is high. Owing to this reason, the size of lignin in the fabricated bio-composite film was measured for the bio-composite films. The result shows that the average size of lignin in 0.5 wt% and 2.0 wt% lignin-filled WPU bio-composite films was 28.63 and 40.3 μm, respectively. Similar trend is also observed in the functionalized lignin-filled WPU bio-composite films, as shown in Fig. 7 (d) and (e) where the average size of the functionalized lignin was measured at 62.87 and 72.39 μm, respectively.
The agglomeration is attributed to the hydrophobic nature of lignin. Owing to the WPU is synthesized by using water as the synthesis medium, the hydrophobic lignin has a high tendency to react with each other during the mixing process. For this reason, the lignin agglomerate when their
Fig. 6 Surface microstructure of lignin and APTES functionalized lignin
Fig. 5 Proposed chemical reaction among APTES, lignin and WPU
hydrogen bonds with the WPU, as evidenced in the FTIR spectra and scanning electron micrographs. The optimum ultimate tensile strength of the resulting bio-composite film is still identified at 0.5 wt%. However, the ultimate tensile strength of the bio-composite films has increased by 9%.
The functionalized lignin-filled WPU bio-composite films also becomes thermally more stable through the improved surface interaction. The present study confirms the use of lignin as a reinforcing filler for the development of WPU bio-composite films. The fabricated films even possess bet- ter performance when the APTES functionalized lignin is used as the reinforcing filler.
Acknowledgements This work was financially supported by (i) Taylor’s University [Project Code: TRGS/ERFS/1/2018/SOE/030]
through the Emerging Research Funding Scheme [Budget Code:
320201-SR67-429-C31] and (ii) Ministry of Higher Education (MoHE) Malaysia, under the Fundamental Research Grant Scheme
(a)), the visible gap between the functionalized lignin and WPU in the bio-composite film is significantly smaller, sug- gesting better surface interaction between the functionalized lignin and WPU polymer chains. This observation further confirms the findings of tensile properties, thermal stability and FTIR analysis, whereby the functionalization process further improves the reinforcing effect of lignin in improv- ing the properties of WPU.
4. Conclusions
The WPU bio-composite films filled with lignin and func- tionalized lignin were successfully fabricated in this work.
The ultimate tensile strength of the lignin-filled WPU bio- composite film reaches its optimum point when 0.5 wt%
of lignin is incorporated. The increase in the lignin load- ing leads to the increase in Young’s modulus and decrease in elongation at break and thermal stability of the result- ing bio-composite film. In contrast, the APTES function- alized lignin has demonstrated a pronounced reinforcing effect through the formation of extra carbamate, urea and
Fig. 8 Surface interaction between WPU and (a) lignin (b) function- alized lignin in 0.5 wt% bio-composite films at microstructural level Fig. 7 Scanning electron micrograph of (a) pristine WPU film, (b) 0.5
wt% lignin-filled WPU bio-composite film, (c) 2.0 wt% lignin-filled WPU bio-composite film, (d) 0.5 wt% functionalized lignin-filled WPU bio-composite film and (e) 2.0 wt% functionalized lignin-filled WPU bio-composite film
9. Datta J, Kopczyńska P (2015) Effect of kenaf fibre modification on morphology and mechanical properties of thermoplastic poly- urethane materials. Ind Crops Prod 74:566–576
10. Ghazali SK, Lee SL, Low JH, Wan Abd Rahman WA (2019) In:
Che Man SH, Baharulrazi N (eds) Biomaterial based polymer composites: properties and characterization. Penerbit UTM Press, Johor Bahru
11. Toh WY, Lai JC, Wan Abdul Rahman WA (2011) Mechanical and water absorption properties of poly(vinyl alcohol)/sago pith waste biocomposites. J Compos Mater 45(11):1201–1207 12. Wan Omar WNA, Ghazali SK, Low JH, Wan Abd Rahman WA
(2019) In: Che Man SH, Baharulrazi N (eds) Biomaterial based polymer composites: properties and characterization. Penerbit UTM Press, Johor Bahru
13. Pang MM, Aaron Y, Koay SC, Low JH, Choo HL, Tshai KY (2019) Soil burial, hygrothermal and morphology of durian skin fiber filled polylactic acid biocomposites. Adv Environ Biol 13:21–25
14. Manzine Costa LM, Molina de Olyveira G, Cherian BM, Leão AL, Souza SF, Ferreira M (2015) Bionanocomposites from elec- trospun PVA/pineapple nanofibers/Stryphnodendron adstringens bark extract for medical applications. Ind Crops Prod 41:198–202 15. Pang MM, Koay SC, Low JH, Buys YF, Tshai KY(2018) Study on the plasticiser type for biobased microcrystalline cellulose filled polylactic acid composite. IOP Conference Series: Materi- als Science and Engineering 458:1–6
16. Chong TY, Law MC, Chan YS (2021) The potentials of corn waste lignocellulosic fibre as an improved reinforced bioplastic composites. J Polym Environ 29(2):363–381
17. Ayrilmis N, Yurttaş E, Durmus A, Özdemir F, Nagarajan R, Kalimuthu M, Kuzman MK (2021) Properties of biocomposite films from pla and thermally treated wood modified with silver nanoparticles using leaf extracts of oriental sweetgum. J Polym Environ 29:2409–2420
18. Mwaikambo LY, Martuscelli E, Avella M (2000) Kapok/cotton fabric-polypropylene composites. Polym Test 19(8):905–918 19. Cruz-Estrada RH, Guillen-Mallette J, Cupul-Manzano CV,
Balam-Hernandez JI (2020) Potential use of waste from tree pruning and recovered plastic to obtain a building material: case study of Merida. Mexico Waste Management & Research: The Journal for a Sustainable Circular Economy 38(11):1222–1230 20. Aris NF, Ghazali SK, Mohamad Z, Jamaluddin J, Adrus N, Abdul
Aziz A, Low JH, Majid A R (2022) The effects of alkaline treat- ment on the oil residue, thermal properties and surface morphol- ogy of oil palm Mesocarp fiber. Environ Qual Manag. https://doi.
org/10.1002/tqem.21871
21. Low JH, Ghanbari T, Wan Abdul Rahman WA, Majid A R (2018) Preparation and characterization of kenaf papers reinforced with tapioca starch: physicomechanical and morphological properties.
J Nat Fibers 15:191–203
22. Majid A, Rusman R, Mohamad R, Zulkornain ZA, Halim AA, Abdullah N, Low M JH (2018) Development of tea waste/kapok fiber composite paper. Chem Eng Trans 63:457–462
23. Rusman R, Majid A, Wan Abd Rahman R, Low WA JH (2017) Carboxymethyl Cassava starch/polyurethane dispersion blend as surface sizing agent. Chem Eng Trans 56:1171–1176
24. Low JH, Lee ZX, Yoon LW, Pang MM, Wong S (2019) Explo- ration of tree pruning waste for papermaking. AIP Conf Proc 2137(1):0200081-020008-6
25. Lim HP, Wan Abdul Rahman WA, Low JH (2020) Properties characterization of Napier grass (Pennisetum purpureum) as the non-wood substitution for natural fiber papermaking. J Adv Mech Eng Appl 1(1):27–35
26. Sarah S, Rahman WAWA, Majid RA, Yahya WJ, Adrus N, Hasan- nuddin AK, Low JH (2018) Optimization of pineapple leaf fibre (FRGS) (FRGS/1/2019/TK02/TAYLOR/02/1).
Authors’ contributions All authors contributed to the study conception and design. Material preparation, data collection, data analysis and manuscript preparation were performed by Qi Yuan Ng and Jiun Hor Low. All authors read and approved the final manuscript.
Funding This work was financially supported by (i) Taylor’s Universi- ty [Project Code: TRGS/ERFS/1/2018/SOE/030] through the Emerg- ing Research Funding Scheme [Budget Code: 320201-SR67-429-C31]
and (ii) Ministry of Higher Education (MoHE) Malaysia, under the Fundamental Research Grant Scheme (FRGS) (FRGS/1/2019/TK02/
TAYLOR/02/1).
Data Availability All data generated or analyzed during this study are included in this published article.
Code Availability Not applicable.
Statements & Declarations
Conflicts of interest/Competing Interests The authors have no con- flicts of interest to declare that are relevant to the content of this article.
Ethics Approval Not applicable.
Consent to Participate Not applicable.
Consent for Publication Not applicable.
References
1. Grand View Research (2017) Plastic films & sheets market size worth $157.5 billion by 2025. https://www.grandviewresearch.
com/press-release/global-plastic-films-and-sheets-market.
Accessed 28 April 2018
2. Transcontinental United Kingdom (2018) Advanced polyurethane films for quality medical care. http://www.coverisadvancedcoat- ings.com/coveris-products/inspire-medical-components/product- constructions/polyurethane-films/. Accessed 29 April 2018 3. Hercule K, Yan Z, Christophe MM (2011) Preparation and char-
acterization of waterborne polyurethane crosslinked by urea bridges. Int J Chem 3(2):88–96
4. Lambourne R, Strivens TA (1999) Paint and surface coatings - theory and practice second edition. Woodhead Publishing, Sawston
5. She Y, Zhang H, Song S, Lang Q, Pu J (2013) Preparation and characterization of waterborne polyurethane modified by nano- crystalline cellulose. BioResources 8(2):2594–2604
6. Liu H, Cui S, Shang S, Wang D, Song J (2013) Properties of rosin-based waterborne polyurethanes/cellulose nanocrystals composites. Carbohydr Polym 96(2):510–515
7. Low JH, Andenan N, Wan Abdul Rahman WA, Rusman R, A.Majid R (2017) Evaluation of rice straw as natural filler for injection molded high density polyethylene bio-composite mate- rials. Chem Eng Trans 56:1081–1086
8. Low JH, Andenan N, Wan Abdul Rahman WA (2018) The influ- ence of crosslink chemicals on the mechanical strength and water absorption of rice straw-based green composites. J Nat Fibers 15:122–130
38. Nilwala K, Chanaka S, Piyumi P, Nadeesh M, Veranja K (2014) Modified layered nanohybrid structures for the slow release of urea. Nanosci Nanotechnol - Asia 4(2):94–102
39. Oh T, Choi C (2010) Comparison between SiOC thin films fabri- cated by using plasma enhanced chemical vapor deposition and SiO2 thin films by using Fourier transform infrared spectroscopy.
J Korean Phys Soc 56(4):1150–1155
40. Pardini OR, Amalvy JI (2008) FTIR, 1H-NMR spectra, and ther- mal characterization of water-based polyurethane/acrylic hybrids.
J Appl Polym Sci 107(2):1207–1214
41. Lin-Vien D, Colthup NB, Fateley WG, Grasselli JG (1991) The handbook of infrared and Raman characteristic frequencies of organic molecules. Academic Press Limited, London
42. Zhu J, Xue L, Wei W, Mu C, Jiang M, Zhou Z (2015) Modifi- cation of lignin with silane coupling agent to improve the inter- face of poly(L-lactic) acid/lignin composites. BioResources 10(3):4315–4325
43. Kaewtatip K, Thongmee J (2013) Effect of kraft lignin and esteri- fied lignin on the properties of thermoplastic starch. Mater Des 49:701–704
44. Lv S, Tan H, Gu J, Zhang Y (2015) Silane modified wood flour blended with poly(lactic acid) and its effects on composite perfor- mance. BioResources 10(3):5426–5439
45. Spragg R(2014) Measuring orientation in polymer films.Spec- trosc Suppl29(8)
Publisher’s Note Springer Nature remains neutral with regard to juris- dictional claims in published maps and institutional affiliations.
Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
extraction methods and their biodegradabilities for soil cover application. J Polym Environ 26(1):319–329
27. Low JH, Jusoh@Taib ER, Wan Abdul Rahman WA, S. W (2019) In: Che Man SH, Baharulrazi N (eds) Biomaterial based polymer composites: properties and characterization. Penerbit UTM Press, Johor Bahru
28. Beh JH, Lai JC, Lim TH, Low JH(2019) In: Fangueiro R (ed) Proceedings of the 4th international conference on natural fibers - smart sustainable solutions. TecMinho - Associação Universi- dade-Empresa para o Desenvolvimento, Porto
29. Dias OAT, Negrão DR, Silva RC, Funari CS, Cesarino I, Leao AL (2016) Studies of lignin as reinforcement for plastics composites.
Mol Cryst Liq Cryst 628(1):72–78
30. Hu J, Zhang Q, Lee D-J (2018) Kraft lignin biorefinery: a per- spective. Bioresour Technol 247:1181–1183
31. Teoh SW, Yoon LW, Wong WY, Low JH (2022) Application of black liquor derived carbonaceous compound as fuel in direct car- bon fuel cell. Int J Integr Eng 14(2):146–156
32. Haldar D, Purkait MK (2022) Thermochemical pretreatment enhanced bioconversion of elephant grass (Pennisetum purpu- reum): insight on the production of sugars and lignin. Biomass Convers Biorefinery 12:1125–1138
33. Duarah P, Haldar D, Purkait MK (2020) Technological advance- ment in the synthesis and applications of lignin-based nanopar- ticles derived from agro-industrial waste residues: a review. Int J Biol Macromol 163:1828–1843
34. Chen H (2015) Lignocellulose biorefinery engineering. Wood- head Publishing, Sawston
35. Cheremisinoff NP, Rosenfeld PE (2010) Best practices in the wood and paper industries. William Andrew, Norwich
36. Merck(2019) IR Spectrum Table & Chart. https://www.sigmaal- drich.com/technical-documents/articles/biology/ir-spectrum- table.html. Accessed 12 January 2020
37. Low JH, Wan Abdul Rahman WA (2017) In: Kozlowski RM, Muzyczek M (eds) Natural fibers: properties, mechanical behav- ior, functionalization and applications. Nova Science Publishers, Inc, New York