Pengaruh Komposisi Limbah Sekam Padi Dan Abu Sekam Padi Sebagai Pengisi Komposit Hibrid Limbah Botol Plastik Kemasan Minuman Dengan Penambahan Gliserol Sebagai Plasticizer

(1)

LAMPIRAN A

DATA PENELITIAN

A.1 DATA HASIL MODULUS YOUNG

Tabel A.1 Data Hasil Modulus Young

Komposisi Sampel 1 Sampel 2 Sampel 3 Rata-Rata

95 : 5 98.964 111,234 101.989 98.964

90 : 10 103.977 101.019 100.221 102.039

85 : 15 126.633 83.634 96.255 105.134

A.2 DATA HASIL KEKUATAN TARIK [MPa]

Tabel A.2 Data Hasil Kekuatan Tarik

95 : 5 2.7 3.266 2.187 2.717

90 : 10 2.969 2.141 2.037 2.382

85 : 15 1.247 2.673 1.905 1.941

A.3 DATA HASIL PEMANJANGAN PADA SAAT PUTUS [%]

Tabel A.3 Data Hasil Pemanjangan Pada Saat Putus

95 : 5 2.728 2.937 2.145 2.603

90 : 10 2.856 2.212 2.033 2.367

85 : 15 1.9847 2.196 1.978 2.053

A.4 DATA HASIL KEKUATAN LENTUR [MPa]

Tabel A.4 Data Hasil Kekuatan Lentur

95 : 5 5.633 8.078 6.146 6.619

90 : 10 5.933 5.342 5.526 5.60

85 : 15 3.094 4.516 4.231 3.947

A.5 DATA HASIL KEKUATAN BENTUR [J/M2]

(2)

A.6 DATA HASIL PENYERAPAN AIR KOMPOSIT HIBRID DENGAN

PENAMBAHAN GLISEROL [%]

Table A.6 Data Hasil Penyerapan Air (Data nilai rata-rata)

jam 100 95/5 90/10 85/15

(3)

LAMPIRAN B

CONTOH PERHITUNGAN

B.1 PERHITUNGAN PENYERAPAN AIR KOMPOSIT HIBRID

Perhitungan Penyerapan Air Komposit Hibrid PET Limbah Botol Plastik Kemasan Minuman Massa Awal : 1.0501

Massa setelah 24 jam : 1.055403 Maka persen penyerapan air =

1.0501 1.0501 1.055403

x 100%= 0.5050%

(4)

LAMPIRAN C

DOKUMENTASI PENELITIAN

C.1 PENYEDIAAN PET LIMBAH BOTOL PLASTIK KEMASAN MINUMAN

Gambar C.1 Penyediaan PET Limbah Botol Plastik Kemasan Minuman

C.2 PENYEDIAAN ABU SEKAM PADI

(5)

C.3 PENYEDIAAN SEKAM PADI

Gambar C.3 Penyediaan Sekam Padi

C.4 PENYEDIAAN GLISEROL

(6)

C.5 PROSES PENCAMPURAN DENGAN EKSTRUDER

Gambar C.5 Proses Pencampuran Dengan Ekstruder

C.6 PROSES PENCETAKAN DENGAN ALAT HOT PRESS

(7)

C.7 HASIL KOMPOSIT HIBRID DENGAN PENAMBAHAN GLISEROL

SEBAGAI PLASTICIZER

Gambar C.7 Hasil Komposit Hibrid dengan Penambahan Gliserol Sebagai Plasticizer

C.8 ALAT UNIVERSAL TESTING MACHINE (UTM) GOTECH AL-7000M

GRID TENSILE

(8)

C.9 ALAT UNIVERSAL TESTING MACHINE (UTM) GOTECH AL-7000M

GRID FLEXURAL

Gambar C.9 Alat UTM Gotech Al-7000 M Grid Flexural

C.10 ALAT IMPACT TESTER GOTECH

(9)

LAMPIRAN D

HASIL PENGUJIAN LAB ANALISIS DAN

INSTRUMEN

D.1 HASIL FTIR PET LIMBAH BOTOL PLASTIK KEMASAN

MINUMAN

(10)

D.2 HASIL FTIR ABU SEKAM PADI

Gambar D.2 Hasil FTIR Abu Sekam Padi

(11)

D.4 HASIL FTIR KOMPOSIT HIBRID PET LBPKM-ABU SEKAM PADI

DAN SEKAM PADI

(12)

D.5 HASIL FTIR KOMPOSIT HIBRID PET LBPKM-ABU SEKAM PADI

DAN SEKAM PADI DENGAN PENAMBAHAN GLISEROL

SEBAGAI PLASTICIZER

(13)

D.6 HASIL SEM PET LBPKM (LIMBAH BOTOL PLASTIK KEMASAN

MINUMAN)

(14)

D.7 HASIL SEM KOMPOSIT HIBRID PET LBPKM-ABU SEKAM PADI

DAN SEKAM PADI DENGAN PENAMBAHAN GLISEROL

SEBAGAI PLASTICIZER PADA RASIO 95/5

(15)

D.8 HASIL SEM KOMPOSIT HIBRID PET LBPKM-ABU SEKAM PADI

DAN SEKAM PADI DENGAN PENAMBAHAN GLISEROL SEBAGAI

PLASTICIZER PADA RASIO 85/15