BERAT ISI AGREGAT HALUS UNTUK MATERIAL BETON
ASTM C 29/C 29M – 90 1. Calibration Of Measure
Suhu Ruangan oC 28
Suhu Air oC 26
Berat Bejana Kg 0.47
Berat Air Kg 1.85
Berat Isi Air Kg/m3 996.77
Faktor Koreksi, C=(B/A) 539.96
Diameter Agregat Maksimum Mm 5
2. Hasil Pemeriksaan
Berat
Cara Merojok Cara Longgar
Sampel 1 (kg) 3.01 2.86
Sampel 2 (kg) 3.06 2.84
Total (kg) 6.07 5.7
Rata-rata (kg) 3.035 2.85
Net Wwight (G), kg 2.571 2.386
ANALISA AYAKAN PASIR UNTUK MATERIAL BETON
(ASTM C 136 – 84a)
Diameter Ayakan.
(mm)
Berat Fraksi Tertahan Kumulatif Berat
Sampel 1 (gr)
Berat Sampel
2 (gr)
Berat Total (gr)
% Tertahan (%)
Lolos (%) 9.50 0 0 0 0.00 0.00 100
4.75 0 3 3 0.15 0.15 99.85
2.36 7 5 12 0.60 0.75 99.25
1.18 121 115 236 11.80 12.55 87.45
0.60 257 260 517 25.85 38.4 61.6
0.30 284 274 558 27.90 66.3 33.7
0.15 245 261 506 25.30 91.6 8.4
Pan 86 82 168 8.40 100 0
Total 1000 1000 2000 100
Fineness Modulus (FM) = 209.75
100 = 2.10 Klasifikasi psir yang baik:
Halus : 2.2<FM<2.6
Sedang : 2.6<FM<2.9
BERAT JENIS DAN ABSORBSI AGREGAT HALUS UNTUK
MATERIAL BETON
ASTM C 128 – 88
Sampel 1 Sampel 2 Rata-rata Berat agregat dalam keadaan SSD di
udara, g (S) 500 500 500 Berat piknometer + agregat + air
yang dikalibrasi, g (C) 981 979 980 Berat kering oven agregat di udara,g
(A) 482 483 482.5
Berat piknometer yang terisi air, g
(B) 668 669 668.8
Berat Jenis Kering =
( +�− ) 2.58 2.54 2.56
Berat Jenis SSD = �
( +�− ) 2.67 2.63 2.65
Berat Jenis Semu =
( + − ) 2.85 2.79 2.82
PEMERIKSAAN KADAR LUMPUR AGREGAT HALUS
UNTUK MATERIAL BETON
ASTM C 117 – 90
Sampel 1 Sampel 2 Rata-rata Berat agregat mula-mula, g 500 500 500
Berat kering agregat setelah dicuci, g 490 491 490
Berat lumpur yang telah dicuci
dengan ayakan No.200, g 10 9 9.5 Kadar lumpur pada agregat yang
PENGUJIAN COLORIMETRIC KANDUNGAN BAHAN
ORGANIK AGREGAT HALUS
(ASTM c40 – 84)
Sampel Perbandingan Terhadap Organic
Plate
Lebih Terang
Sama No.3
UJI BERAT JENIS SEMEN PORTLAND
Jenis Semen : Semen Padang Tipe I I II III Berat Benda Uji, gr B 60.11 60.06 63.9
Volume Awal, gr V1 0.1 0.1 0
Volume Akhir, gr V2 20.7 20.6 21.4
Berat Jenis Semen B*d/(V2-V1) 3.01 3.02 3.08
UJI BERAT JENIS SERBUK KACA
Jenis Semen : Semen Padang Tipe I I II III Berat Benda Uji, gr B 45.12 45.1 45.14
Volume Awal, gr V1 0.1 0 0
Volume Akhir, gr V2 18.55 18.48 18.51
Berat Jenis Semen B*d/(V2-V1) 2.52 2.51 2.51
HASIL PENGUJIAN PENYIMPANGAN UKURAN BATAKO DENGAN FOAMING AGENT
No. Benda
Ukuran batako yang menjadi acuan: Panjang = 400mm; Lebar = 200mm; Tebal = 100mm
*
HASIL PENGUJIAN PENYIMPANGAN UKURAN BATAKO DENGAN SUBSTITUSI SERBUK KACA 20% LOLOS AYAKAN No. 200 DAN
FOAMING AGENT
No. Benda
Ukuran batako yang menjadi acuan: Panjang = 400mm; Lebar = 200mm; Tebal = 100mm
*
HASIL PENGUJIAN BERAT ISI BATAKO DENGAN FOAMING AGENT
No. Bahan Tambah
Benda Uji
Volume (m3)
Berat Basah (Kg)
Berat Kering
(Kg)
Berat Isi (Kg/m3)
1
Foaming Agent
HASIL PENGUJIAN BERAT ISI BATAKO DENGAN SUBSTITUSI SERBUK KACA 20% LOLOS AYAKAN No. 200 DAN FOAMING AGENT
No. Bahan Tambah
Benda Uji
Volume (M3)
Berat Basah (Kg)
Berat Kering
(Kg)
Berat Isi (Kg/m3)
1
SK 20% + Foaming
Agent
HASIL PENGUJIAN BERAT ISI SILINDER DENGAN FOAMING AGENT
No. Bahan Tambah
Benda Uji
Volume (M3)
Berat Basah (Kg)
Berat Kering
(Kg)
Berat Isi (Kg/m3)
1
Foaming Agent
P1. 1 0.00157 2.132 1.705 1085.987
2 P1. 2 0.00157 2.189 1.658 1056.051
3 P1. 3 0.00157 2.200 1.733 1103.822
4 P1. 4 0.00157 2.191 1.683 1071.975
5 P1. 5 0.00157 2.266 1.802 1147.771
6 P1. 6 0.00157 2.292 1.786 1137.580
7 P1. 7 0.00157 2.270 1.782 1135.032
8 P1. 8 0.00157 2.329 1.793 1142.038
9 P1. 9 0.00157 2.271 1.723 1097.452
10 P1. 10 0.00157 2.263 1.719 1094.904
HASIL PENGUJIAN BERAT ISI SILINDER DENGAN SUBSTITUSI SERBUK KACA 20% LOLOS AYAKAN No. 200 DAN FOAMING AGENT
No. Bahan Tambah
Benda Uji
Volume (M3)
Berat Basah (Kg)
Berat Kering
(Kg)
Berat Isi (Kg/m3)
1
SK 20% + Foaming
Agent
P2. 1 0.00157 2.478 2.264 1442.038
2 P2. 2 0.00157 2.281 2.308 1470.064
3 P2. 3 0.00157 2.864 2.692 1714.650
4 P2. 4 0.00157 2.812 2.47 3 1575.159
5 P2. 5 0.00157 2.563 2.263 1441.401
6 P2. 6 0.00157 2.496 2.170 1382.166
7 P2. 7 0.00157 2.652 2.350 1496.815
8 P2. 8 0.00157 2.481 2.144 1365.605
9 P2. 9 0.00157 2.660 2.368 1508.280
10 P2. 10 0.00157 2.829 2.624 1671.338
HASIL PENGUJIAN ABSORBSI BATAKO DENGAN FOAMING AGENT
No. Bahan Tambah
Benda Kering (Kg)
HASIL PENGUJIAN ABSORBSI BATAKO DENGAN SUBSTITUSI SERBUK KACA 20% LOLOS AYAKAN No. 200 DAN FOAMING AGENT
No. Bahan Tambah
Benda Kering
(Kg) Foaming
HASIL PENGUJIAN ABSORBSI SILINDER DENGAN FOAMING AGENT
No. Bahan Tambah
Benda Uji
Berat Basah (Kg)
Berat Kering
(Kg)
Daya Serap (%)
Mutu Benda Uji
SNI 03-
0349-1989
1
Foaming Agent
P2. 4 2.132 1.705 25.044 35 2
2 P2. 5 2.189 1.658 32.027 35 2
3 P2. 6 2.200 1.733 26.947 35 2
4 P2. 7 2.191 1.683 30.184 35 2
5 P2. 8 2.266 1.802 25.749 35 2
6 P2. 9 2.292 1.786 28.331 35 2
7 P2. 10 2.270 1.782 27.385 35 2
8 P3. 1 2.329 1.793 29.894 35 2
9 P3. 2 2.271 1.723 31.805 35 2
10 P3. 3 2.263 1.719 31.646 35 2
HASIL PENGUJIAN ABSORSI SILINDER DENGAN SUBSTITUSI SERBUK KACA 20% LOLOS AYAKAN No. 200 DAN FOAMING AGENT
No. Bahan Tambah
Benda Uji
Berat Basah (Kg)
Berat Kering
(Kg)
Absorbsi (%)
Mutu Benda Uji
SNI 03-
0349-1989
1
SK 20% + Foaming
Agent
P2. 4 2.478 2.264 9.452 25 1
2 P2. 5 2.281 2.308 7.496 25 1
3 P2. 6 2.864 2.692 6.389 25 1
4 P2. 7 2.812 2.473 13.708 25 1
5 P2. 8 2.563 2.263 13.257 25 1
6 P2. 9 2.496 2.170 15.023 25 1
7 P2. 10 2.652 2.350 12.851 25 1
8 P3. 1 2.481 2.144 15.718 25 1
9 P3. 2 2.660 2.368 12.331 25 1
10 P3. 3 2.829 2.624 7.813 25 1
HASIL PENGUJIAN KUAT TEKAN BATAKO DENGAN FOAMING AGENT
No. Bahan Tambah
S
Tanggal
Umur (Hari)
Pembacaan Dial
Rata-rata (KN)
Luas Daerah
Tekan (cm2)
Kuat Tekan (Kg/cm2)
HASIL PENGUJIAN KUAT TEKAN BATAKO DENGAN SUBSTITUSI SERBUK KACA 20% LOLOS AYAKAN No. 200 DAN FOAMING AGENT
No. Bahan Tambah
S
Tanggal
Umur (Hari)
Pembacaan Dial
Rata-rata (KN)
Luas Daerah
Tekan (cm2)
Kuat Tekan (Kg/cm2) Foaming
HASIL PENGUJIAN TEKAN SILINDER DENGAN FOAMING AGENT
No. Bahan Tambah
S
Tanggal
Umur (Hari)
Pembacaan Dial
Rata-rata (KN)
Luas Daerah
Tekan (cm2)
Kuat Tekan Rata-rata
(Kg/cm2)
HASIL PENGUJIAN TEKAN SILINDER DENGAN SUBSTITUSI SERBUK KACA 20% LOLOS AYAKAN No. 200 DAN FOAMING AGENT
No. Bahan Tambah
S
Tanggal
Umur (Hari)
Pembacaan Dial
Rata-rata (KN)
Luas Daerah
Tekan (cm2)
Kuat Tekan Rata-rata
(Kg/cm2) Foaming
HASIL PENGUJIAN KUAT TEKAN DINDING BATAKO
No. Bahan Tambah
S
Tanggal
Umur (Hari)
Pembacaan Dial (KN)
Kuat Tekan (Kg/cm2) Foaming
DOKUMENTASI PENGUJIAN
Pasir yang Digunakan Semen Padang Tipe I
Cetakan Batako dan Silinder Alat Pemecah Botol Kaca
Botol Kaca Sebelum dihaluskan Proses Penghancuran Botol Kaca
Blender Penghalus Serbu Kaca Pengayakan Serbuk Kaca dengan
Serbuk Kaca yang Dihaluskan Penuangan Cairan Foaming Agent
Pencampuran Cairan Foaming Agent Pembuatan Foaming Agent
Dengan Air
Penimbangan Foaming Agent Proses Pengecoran Sampel
Proses Pembukaan Cetakan Batako Hasil Pengecoran batako dan silinder
Curing Sampel Pengukuran Batako Menggunakan
Penggaris
Pengujian Absorbsi Batako Penimbangan Sampel
Pemasangan Dinding Batako Dinding Batako Selesai Dipasang
Alat Hydraulic Jack untuk Menekan Pemasangan Alat Tekan Dinding
Dinding
Pengujian Kuat Tekan Dinding Proses Pengujian Tekan Dinding