PENGARUH PENAMBAHAN FOAM AGENT TERHADAP PEMBUATAN BETON BUSA
(TINJAUAN TERHADAP DENSITAS, KONDUKTIVITAS TERMAL DAN SOUND ABSORPTION)
TUGAS AKHIR
Diajukan kepada Fakultas Teknik Universitas Muhammadiyah Malang Untuk Memenuhi Salah Satu Persyaratan Akademik dala Menyelesaikan
Program Sarjana Teknik
Oleh :
SEVTIAN ARIEF NUR CAHYO 201110340311041
JURUSAN TEKNIK SIPIL FAKULTAS TEKNIK
Pengaruh Penambahan Foam Agent Pada Pembuatan Beton Busa (Tinjauan Terhadap Densitas, Konduktivitas Termal dan Sound Absorption)
Sevtian Arief Nur Cahyo Jurusan Teknik Sipil
Fakultas Teknik-Universitas Muhammadiyah Malang Kampus III Jl. Tlogomas No.246
Tlp. (0341) 46318-319 Psw.130 Fax. (0341) 460435
Abstrak
Peningkatan suhu di lingkungan sekitar dan tingkat kebisingan suatu lingkungan dapat mempengaruhi kenyamanan penghuni bangunan. Dalam hal ini dinding berfungsi untuk melindungi dan membatasi antar ruang dengan ruang maupun ruang dengan daerah luar bangunan. Menghadapi situasi tersebut beton busa menjadi solusi alternatif bahan material dinding yang dapat meningkatkan kenyamanan dalam mengurangi gangguan peningkatan suhu dan kebisingan dalam ruangan.
Beton busa memiliki kemampuan yang baik untuk mereduksi panas yang diterima dan baik juga untuk menyerap suara. Dalam penelitian beton busa ini menggunakan metode eksperimen dan variabel yang digunakan ada 2 yaitu variabel terikat dan variabel bebas. Dimana variabel terikat : campuran semen, air dan pasir sedangkan untuk variabel bebasnya adalah prosentase foam agent dengan variasi 0%, 2%, 3% dan 4% dari berat semen yang digunakan dan digunakan rasio pengolahan foam agent : air = 1 : 20. Pengujian dilaksanakan pada beton busa umur 28 hari.
Berdasarkan dari hasil penelitian ini di dapat nilai densitas untuk penambahan foam agent 2%, 3% dan 4% secara berurutan sebesar 1768kg/m3; 1698kg/m3dan 1666 kg/m3 . Hasil pengujian konduktivitas termal beton busa dengan penambahan foam agent 2%, 3% dan 4% adalah sebesar 0,897 W/m.K; 0,894 W/m.K dan 0,886 W/m.K lebih baik dibandingkan dengan beton biasa (k=1,448 W/m.K). Sedangkan untuk pengujian penyerapan bunyi pada penambahan foam agent 2%, 3% dan 4 % adalah sebesar 0.707, 0.734 dan 0.760 yang lebih baik dibandingkan dengan nilai penyerapan suara pada bahan mortar normal (α=0,636)
PENGARUH PEMAKAIAN FOAM AGENT PADA PEMBUATAN BETON BUSA
(TINJAUAN TERHADAP DENSITAS, KONDUKTIVITAS TERMAL DAN SOUND ABSORPTION)
TUGAS AKHIR Diajukan kepada
Fakultas Teknik Universitas Muhammadiyah Malang Untuk Memenuhi Salah Satu Persyaratan
Akademik dalam Menyelesaikan Program Sarjana Teknik
Oleh :
Sevtian Arief Nur Cahyo 201110340311041
JURUSAN TEKNIK SIPIL FAKULTAS TEKNIK
LEMBAR PENGESAHAN
JUDUL : PENGARUH PEMAKAIAN FOAM AGENT PADA
PEMBUATAN BETON BUSA (TINJAUAN TERHADAP
DENSITAS, KONDUKTIVITAS TERMAL DAN SOUND
ABSORPTION)
Nama : Sevtian Arief Nur Cahyo
NIM : 201110340311041
Pada hari Sabtu 30 Januari 2016, telah diuji oleh tim penguji :
1. Mohammad Abduh, ST. MT. Dosen Penguji I ....…
………
2. Ir. Lukito Prasetyo, MT. Dosen Penguji II ………
Dosen Pembimbing I, Dosen Pembimbing II,
(Ir. Erwin Rommel, MT) (Ir. Yunan Rusdianto, MT)
Mengetahui,
Ketua Jurusan Teknik Sipil
SURAT PERNYATAAN
Yang bertanda tangan di bawah ini:
Nama : Sevtian Arief Nur Cahyo
NIM : 201110340311041
Jurusan : Teknik Sipil
Fakultas : Teknik
UNIVERSITAS MUHAMMADIYAH MALANG
Dengan ini saya menyatakan sebenar-benarnya bahwa: Tugas Akhir dengan judul:
PENGARUH PEMAKAIAN FOAM AGENT PADA PEMBUATAN BETON
BUSA (TINJAUAN TERHADAP DENSITAS, KONDUKTIVITAS TERMAL
DAN SOUND ABSORPTION) adalah hasil karya saya dan bukan karya tulis
orang lain. Dalam naskah tugas akhir ini tidak terdapat karya ilmiah yang pernah
diajukan oleh orang lain untuk memperoleh gelar akademik di suatu Perguruan
Tinggi dan tidak terdapat karya atau pendapat yang pernah ditulis atau diterbitkan
oleh orang lain, baik sebagian maupun seluruhnya, kecuali yang secara tertulis
dikutip dalam naskah ini dan disebutkan dalam sumber kutipan atau daftar
pustaka.
Demikian pernyataan ini saya buat dengan sebenarnya dan apabila penyataan ini
tidak benar saya bersedia mendapat sangsi akademis.
Malang, 30 Januari 2016
Yang menyatakan,
LEMBAR PERSEMBAHAN
Bismillahirrohmaanirrohiim...
Terlebih dahulu, sujud dan syukur kupersembahkan kepada Allah SWT. atas
semua nikmat dan karunia-Nya. Serta shalawat dan salam selalu terlimpahkan
kepada Nabi Muhammad SAW. beserta keluarga, para sahabat dan kaumnya yang
setia hingga akhir zaman.
Dan tak lupa kupersembahkan tugas akhir ini kepada:
1. Ibunda tercinta Siti Ro’isah yang selalu memberikan segala dukungan dan
kasih sayang serta doa tiada hentinya.
2. Ayahanda Abd. Munim, BA. yang selalu memberikan segala dukungan
dan kasih sayang serta doa tiada hentinya.
3. Kakak-kakakku Cicik Rahmawati, Yusroni Izzul Mutho’ dan Bagus
Setiawan yang telah memberikan semangat dan doa.
4. Dosen pembimbing satu Ir. Erwin Rommel, MT. dan bapak pembimbing
dua Ir. Yunan Rusdianto, MT.
5. Sahabat-sahabatku sepenelitian Andri Slamet Riyanto, Reza Arief Susanto
dan Angga Wahyudin yang selalu memberikan semangat, motivasi, tawa
selama menyelesaikan tugas akhir ini.
6. Teman-teman Sipil A Angkatan 2011 : Bayu, Pangestu, Amif, irfan, Desi,
Aji, Tya, Dadang, dan seluruhnya teman-teman sipil A angkatan 2011
yang tidak bisa saya sebutkan satu per satu, terimakasih banyak atas
dukungannya, semangat terus buat yang belum lulus. Cepet menyusul ya
7. Serta semua yang turut membantu terselesaikannya skripsi ini yang tidak
bisa saya sebutkan satu per satu.
Semoga atas semua bantuan yang telah diberikan kepada penulis
mendapatkan ridho dan pahala dari Allah SWT., Aamiin...
KATA PENGANTAR
Segala puja dan puji bagi ALLAH SWT atas semua nikmat dan
karunia-Nya yang tak terhingga yang diperuntukkan bagi semua hamba-karunia-Nya. Shalawat
dan salam juga bagi NABI MUHAMMAD SAW berserta keluarga, para sahabat
dan kaumnya yang setia hingga akhir zaman.
Tugas akhir ini penulis tulis dengan judul PENGARUH PEMAKAIAN
FOAM AGENT PADA PEMBUATAN BETON BUSA (TINJAUAN
TERHADAP DENSITAS, KONDUKTIVITAS TERMAL DAN SOUND
ABSORPTION) untuk memenuhi salah satu syarat untuk mencapai gelar Sarjana
Teknik Sipil Universitas Muhammadiyah Malang.
Dalam masa perkuliahan sampai penulisan tugas akhir ini tentunya banyak
suka duka yang terjadi, namun berkat bantuan berbagai pihak kami dapat
menyelesaikan penulisan tugas akhir ini, untuk itu tidak lupa kami sampaikan
terima kasih kepada:
1. Drs. Fauzan, Mpd. selaku Rektor Universitas Muhammadiyah Malang
2. Bapak Ir. Sudarman, MT. selaku Dekan Fakultas Teknik Universitas
Muhammadiyah Malang
3. Ibu Ir. Rofikatul Karimah, MT. selaku Ketua Jurusan Teknik Sipil
Universitas Muhammadiyah Malang
4. Bapak Ir. Erwin Rommel, MT. selaku Dosen Pembimbing I
5. Bapak Ir. Yunan Rusdianto, MT. selaku Dosen Pembimbing II
7. Seluruh Staf Jurusan Teknik Sipil, Staf Laboratorium Teknik Sipil dan
Staf TU Fakultas Teknik.
8. Seluruh teman-teman yang telah membantu.
Akhir kata penulis mengharapkan kritik dan saran demi kesempurnaan
tugas akhir ini dan semoga tugas akhir ini membawa manfaat bagi perkembangan
ilmu pengetahuan dibidang ketekniksipilan.
Malang, 30 Januari 2015
ABSTRAK
Beton busa memiliki kemampuan yang baik untuk mereduksi panas yang
diterima dan baik juga untuk menyerap suara. Dalam penelitian beton busa ini
menggunakan metode eksperimen dan variabel yang digunakan ada 2 yaitu
variabel terikat dan variabel bebas. Dimana variabel terikat : campuran semen,
air dan pasir sedangkan untuk variabel bebasnya adalah prosentase foam agent
dengan variasi 0%, 2%, 3% dan 4% dari berat semen yang digunakan dan
digunakan rasio pengolahan foam agent : air = 1 : 20. Pengujian dilaksanakan
pada beton busa umur 28 hari.
Berdasarkan dari hasil penelitian ini di dapat nilai densitas untuk
penambahan foam agent 2%, 3% dan 4% secara berurutan sebesar 1768kg/m3;
1698kg/m3; 1666 kg/m3 telah memenuhi standard SNI 03-2847-2002. Hasil
pengujian konduktivitas termal beton busa dengan penambahan foam agent 2%,
3% dan 4% adalah sebesar 0,897 W/m.K; 0,894 W/m.K dan 0,886 W/m.K lebih
baik dibandingkan dengan beton biasa (k=1,448 W/m.K). Sedangkan untuk
pengujian penyerapan bunyi pada penambahan foam agent 2%, 3% dan 4 %
adalah sebesar 0.707, 0.734 dan 0.760 yang lebih baik dibandingkan dengan nilai penyerapan suara pada bahan mortar normal (α=0,636).
ABSTRACT
Foam concrete has a good ability to reduce heat well received and also to
absorb the sound. In this foamed concrete research using experimental methods
and variables used there are 2 of the dependent variable and independent
variables. Where the dependent variable: a mixture of cement, water and sand
while the independent variable is the percentage of foam agent with a variation of
0%, 2%, 3% and 4% of the weight of cement used and the ratio of foam
processing agent: water = 1: 20. Testing held on foamed concrete 28 days.
Based on the results of this study can increase the density of foam agent
2%, 3% and 4% respectively of 1768kg / m3; 1698kg / m3; 1666 kg / m3 has met
the standard of SNI 03-2847-2002. Results of testing the thermal conductivity of
foam concrete foam agent with the addition of 2%, 3% and 4% is equal to 0.897
W / m.K; 0.894 W / m.K and 0.886 W / m.K better than ordinary concrete (k =
1.448 W / m.K). As for testing the sound absorption on the addition of foam agent
2%, 3% and 4% is for 0707, 0734 and 0760 were better than the sound
absorption values in normal mortar material (α = 0.636).
DAFTAR ISI
Halaman JUDUL
LEMBAR PENGESAHAN... i
ABSTRAKSI... ii
DAFTAR ISI... iii
BAB I PENDAHULUAN 1.1Latar Belakang... 1
1.2Rumusan Masalah... 2
1.3Batasan Masalah... 2
1.4Tujuan Penelitian ... 2
1.5Manfaat Penelitian... 3
BAB II TINJAUAN PUSTAKA 2.1 Riset Terdahulu... 4
2.2 Landasan Teori... 6
2.2.1 Beton Ringan... 6
2.2.2 Beton Busa (Foamed Concrete)... 6
2.2.3 Proses Pembuatan Beton Busa... 7
2.2.4 Dinding Beton Ringan... 8
2.3 Bahan Penyusun Beton Busa……….. 9
2.3.1 Foam Agent ………. 9
2.3.3 Air………... 12
2.3.4 Pasir……… 13
2.4 Konduktivitas Thermal………...…... 14
2.5 Penyerapan Suara (Sound Absorption)………..……… 17
2.5.1 Frekuensi Bunyi………..……… 19
2.5.2 Intensitas Bunyi……….…………..………... 19
2.5.3 Koefisien Serapan Bunyi/Suara………..……… 19
2.6 Desitas……….…. . . 22
BAB III METODE PENELITIAN 3.1 Lokasi Penelitian…... 24
3.2 Rancangan Penelitian... 24
3.3 Benda Uji... 26
3.4 Alat dan Bahan Penelitian………. 27
3.4.1 Peralatan... 27
3.5 Tahapan Penelitian……….…... 30
3.5.1 Persiapan Bahan……… 30
3.5.2 Pembuatan dan Pencetakan Benda Uji……….………. 31
3.5.3 Perawatan Benda Uji……….……… 33
3.6 Tahapan Pengujian Fisik Beton Busa……….…….…. 33
3.6.1 Uji Pengukuran Densitas……….…….. 33
3.6.2 Uji Sound Absorption……….…………... 33
BAB IV HASIL PENELITIAN DAN PEMBAHASAN
4.1 Density Beton Busa... 37
4.2 Koduktivitas Termal ... 40
4.3 Sound Absorption ... 45
BAB V PENUTUP
5.1 Kesimpulan... 50
5.2 Saran... 51
DAFTAR TABEL
Tabel 2.1 Susunan Unsur Semen biasa... 11
Tabel 2.2 Nilai k Bahan Bangunan……... 15
Tabel 2.3 Koefisien Penyerapan Suara………... 18
Tabel 2.4 Kumpulan Nilai Densitas Beton………... 23
Tabel 3.1 Hasil Pengujian Konsistensi Mortar... 25
Tabel 3.2 Komposisi Campuran Beton Busa... 26
Tabel 3.3 Properti Benda Uji Konduktivitas Termal ... 27
Tabel 3.4 Properti Benda Uji Penyerapan Suara…... ... 27
Tabel 4.1 Hasil Density Beton Busa…………...…... ... 37
Tabel 4.2 Nilai Konduktivitas Termal………... ... 40
Tabel 4.3 Nilai Koefisiensi Penyerapan Suara…….. ... 45
DAFTAR GAMBAR
Gambar 2.1 Percobaan untuk mengetahui konduktivitas termal dari material... 14
Gambar 2.2 Perpindahan panas konduksi satu dimensi... 15
Gambar 3.1 Benda Uji Kondutivitas Termal………... 26
Gambar 3.2 Benda Uji Penyerapan Suara... 26
Gambar 3.3 Alat Uji Konduktivitas Termal... 28
Gambar 3.4 Alat Uji Penyerapan Suara………... 29
Gambar 3.5 Proses Pengayakan Pasir………... 30
Gambar 3.6 Proses Penimbangan Semen dan Pasir……... 30
Gambar 3.7 Proses Pembuatan Pasta Mortar... 31
Gambar 3.8 Proses Pembuatan Busa Foam Agent... 31
Gambar 3.9 Proses Pencampuran Busa Foam Agent dengan Pasta Mortar... 32
Gambar 3.10 Proses Pencetakan Beton Busa…………... 32
Gambar 3.11 Proses Pengujian Sound Absorption (Penyerapan Suara)... 34
Gambar 3.12 Proses Pengujian Konduktivitas Termal Beton Busa... 35
Gambar 3.13 Flow Chart………..... 36
Gambar 4.1 Hubungan Antara Jumlah Foam agent dan Densitas... 38
Gambar 4.2 Hubungan Antara Jumlah Foam agent dan Densitas... 38
Gambar 4.3 Hubungan Konduktivitas Termal dengan Penambahan Foam Agent pada Beton Busa... 40
Gambar 4.4 Hubungan Konduktivitas Termal dan Komposisi Campuran... 41
Gambar 4.5 Hubungan Konduktivitas Termal dengan Densitas... 42
Gambar 4.7 Hubungan Koefisiensi Penyerapan Suara dengan Frekuensi... 46
Gambar 4.8 Hubungan Koefisiensi Rerata Penyerapan Bunyi dengan Prosentase
[image:17.595.153.442.271.564.2]Foam………... 48
DAFTAR PUSTAKA
ASTM C 138/138M-01a, tentang “Standart Test Method for Density (Unit Weight),
Yield and Air Content (Gravimetric) of Concrete”.
ASTM C 177-97, tentang “Standard Test Method for Steady-State Heat Flux Measurments and Thermal Transmission Properties by Means of the
Guarded-Hot-Plate Apparatus”.
ASTM C 384, tentang “Standard Test Method for Impedance and Absorption of Materials by Impedance Tube Method”.
ASTM C 1044-98, tentang “Standard Practice for Using a Guarded-Hot-Plate Apparatus or Thin-Heater Apparatus in the Single-Sides Mode”.
Http://digilib.unimed.ac.id/public/UNIMED-Undergraduate-22345-BAB%202.pdf
(Diakses tgl 25-08-2015)
Http://hypertextbook.com/facts/1999/KatrinaJones.shtml(Diakses tgl 25-12-2015) Malau, F. Blasius., 2014, “Penelitian Kuat Tekan dan Berat Jenis Mortar untuk Dinding Panel dengan Membandingkan dengan Penggunaan Pasir Bangka dan
Pasir Baturaja dengan Tambahan Foaming Agent dan Silica Fume”. Jurnal
Teknik Sipil dan Lingkungan Vol.2. No.2, Juni 2014, ISSN 2355-374X,
Universitas Sriwijaya, Palembang.
Pradana Susanto, Eka dkk., 2012, Studi Penggunaan Dinding Foam Concrete (FC)
dalam Efisiensi Energi dan Biaya untuk Pendinginan Udara ( Air Conditioner
), Institut Teknologi Bandung, Bandung.
RSNI T-05-2005, tentang “Metode Pengujian Penyerapan Bunyi Pada Bahan Akustik Dengan Metode Tabung”.
Safrianti, Nina. 2014, Studi Daya Tahan Api, Serap Suara dan Konduktivitas Termal
Pada Dinding Bata Kertas (Peperbrick) Menggunakan Kertas Koran, Jurusan
Teknik Sipil, Universitas Syah Kuala Darussalam, Banda Aceh.
BAB I PENDAHULUAN 1.1 Latar Belakang
Dinding beton ringan adalah dinding non struktur yang memiliki kuat tekan
minimum dibawah kuat tekan beton normal, namun memiliki massa jenis beton yang
rendah. Salah satu jenis beton ringan yang digunakan dalam penelitian ini adalah
Beton busa (Foamed Concrete) yang memanfaatkan foam agent sebagai bahan
tambahan yang berfungsi sebagai bahan pengembang beton agar lebih ringan dan
mampu menyerap panas.
Sifat Foamed Concrete yang mampu menyerap panas ini sangat sesuai dengan
wilayah Indonesia yang beriklim tropis, dimana suhu rata-rata harian cukup tinggi
yaitu sekitar 25°-32° C. Dinding bangunan biasa kurang bisa menyerap panas yang
diterima dari sinar matahari sehingga suhu dalam ruangan pun menjadi naik dan
panas. Pada umumnya masyarakat mengatasi masalah suhu dalam ruangan dengan
pemasangan AC (Air Conditioner), padahal cara ini tidak ramah lingkungan dan
cenderung tidak hemat energy.
Beton busa biasanya digunakan sebagai dinding non struktur yang mampu
menyerap panas dan meredam suara. Fungsi penyerapan panas ini dimaksudkan
untuk mengatur suhu dalam ruangan agar tidak terlalu panas sehingga dapat
mengurangi penggunaan pendingin ruangan (AC) yang tidak ramah lingkungan.
Sedangkan fungsi peredam suara adalah agar kegiatan yang dilakukan di dalam
1.2 Rumusan Masalah
Rumusan masalah dari penelitian ini adalah :
1. Bagaimana nilai densitas yang dimiliki oleh beton busa?
2. Berapa besar nilai konduktivitas termal yang dihasilkan dari variasi persentase
penambahan foam agent?
3. Berapa besar nilai sound absorpsion yang dihasilkan dari variasi persentase
penambahan foam agent?
1.3 Batasan Masalah
Batasan masalah yang menjadi pokok pembahassan tidak meluas dan
menyimpang dari tujuan. Adapun batasan masalah dari skripsi ini adalah :
1. Tidak membahas reaksi kimia yang terjadi pada campuran foam agent dan
bahan penyusun beton busa lainnya.
2. Tidak melakukan pengujian kimia pada bahan penyusun beton busa
3. Pembuatan alat uji konduktivitas termal berdasarkan ASTM C177-97.
4. Pembuatan alat uji sound absorption berdasarkan ASTM 384-04.
5. Merupakan penelitian pendahuluan untuk mengetahui karakteristik fisik beton
busa yang nantinya akan di aplikasikan sebagai bahan dinding non-struktur
(panel) pada sebuah bangunan konstruksi.
1.4 Tujuan Penelitian
Tujuan dari penelitian ini adalah :
1. Mengetahui nilai densitas yang dimiliki oleh beton busa.
2. Mengetahui besar nilai konduktivitas termal yang dihasilkan dari variasi
3. Mengetahui besar nilai sound absorbsion yang dihasilkan dari variasi
persentase penambahan foam agent.
1.5 Manfaat Penelitian
Manfaat dari penelitian ini adalah :
1. Secara tidak langsung dapat membantu penghematan energy dalam hal
pengaturan suhu ruangan dengan penggunaan beton busa.
2. Sebagai sumbangsih akademisi dalam memberikan informasi dan