PERANAN DIVINIL BENZENA TERHADAP KOMPATIBILITAS CAMPURAN LOW DENSITY POLYETHYLENE (LDPE) DAN ABU BAN BEKAS MENGGUNAKAN INISIATOR DIKUMIL PEROKSIDA

N/A
N/A
Protected

Academic year: 2021

Membagikan "PERANAN DIVINIL BENZENA TERHADAP KOMPATIBILITAS CAMPURAN LOW DENSITY POLYETHYLENE (LDPE) DAN ABU BAN BEKAS MENGGUNAKAN INISIATOR DIKUMIL PEROKSIDA"

Copied!
14
0
0

Teks penuh

(1)

PERANAN DIVINIL BENZENA TERHADAP KOMPATIBILITAS

CAMPURAN LOW DENSITY POLYETHYLENE (LDPE) DAN

ABU BAN BEKAS MENGGUNAKAN INISIATOR

DIKUMIL PEROKSIDA

SKRIPSI

DEWI ANJARSARI SINAGA

060802014

DEPARTEMEN KIMIA

FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM

UNIVERSITAS SUMATERA UTARA

MEDAN

2011

(2)

PERANAN DIVINIL BENZENA TERHADAP KOMPATIBILITAS CAMPURAN LOW DENSITY POLYETHYLENE (LDPE) DAN

ABU BAN BEKAS MENGGUNAKAN INISIATOR DIKUMIL PEROKSIDA

SKRIPSI

Diajukan untuk melengkapi tugas dan memenuhi syarat mencapai gelar Sarjana Sains

DEWI ANJARSARI SINAGA 060802014

DEPARTEMEN KIMIA

FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM UNIVERSITAS SUMATERA UTARA

MEDAN 2011

(3)

PERSETUJUAN

Judul : PERANAN DIVINIL BENZENA TERHADAP KOMPATIBILITAS CAMPURAN LOW DENSITY POLYETHYLENE (LDPE) DAN ABU BAN BEKAS MENGGUNAKAN INISIATOR DIKUMIL PEROKSIDA

Kategori : SKRIPSI

Nama : DEWI ANJARSARI SINAGA

Nomor Induk Mahasiswa : 060802014

Program Studi : SARJANA (S-1) KIMIA

Departemen : KIMIA

Fakultas : MATEMATIKA DAN ILMU PENGETAHUAN ALAM (FMIPA) UNIVERSITAS SUMATERA UTARA

Diluluskan di: Medan, 19 Mei 2011

Komisi Pembimbing:

Pembimbing II Pembimbing I

Dr. Darwin Yunus Nasution, MS Drs. Amir Hamzah Siregar, M.Si. NIP. 195508101981031001 NIP. 196106141991031002

Diketahui/Disetujui oleh:

Departemen Kimia FMIPA USU Ketua,

DR. Rumondang Bulan Nst, MS. NIP. 195408301985032001

(4)

PERNYATAAN

PERANAN DIVINIL BENZENA TERHADAP KOMPATIBILITAS CAMPURAN LOW DENSITY POLYETHYLENE (LDPE) DAN

ABU BAN BEKAS MENGGUNAKAN INISIATOR DIKUMIL PEROKSIDA

SKRIPSI

Saya mengakui bahwa skripsi ini adalah hasil kerja saya sendiri, kecuali beberapa kutipan dan ringkasan yang masing-masing disebutkan sumbernya.

Medan, 19 Mei 2011

Dewi Anjarsari Sinaga 060802014

(5)

PENGHARGAAN

Syukur Alhamdulillah penulis ucapkan kepada Allah SWT, pemberi rahmat atas ciptaan-Nya, pemilik hidayah hingga ditunjuknya orang – orang yang menempuh jalan kebenaran, sekaligus pemilik kesesatan hingga disesatkan orang – orang yang menempuh jalan aniaya. Serta sholawat dan salam atas junjungan Nabi Muhammad SAW, keluarga, sahabat dan pengikut – pengikutnya yang senantiasa mengajarkan makna hidup sehingga penulis senantiasa termotivasi untuk berjuang hingga waktu selesainya penelitian ini dan menjadi sebuah skripsi.

Penulis menyampaikan terima kasih kepada kedua orangtua yang senantiasa mendoakan dan memotivasi penulis dengan penuh kasih sayang dan pengorbanan yakni kepada Ayahanda Jaya Supena Sinaga dan Ibunda Nurmala Purba sehingga penulis sampai pada jenjang saat ini semoga kelak Allah menempatkan ditempat yang layak. Kepada abang tersayang Prasetio Anggi kusuma Sinaga serta tiga adik tersayang Anggun Paramita Sinaga, M. Gunawan Sinaga, dan M. Soleh Sinaga yang senantiasa memberikan perhatian dan dorongan yang tak ternilai harganya hingga selesainya penulisan skripsi ini.

Pada kesempatan ini dengan segala kerendahan dan ketulusan hati penulis mengucapkan terimakasih yang sebesar-besarnya kepada:

1. Bapak Drs. Amir Hamzah Siregar,M.Si, dan Almr. Bapak Drs. Syamsul Bachri Lubis, M.Si. selaku Pembimbing I dan Pembimbing II yang telah banyak membantu penulis dan memberi bimbingan kepada penulis hingga selesainya skripsi ini.

2. Bapak Dr. Darwin Yunus Nasution, MS selaku pengganti pembimbing II, terima kasih atas kesediaan Bapak.

3. Ibu Hj. Dr. Rumondang Bulan, MS selaku ketua jurusan Kimia Fakultas Matematika Dan Ilmu Pengetahuan Alam USU.

4. Bapak Drs. Albert Pasaribu, M.Sc selaku sekretaris jurusan Kimia Fakultas Matematika Dan Ilmu Pengetahuan Alam USU.

(6)

5. Kepala dan Staf Laboratorium Kimia Fisika dan Polimer yang telah memberikan bimbingan dan masukan serta saran kepada penulis selama melakukan penelitian

6. Buat sahabat seperjuangan ( Kak reje, Kak wiji, Kak Alfi, Kak Endang, Kak Dewi, Bibah, Mimi, Endah, Inur, Susi, Izut, Yuni, Rina, Titin, Ela, Fini, Femy, Eza dan Eka) tetap semangat & Semoga diberi kekuatan oleh Allah hingga janji itu terwujud. Rekan-rekan seperjuangan kimia stambuk 2006 terutama (Hary, Mardiana, Nora, Febry, Fitri, fatma, Nelvi, dan Rani).

7. Serta teman – teman yang tidak bisa dituliskan satu persatu terima kasih atas bantuan dan dukungannya.

Penulis menyadari banyak kekurangan dalam penulisan skripsi ini, karena itu penulis menerima saran yang bersifat membangun untuk penyempurnaan skripsi ini. Semoga skripsi ini berguna untuk penelitian selanjutnya dan untuk kemajuan kita bersama.

Medan, 19 Mei 2011

(7)

ABSTRAK

Dalam penelitian ini telah dilakukan perbandingan campuran LDPE (50 gr)-Abu Ban Bekas (50 g) dengan variasi konsentrasi inisiator DKP (1,2,3 phr) dan variasi konsentrasi bahan pengikat silang DVB (0,1,2,3 phr). Dari hasil pencampuran LDPE (50 g)-Abu Ban Bekas (50 g)-dengan variasi konsentrasi DKP 2 phr diperoleh kekuatan tarik dan kemuluran optimum 0,89 kgf/mm2 dan 89,66 %. Sedangkan pencampuran LDPE (50 g)-Abu Ban Bekas (50 g) dengan konsentrasi 2 phr DKP dan 2 phr DVB diperoleh kekuatan tarik dan kemuluran optimum 1,04 kgf/mm2 dan 157,9%. Dari analisis SEM menunjukkan adanya pengaruh penambahan DVB yaitu dihasikannya permukaan yang lebih rata dan homogen. Dari hasil analisis FT-IR memperlihatkan bahwa tidak ada perubahan gugus fungsi, dan interaksi yang terjadi hanya interaksi fisik. Sedangkan data analisa kandungan gel menunjukkan bahwa pada campuran variasi konsentrasi LDPE-Abu Ban Bekas-DKP-DVB (b/b) : 2 phr : 2 phr menghasilkan persentase kandungan gel lebih besar karena semakin kuatnya interaksi antara komponen-komponen penyusun campuran sehingga pelarut xilena tidak dapat melarutkannya.

(8)

THE ROLE OF ADDING DIVINYL BENZENE ON THE COMPATIBILITY BLENDING POLYETHYLENE (LDPE) AND WASTE TYRE DUST

INITIATOR DICUMYL PEROXIDE

ABSTRACT

In the research has been done, blending ratio of LDPE (50 g)-waste tyre dust (50 g) variation of concentration initiator DCP (1,2,3 phr) and variation of concentration crosslink agent DVB (0,1,2,3 phr). From blending LDPE (50 g)-waste tyre dust (50 g) with concentration DCP 2 phr was found tensile strength and elasticity optimum 0,89 kgf/mm2 and 89,66 %. While blending LDPE (50 g)-waste tyre dust (50 g) with concentration 1 phr DCP and 2 phr DVB was found tensile strength and elasticity optimum1,04 kgf/mm2 and 157,9 %. From the SEM analysis result was obtained that the addition of divinylbenzene could improve surface become more flat and homogeneus. From the functional group analysis FT-IR showed functional group is not change and interaction occurring only physical interaction. Analysis of gel content indicated blending variation of concentration Low Density Polyethylene (LDPE) (50 g)-waste tyre dust (50 g)-DCP-DVB 2 phr : 2 phr blending see xylene solvent no able dissolve.

(9)

DAFTAR ISI Halaman Persetujuan ii Pernyataan iii Penghargaan iv Abstrak vi Abstract vii

Daftar isi viii

Daftar gambar x

Daftar tabel xi

Daftar lampiran xii

Daftar singkatan xiii

BAB 1 PENDAHULUAN 1.1 Latar Belakang 1 1.2 Perumusan Masalah 3 1.3 Pembatasan Masalah 3 1.4 Tujuan Penelitian 3 1.5 Manfaat Penelitian 4 1.6 Lokasi Penelitian 4 1.7 Metodelogi Percobaan 4

BAB 2 TINJAUAN PUSTAKA

2.1 Polietilen 6

2.2 Ban Bekas 8

2.3 Dikumil Peroksida 9

2.4 Divinil benzena 11

2.5 Xilena 11

2.6 Karakterisasi Campuran Polimer 12

2.6.1 Analisis FT-IR(Fourier Transform Infrared Spectroscopy 12 2.6.2 Skaning Elektron Mikroskopi (SEM) 15 2.6.3 Kandungan Gel (derajat sambung silang) 15

(10)

BAB 3 METODE PENELITIAN

3.1 Alat 18

3.2 Bahan 18

3.3 Prosedur 19

3.3.1 Preprasi Sampel 19

3.3.2 Pembuatan campuran polimer LDPE dan Abu Ban Bekas 19 3.3.3 Pembuatan campuran LDPE dan Abu Ban Bekas 19 3.3.4 Pembuatan campuran LDPE, Abu Ban Bekas, DKP dan DVB 20 3.4 Pembuatan Film Spesimen Hasil poliblen 20

3.5 Analisa dan Karaterisasi 20

3.5.1 Specimen kekuatan tarik 21

3.5.2 Analisa Permukaan dengan SEM 21

3.5.3 Analisa Spektroskopi Infra Merah (FTIR) 22

3.6 Analisa Data 22

3.7 Skema Pengambilan data 24

3.7.1 Pencampuran LDPE-Abu Ban Bekas 24

3.7.2 Pencampuran LDPE-Abu Ban Bekas-DKP 25 3.7.3 Pencampuran LDPE-Abu Ban Bekas-DKP -DVB 26

BAB 4 HASIL DAN PEMBAHASAN

4.1 Hasil 27

4.1.1 Pengujian sifat mekanik berdasarkan kekuatan tarik (σt) dan

kemuluran (ε) 27

4.2 Analisis Uji Mekanis dengan Uji Tarik 29

4.3 Scanning Elektroan Microscope (SEM) 32

4.4 Analisa gugus fungsi dengan FT-IR 32

4.5 Kandungan Gel (Penentuan Derajat Sambung Silang) 34 4.6 Rancangan Mekanisme Reaksi Termoplastik Elastomer 35

BAB 5 KESIMPULAN DAN SARAN

5.1 Kesimpulan 37

5.2 Saran 37

Daftar Pustaka 38

(11)

DAFTAR GAMBAR

Halaman

Gambar 2.1 Struktur rantai polietilena 6

Gambar 2.2 Struktur dikumil peroksida 9

Gambar 2.3 Reaksi dekomposisi dikumil peroksida 10

Gambar 2.4 Struktur divinil benzena 11

Gambar 3.1 Spesimen uji kekuatan tarik berdasarkan ASTM D 638 21 Gambar 4.1 Grafik kekuatan tarik (σt) pada campuran TPE tanpa penambahan

DVB 29

Gambar 4.2 Grafik kemuluran (ε) pada campuran TPE tanpa penambahan DVB 30 Gambar 4.3 Grafik kuat tarik (σt) pada campuran TPE dengan penambahan DVB 30 Gambar 4.4 Grafik kemuluran (ε) pada campuran TPE dengan penambahan DVB 31

Gambar 4.5 Data hasil pengujian SEM 32

Gambar 4.6 Kandungan gel 34

(12)

DAFTAR TABEL

Halaman

Tabel 2.1 Sifat-sifat xilena 12

Tabel 4.1 Hasil pengujian kekuatan Tarik (σt) dan kemuluran (ε) Termoplastik Elastromer (TPE) terhadap pengaruh perbandingan variasi konsentrasi

DKP 27

Tabel 4.2 Hasil pengujian kekuatan Tarik (σt) dan kemuluran (ε) Termoplastik elastomer (TPE) terhadap penambahan variasi konsentrasi DKP

dengan variasi konsentrasi DVB 28

Tabel 4.3 Hasil analisis gugus fungsi LDPE dan abu ban bekas dengan

Menggunakan FT-IR 33

Tabel 4.4 Hasil analisis gugus fungsi LDPE, abu ban bekas, 2 phr DVB

(13)

DAFTAR LAMPIRAN

Halaman

Lampiran 1. Data kandungan gel campuran 42

Lampiran 2. Spektrum FT-IR LDPE-Abu Ban Bekas 43

(14)

DAFTAR SINGKATAN

DKP : Dikumil peroksida DVB : Divinil benzena

LDPE : Low Density Polyethylene HVA-2 : N,N’-m-phenylenebismaleimide Phr : Perseratus rubber

ASTM : American standart fortesting of material Kgf : kilogram force

FTIR : Fourier Transform Infrared Spectroscopy SEM : Skanning Elektron Mikroskopi

Referensi

Dokumen terkait

Sidik Ragam Pengaruh Konsentrasi dan Frekuensi Aplikasi Isoprothiolane terhadap Jumlah Polong Hampa Tiap Tanaman .... Sidik Ragam Pengamh Konsentrasi dan Frekuensi

Walaupun HBA dari beberapa metode pemrosesan menghasilkan kecernaan yang berbeda-beda, akan tetapi hasil pemanfaatan HBA dalam ransum ruminansia memberikan respon yang lebih baik

Identitas Bapak/Ibu tidak dicantumkan dalam kuesioner ini, untuk itu saya mohon penilaian sejujurnya untuk peningkatan kinerja bawahan Bapak/Ibu. Atas bantuan dan kerjasama

• Dokumen PDF dapat berisi higher-level information yang berguna untuk pertukaran isi dari berbagai aplikasi • Isi dokumen menyertakan identifikasi dan struktur. logika

Melalui latar belakang masalah yang ada, maka dilakukan penelitian yang bertujuan untuk merancang Sistem Monitoring Nilai Proses Belajar Mengajar Suatu Matakuliah pada

Penelitian ini bertujuan untuk mengetahui :1) Mengetahui perbedaan pengaruh penggunaan pendekatan konstruktivisme dengan metode inkuri terbimbing dan metode

Namun demikian, lokasi dari kegiatan ini yaitu pada area lego jangkar perairan Tanjung Perak yang ramai dimana selama proses ship to ship transfer berlangsung terdapat kapal –

Ada 14 cabang olahraga yang sama dipertandingkan baik di Asian Games dan Asian Para Games 2018, cabang itu adalah: atletik, badminton, tenis, basket, panahan, balap