Pengaruh Buah Asam Jawa (Tamarindus Indica L.) Sebagai Penggumpal Lateks Alam Terhadap Mutu Karet

PEMANFAATAN BUAH ASAM JAWA (

Tamarindus Indica L.

)

SEBAGAI PENGGUMPAL LATEKS ALAM

TERHADAP MUTU KARET

ABSTRAK

Telah dilakukan penelitian mengenai pemanfaatan buah asam jawa (Tamarindus

Indica L.) sebagai penggumpal lateks dengan penambahan variasi konsentrasi

buah asam jawa 10 % ; 20 % ; dan 30 % dan variasi suhu 25

0

C ; 30

0

C ; dan 35

0

C.

Sebagai kontrol digunakan asam formiat sebagai penggumpal lateks dengan

penambahan amonia 2,5 % dan tanpa amonia. Terhadap karet kering hasil

penggumpalan selanjutnya dilakukan pengujian mutu berupa Plastisitas Awal

(Po), Plastisitas Retensi Index (PRI), Viskositas Mooney, Kadar Kotoran, Kadar

Abu, dan Kadar Karet Kering (KKK). Dari hasil penelitian menunjukkan variasi

konsentrasi buah asam jawa (Tamarindus Indical L.) 10 % pada suhu 30

0

C tanpa

menggunakan amonia memiliki nilai Plastisitas Awal (Po) adalah 52 ; Plastisitas

Retensi Index (PRI) adalah 68,01 % ; Viskositas Mooney adalah 91,2857 ; Kadar

Abu adalah 0,106 % ; Kadar Kotoran adalah 0,015 % ; dan Kadar Karet Kering

(KKK) adalah 79,071%. Hasil penelitian variasi konsentrasi buah asam jawa

(Tamarindus Indica L.) 10 % pada suhu 25

0

dengan menggunakan amonia

memiliki nilai Plastisitas Awal (Po) adalah 53,33 ; Plastisitas Retensi Index (PRI)

adalah 96,24 % ; Viskositas Mooney adalah 80,7142 ; Kadar Abu 1,166 % ;

Kadar Kotoran 0,024 % ; dan Kadar Karet Kering (KKK) adalah 36,318 % serta

sifat fisika yang dihasilkan menurut Standar Indonesia Rubber (SIR) 20.

Kata Kunci : Amonia, Asam Formiat, Buah Asam Jawa (Tamarindus Indica L.),

Standar Indonesia Rubber (SIR) 20.

UTILIZATION OF FRUIT TAMARIND (Tamarindus indica L.)

AS A NATURAL LATEX COAGULANT

QUALITY OF RUBBER

ABSTRACT

The research about

tamarind fruit (Ta marindus indica L.) had been done as a

coagulant latex with the addition of tamarind fruit concentration variation of 10

% ; 20 % ; and 30% and temperature variations 25

0

C ; 30

0

C ; and 35

0

C. Formic

acid were used as a control for coagulant of latex with the addition of ammonia

2,5 % and without ammonia. Quality test of rubber that formed wa s considered by

measure the value of Early P lasticity (Po), Plasticity Retention Index (PRI),

Mooney Viscosity, Dirt Content, Ash Content, and The Dry Rubber Content

(KKK). The results of reasearch shows that value variations in the concentration

of tamarind fruit (Tamarindus Indical L.) 10% at a temperature of 30

0

C without

ammonia has a value Initia l Plasticity (Po) is 52 ; Plasticity Retention Index

(PRI) is 68.01 % ; Mooney Viscosity is 91.2857 ; Ash Content is 0.106 % ; Dirt

Content is 0.015 % ; and The Dry Rubber Content (KKK) is 79.071 %. The result

of variations in the concentration of tamarind fruit (Tama rindus Indica L.) 10 %

at a temperature of 25

0

C with the addition of ammonia has a value Initial

Plasticity (Po) is 53,33 ; Plasticity Retention Index (PRI) is 96,24 % ; Mooney

Viscosity is 80, 7142 ; Ash Content is 1,166 % ; Dirt Content is 0,024 % ; and The

Dry Rubber Content (KKK) is 36,318 % and the resulting physical properties

according to Standard Indonesian Rubber (SIR) 20.

Keywords :

Ammonia, Formic Acid, Tama rind Fruit, Standard Indonesian Rubber

(SIR) 20.