PEMANFAATAN LIMBAH PADAT PECAHAN BETON DAN DINDING BATA SEBAGAI PENGGANTI AGREGAT KASAR PADA PEMBUATAN
BETON NORMAL
Dibuat untuk Memenuhi Syarat dalam Menyelesaikan
Pendidikan Diploma III Jurusan Teknik Sipil Konsentrasi Transportasi Politeknik Negeri Sriwijaya
Disusun Oleh : 1. Nama : Latifah Safitri
Nim : 0610 3010 0729
2. Nama : Melisa Putri Wulandari Nim : 0610 3010 0731
JURUSAN TEKNIK SIPIL POLITEKNIK NEGERI SRIWIJAYA
PEMANFAATAN LIMBAH PADAT PECAHAN BETON DAN DINDING BATA SEBAGAI PENGGANTI AGREGAT KASAR PADA PEMBUATAN
BETON NORMAL
LAPORAN AKHIR
Disetujui oleh Pembimbing
Laporan Akhir Jurusan Teknik Sipil
Politeknik Negeri Sriwijaya
Pembimbing I, Pembimbing II,
Ir. Kosim, M.T Ika Sulianti , S.T.,M.T NIP. 196210181989031002 NIP.198107092006042001
Mengetahui,
Ketua Jurusan Teknik Sipil Politeknik Negeri Sriwijaya
PEMANFAATAN LIMBAH PADAT PECAHAN BETON DAN DINDING BATA SEBAGAI PENGGANTI AGREGAT KASAR PADA PEMBUATAN
BETON NORMAL
LAPORAN AKHIR
Disetujui Oleh Penguji
Laporan Akhir Jurusan Teknik Sipil Politeknik Negeri Sriwijaya
Nama Penguji Tanda Tangan
1. Andi Herius, S.T ………...
NIP. 197609072001121002
2. Amiruddin, S.T.,M.Eng Sc. ………... NIP. 197005201995031001
3. Drs. Bambang Hidayat Fuady., S.T., M.M ………... NIP. 195807161986031004
4. Drs. Yurpino ... NIP.195911261986031001
5. Drs.Mochammad Absor, M.T ... NIP. 195801121989031008
6. Ir. Kosim., M.T ………...
PEMANFAATAN LIMBAH PADAT PECAHAN BETON DAN DINDING BATA SEBAGAI PENGGANTI AGREGAT KASAR PADA PEMBUATAN
BETON NORMAL
LAPORAN AKHIR
Disetujui Oleh Penguji
Laporan Akhir Jurusan Teknik Sipil Politeknik Negeri Sriwijaya
Nama Penguji Tanda Tangan
1. Ir. Puryanto, M.T ………...
NIP. 195802161988111001
2. Ir. Effendy Susilo, M.T ………... NIP. 195205181984031001
3. Drs. Raja Marpaung, S.T.,M.T ………... NIP. 195706061988031001
4. Lina Flaviana Tilik , S.T.,M.T ... NIP. 197202271998022003
5. M. Sazili Harmawansyah, S.T ... NIP. 197207012006041001
6. Indrayani, S.T., M.T ... NIP. 197402101997022001
Memori perjuangan senantiasa berdiri disamping saya dengan kesetiaan dan cinta yang selalu dihadirkan dan memiliki pengaruh besar atas diri saya selama ini . . . :
ALLAH SWT dan Baginda Rasulullah Muhammad SAW. Kedua Orang tua, adik – adik saya serta Keluarga Besar.
Saudari yang senantiasa dalam ikatan cinta yang terjaga, cc Pratiwi Eka Putri, Msy Anggun NR, Fatimah Tuzzahra, Ami Caresya, dan Lia W.A Dosen teristimewa, Ibu Ika Sulianti S.T.,M.T yang senantiasa memberikan
waktu tanpa batas untuk kami dan menjadi motivator yang nyata dalam diri saya. Serta Bapak Ir. Kosim, M.T yang senantiasa memberikan pengarahan dan motivasi bagi saya dan rekan – rekan mahasiswa lainnya. dan tentu saja Melisa Putri Wulandari yang menjadi solid team work
sehingga semua telah rampung menjadi “ 115 halaman bersampul coklat” serta Etty Oktaria, Resy Indah Syari, Retno Tiyas Utami dan sekali lagi
Melisa Putri W, yang benar – benar mengisi Memori 3 tahun Terbaik dibangku kuliah...
... Dan yang saya sebut “115 halaman bersampul coklat ” tidak akan pernah bersampul tanpa mereka yang bersedia berdiri dibelakang saya memberikan motivasi secara nyata dan meninggalkan jejak memori yang tentu saja tidak akan pernah usang. Dengan bangga saya ucapakan terima kasih, kepada :
Almamater Politeknik Negeri Sriwijaya
persaudaraan bersama kalian” .. Sungguh, ingatan bersama kalian akan menjadi “nostalgila terindah” yang akan terekam rapi dimemori saya. Bapak Munada Asro, Pak Amiruddin, Pak Helan, Pak Bandi Purniawan,
Bu. Sumi, Pak Andi Herius,yang senantiasa mengarahkan dan membimbing selama proses menjadi “kuli beton”
Dan untuk Siti Ulfa Aziza dan Siti Maya Sari, terima kasih telah menjadi “kawan becak” yang setia
Terkhusus yang telah berperan dalam rampungnya “115 halaman bersampul coklat” selama prosesnya, cc Chorial Champelo, Etty Oktaria, Retno Tiyas Utami, Eric Dwi Permadi, Firlin Cardinata, Royete Marice, Caisar Arfy, dan Romiza Wijaya, terima kasih atas ketersediaannya membantu kami
“
Suatu Kehormatan Bisa menjadi Bagian dari Keluarga
Besar Politeknik Negeri Sriwijaya
”
MOTTO
Katakanlah “hai hamba2ku yang melampaui batas terhadp diri
sendiri, janganlah kamu berputus asa dr rahmat Allah
(az-zumar : 53)
Ketika ingin melihat pelangi, ada matahari dan hujan Ketika ingin
sukses, harus ada keringat dan air mata... ( melisa PW)
I’ve no special talent, I’m only passinately curious.”
“it’s not that I’m so smart, it’s just that I say with the problem
longer.” (Albert Einstein)
Jadikanlah kesuksesanmu itu tujuan hidup. Dimana bahagia itu
benar2 memenangkan hati. Bukan malah semakin meresahkan dan
takut.
Kegagalan memberimu kekuatan dan bahan bakar semangat yang
lebih hebat untuk lebih berani dan gentar mewujudkan mimpimu..
Laporan akhir ini aku persembahkan :
Allah SWT Tuhan Semesta Alam
Suri Tauladanku Nabi Muhammad SAW
Terutama dan utama untuk ayahku YUSMAN EFFENDI AB dan
ibuku SRI ENDANG HASTUTI yang selalu memberikan
dukungannya, nasehat, dan tiada lelah untuk selalu mengingatkan
aku untuk selalu bersyukur dan bersemangat. Terimaksih untuk
kasih sayangnya, dengan kening keriput yang dibasahi keringat..
terimakasih .. you are my inspiration and my motivation love you
Untuk saudara-saudaraku ayukku Okta liantini, septi Ariani, Nova
Apriani, Anta liandri, Ria Feronika, dan adikku Oktia sherlina dan
Dina Arenza Reka dora yang selalu mensupportku dan
memotivasiku untuk membanggakan ke-2 orangtua kita...
Untuk dosen pembimbingku pak Ir Kosim MT terimakasih atas
bimbingan dan nasehatnya..
untuk dosen pembimbingku ibu Ika sulianti ST MT terimakasih
untuk semuanya, bimbingan dan pengertian serta nasehat –
nasehat yang diberikan.. makasih bu.. :D
untuk partner, sahabat, teman, saudara semuanya ada pada Latifah
Safitri (LATEP) terimaksih untuk sabar dalam menghadapiku,,
sooo nice ehhehe :D
untuk Funtut ( etty, latifah, melisa ),, terimaksih untuk selalu
memahamiku, dari mulai magang semua sikap keluar, sampai
Laporan ini selesai,,,
semua teman-teman yang membantu kami pada saat di
laboraturium,, Chorial, Retno, Widya, Firlin, Eric, Caisar, Romiza.
Untuk Bapak Munada, Pak Amir, Pak Bandi, Pak Helan, dan Bu
Judul : Pemanfaatan Limbah Padat Pecahan Beton dan Dinding Bata sebagai Pengganti Agregat Kasar dalam Pembuatan beton normal ( Latifah Safitri, Melisa Putri Wulandari , 17 Juli 2013, 115 halaman)
ABSTRAK
Beton merupakan campuran yang tersusun atas agregat kasar (batu pecah dan batu tidak pecah), agregat halus ( pasir), semen dan air dengan atau tanpa bahan tambah. Pembanguanan infrastukur mulai dai bangunan gedung, jalan dan jembatan menggunakan beton, hal ini menunjukkan banyaknya penggunaan beton dalam pembangunan. Perkembangan teknologi beton dituntut untuk memenuhi kebutuhan dalam pembangunan tersebut. Agregat kasar mempunyai komposisi yang paling banyak dalam campuran beton. Hal ini mengakibatkan menipisnya sumberdaya alam yang ada. Pemakaian benda limbah padat buangan sebagai bahan pengganti agregat kasar di harapkan mampu mengurangi penggunaan material alam. Limbah padat tersebut dapat berupa pecahan genteng, pecahan dinding bata, bongkaran bangunan lainnya. Pemanfaatan limbah padat dalam hal ini yaitu pecahan dinding bata dan dinding beton sebagai pengganti agregat kasar. Dengan variasi komposisi yang berbeda – beda, untuk menentukan komposisi mana yang lebih baik dari beberapa komposisi rencana. Adapun variasi komposisi tersebut yaitu limbah pecahan dinding bata 0% dan limbah pecahan dinding beton 100%, limbah pecahan dinding bata 20% dan limbah pecahan dinding beton 80%, limbah pecahan dinding bata 40% dan limbah pecahan dinding beton 60%, limbah pecahan dinding bata 60% dan limbah pecahan dinding beton 40%, limbah pecahan dinding bata 20% dan limbah pecahan dinding beton 80%, limbah pecahan dinding bata 100% dan limbah pecahan dinding beton 0%. Dengan pengujian umur 3 hari, 7 hari, 14 hari, 21 hari, 28 hari. Dari hasil pengujian di dapat proporsi campuran yang memenuhi kuat tekan rencana limbah pecahan dinding bata 20% dan limbah pecahan dinding beton 80%.
Title: Fractional utilization of solid waste concrete and brick walls as a subtitute for coarse agregate in concrete manufacture norma
( Latifah Safitri, Melisa Putri Wulandari , 17 Juli 2013, 115 pages)
ABSTRACT
Concrete is a mixture composed of coarse aggregate (crushed stone and rock is not broken), fine aggregate (sand), cement and water with or without added ingredients. For Development infrastukur began dai buildings, roads and bridges using concrete, it demonstrates to the use of concrete in construction. Development of concrete technology required to meet the needs of the development. Coarse aggregate composition having the most in the concrete mix. This resulted in the depletion of natural resources. Use of objects as solid waste discharges coarse aggregate replacement material is expected to reduce the use of natural materials. The solid waste can be broken tiles, broken brick wall, demolition of other buildings. Utilization of solid waste in this case is broken masonry and concrete walls as a substitute for coarse aggregate. With a variety of different composition - different, to determine the composition of which is better than some of the composition plan. The variations in the composition of the waste fractions brick walls and waste fractions 0% 100% concrete walls, brick walls broken sewage and waste 20% 80% fractional concrete walls, brick walls broken sewage and waste 40% 60% broken concrete walls, wall fractions of waste 60% waste brick and concrete wall fraction 40%, waste brick wall fraction 20% and waste 80% broken concrete walls, brick walls broken sewage and waste fractions 100% 0% concrete wall. By testing the age of 3 days, 7 days, 14 days, 21 days, 28 days. From the test results on the mixture proportions can meet compressive strength plan for broken brick wall of waste fractions 20% and 80% concrete wall.
KATA PENGANTAR
Puji dan syukur penulis panjatkan kehadiran Allah SWT, karena atas berkat rahmat dan karunia-Nya penulis dapat menyelesaikan Laporan Akhir ini dengan judul “Pemanfaatan Limbah Padat Pecahan Dinding Beton dan Dinding Bata sebagai Pengganti Agregat Kasar Pada Pembuatan Beton Normal”. Sholawat serta salam tidak lupa penulis curahkan kepada Baginda Rasulullah Muhammad SAW,yang telah memberikan pencerahan dunia yang lebih baik.
Penyusunan laporan ini bertujuan untuk memenuhi tugas dan kewajiban sebagai persyaratan dalam menyelesaikan studi Program Dioloma III Jurusan Teknik Sipil Politeknik Negeri Sriwijaya.
Dalam menyelesaikan laporan ini, penulis mendapatkan bantuan, bimbingan arahan dan do’a dari berbagai pihak yang langsung maupun tidak langsung. Pada kesempatan ini, dengan penuh rasa hormat dan kerendahan hati izinkan penulis mengucapkan terima kasih kepada :
1. Bapak Rd. Kusumanto, S.T., M.M, selaku Direktur Politeknik Negeri Sriwijaya.
2. Bapak Zainuddin Muchtar, S.T., M.T, selaku Ketua Jurusan Teknik Sipil Politeknik Negeri Sriwijaya.
3. Bapak Drs. Arfan Hasan M.T, selaku Sekretaris Jurusan Teknik Sipil Politeknik Negeri Sriwijaya.
4. Bapak Ir. Kosim M.T, selaku Dosen Pembimbing I, yang telah memberikan bimbingan dan pengarahannya.
5. Ibu Ika Sulianti S.T.,M.T selaku Dosen Pembimbing II, yang telah memberikan bimbingan dan pengarahannya.
7. Seluruh Staf, Teknisi dan Administrasi Laboratorium Teknik Sipil Politeknik Negeri Sriwijaya
8. Almamater Politeknik Negeri Sriwijaya
9. Dan kepada semua pihak yang telah membantu penulis, sehingga laporan ini dapat diselesaikan tepat waktu.
Penulis berharap, semoga laporan ini dapat bermanfaat bagi seluruh elemen mahasiswa atau masyarakat umum lainnya, khususnya mahasiswa Jurusan Teknik Sipil Politeknik Negeri Sriwijaya
Palembang, Oktober 2013
2.8 Slump……… 23
3.3.2 Pengujian Berat Jenis dan SSD dan Penyerapan Agregat Halus…... 36
3.3.3 Pengujian Berat Jenis dan SSD dan Penyerapan Agregat Kasar…... 41
3.4.1 Merancang Campuran Beton Normal Menurut SK.SNI 03-2834-2000... 58
3.4.2 Pengujian Slump Beton………...…… .... 71
3.4.3 Pengujian Kuat Tekan Beton…………...…... 73
BAB IV PEMBAHASAN
4.1 Hasil Pemeriksaan………... 76
4.1.1 Hasil pemeriksaan Analisa Saringan Agregat….... 76
4.1.2 Berat Jenis Agregat dan Penyerapan Agregat…… 79
4.1.3 Pemeriksaan Kadar Air Agregat……… 81
4.1.4 Berat Isi Agregat………... 82
4.1.5 Keausan Agregat………... 87
4.1.6 Kekerasan Agregat………... 88
4.1.7 Pemeriksaan Material Semen………... 89
4.2 Perencanaan Campuran Beton………... 92
4.3 Perbandingan Campuran Beton………... 93
4.4 Hasil Uji Kuat Tekan Beton…...………... 97
4.5 Rekapitulasi Hasil Pengujian Kuat Tekan Beton……….... 111
BAB V KESIMPULAN DAN SARAN 5.1 Kesimpulan………...………...……….... 113
5.2 Saran………...………... 115
DAFTAR PUSTAKA
LAMPIRAN
DAFTAR GAMBAR
Gambar 3.5 Alat untuk menentukan SSD (kerucut terpancung, plat kaca, penumbuk plastik)... 30
Gambar 3.22 Hubungan faktor air semen dan kuat tekan rata-rata untuk benda uji kubus (15cm x 15cm x 15cm)... 61
Gambar 3.23 Hubungan faktor air semen dan kuat tekan rata – rata untuk benda uji silinder (diameter 15cm, tinggi 30cm... 62
Gambar 3.25 Grafik persentase agregat halus terhadap agregat
keseluruhan dengan ukuran butiran maksimum 20m... 68
Gambar 3.26 Grafik persentase agregat halus terhadap agregat keseluruhan dengan ukuran butiran maksimum 10mm... 69
Gambar 3.27 Perkiraan berat isi beton... 70
Gambar 3.28 Proses pengujian nilai slump... 72
Gambar 3.29 Diagram alir penelitian... 75
Gambar 4.1 Grafik gradasi agregat kasar... 77
Gambar 4.2 Grafik gradasi agregat halus... 79
Gambar 4.3 Grafik waktu ikat semen... 91
Gambar 4.4 Grafik uji kuat tekan beton normal... 98
Gambar 4.5 Grafik uji kuat tekan beton komposisi campuran limbah beton 100% dan limbah pecahan dinding bata 0%... 100
Gambar 4.6 Grafik uji kuat tekan beton komposisi campuran limbah beton 80% dan limbah pecahan dinding bata 20% 102
Gambar 4.7 Grafik uji kuat tekan beton komposisi campuran limbah beton 60% dan limbah pecahan dinding bata 40%... 104
Gambar 4.8 Grafik uji kuat tekan beton komposisi campuran limbah beton 40% dan limbah pecahan dinding bata 60%... 106
Gambar 4.9 Grafik uji kuat tekan beton komposisi campuran limbah beton 20% dan limbah pecahan dinding bata 80%... 108
DAFTAR TABEL
Tabel 3.3 Persyaratan jumlah semen minimum dan faktor air semen maks untuk berbagai macam pembetonan lingkungan khusus. 63
Tabel 4.9 Hasil pemeriksaan berat isi agregat kasar... 84
Tabel 4.20 Beton campuran 100% limbah dinding beton dan 0% limbah dinding bata... 94
Tabel 4.21 Beton campuran 80% limbah dinding beton dan 20% limbah dinding bata... 94
Tabel 4.22 Beton campuran 60% limbah dinding beton dan 40% limbah dinding bata. ... 95
Tabel 4.23 Beton campuran 40% limbah dinding beton dan 60% limbah dinding bata. ... 95
Tabel 4.24 Beton campuran 20% limbah dinding beton dan 80% limbah dinding bata... 95
Tabel 4.25 Beton campuran 0% limbah dinding beton dan 100% limbah dinding bata... 96
Tabel 4.26 Hasil uji kuat tekan beton normal... 97
Tabel 4.27 Hasil uji kuat tekan variasi 100 % limbah pecahan Beton... 99
Tabel 4.28 Hasil uji kuat tekan variasi 80 % limbah pecahan beton dan 20 % pecahan dinding bata... 101
Tabel 4.29 Hasil uji kuat tekan variasi 60 % limbah pecahan beton dan 40 % pecahan dinding bata... 103
Tabel 4.31 Hasil uji kuat tekan variasi 20 % limbah pecahan beton dan
80 % pecahan dinding bata... 107 Tabel 4.32 Hasil uji kuat tekan variasi 100 % limbah pecahan
DAFTAR PUSTAKA
Antono, A. 1995. Bahan Konstruksi Teknik Sipil. Penerbit Universitas Atma Jaya. Yogyakarta.
Mulyono, Tri. 2005. Teknologi Beton (Edisi Kedua). CV. Andi Offset. Yogyakarta
Murdock L.J, dan Brook K.M. 1999. Bahan dan Praktek Beton (Edisi Keempat).
Erlangga. Jakarta