Daftar Pustaka
1.Takasaki, S., Yamada, Y.,(2007) ,Effects of temperature and aggressive anions on corrosion of carbon steel in potable water, Corros Sci ,49, 240-247.
2. Larson, E., Skold, R.V., (1958), Laboratory studies relating mineral quality of water to corrosion of steel and cast iron, Corrosion, 14, 285-288.
3. Bundjali, B., (2000), Tinjauan Termodinamika dan Kinetika Korosi serta Teknik-Teknik Pengukuran Laju Korosi, Diktat Kuliah, ITB.
4. Bundjali, B., (2005), Perilaku dan Inhibisi Korosi Baja Karbon dalam Larutan Buffer Asetat, Bikarbonat – CO2, Disertasi , ITB.
5. El Achouri, M., Infante, M.R., Izquierdo, F., (2001), Synthesis of some cationic gemini surfactants and their inhibitive effect on iron corrosion in hydrochloric acid medium, Corros Sci, 43, 19-35.
6. Trethewey, K.R., Chamberlain, J., (1991), Korosi untuk Mahasiswa Sains dan Rekayasa, Gramedia Pustaka Utama.
7. Butler, G., Ison, H.C.K., (1966), Corrosion and Its Prevention in Waters, Chemical and Process Engineering Series, Leonard Hill.
8. Bundjali, B., (2004), Konstruksi diagram potensial-pH untuk baja karbon dalam Buffer Asetat secara potensiodinamik eksperimental, J. Matematika dan Sains, 9, 307-312.
9. Sastri, V.S., (1998), Corrosion Inhibitor Principles and Aplication, John Wiley & Sons Ltd.
10. Wahyuningrum, D., (2008), Sintesis Senyawa Turunan Imidazol dan Penentu- tuan Aktifitas Inhibisi Korosinya pada Permukaan Baja Karbon, Disertasi,
ITB.
11. Surdia, T., Saito, S., (1984), Pengetahuan Bahan Teknik, Departemen Mesin, ITB.
12. Bentiss, F., Bouanis, M., Mernari, B., Traisnel, M., Vezin, H., Lagrene, M., (2007), Understanding the adsorption of 4H-1,2,4-triazole derivatives on mild
14. Ergun,U., (2008), The inhibitory effect of bis-2,6- (3,5dimethylpyrazolyl) pyridine on the corrosion behavior of mild steel in HCl solution, Materials Chem and Phys, 30, 30-30.
15. Fuchs, R., (2007), Inhibitory effect of non ionic surfactants of the triton-x series on the corrosion of carbon steel in sulphuric acid, Chim Acta, 52, 4974 -4981
16. Deyab, M.A., Helal, A., Fouda, A.S., (2007), Effect of cationic surfactant and in organic anions on the electrochemical behavior of carbon steel in formation in formation water, Corros Sci, 49, 2315-2328
17. Abdallah, M., Helal, A., Fouda, A.S., (2006), Aminopyrimidine derivatives as inhibitor for corrosion of 1018 carbon steel nitric acid solution, Corros Sci, 48,1639-1654.
18. Reffass, M., Sabot, R., Savall, C., Jeannin. M., (2006), Localised corrosion of carbon steel in NaHCO3/ NaCl , Corros Sci, 48, 726-728
19. Chetoutani, A., (2006), Inhibition of pure iron by new synthesized tripyrazole derivatives in HCl solution, Corros Sci, 48,2987-2997
20. Lukomska, A.,Smolin, S., Sobkowski, J., (2001), Adsorption thiourea on monocrystalline copper Electrodes, Chim Acta, 46, 3111-3117
21. Stankovi,Z.D., Vukovic, M., (1996), The influence of thiourea on kinetic parameters on the cathodic and anodic reaction at different metals in H2SO4
solution, Chim Acta, 4686, 00066-7
22. Antonia, E., Peyerimhoff, S.D., (2002), On the relationship between corrosion inhibiting effect and molecular structure, chim Acta, 47,1365-1371
23. Jovancicevic,V., Ahn, Y.S., Dougherti, J.,(2000) , CO2 corrosion inhibition by sulfur-containing organic compounds, Paper, NACE.
24. Chikh, Z.A, (2005), Electrochemical and analytical study of corrosion
inhibition on carbon steel in HCl medium by 1,12-bis(1,2,4,triazoly)dodecane, Corros Sci, 47, 447–459
25. Gao, B., Zhang, X., Sheng, Y., (2008), Studies on preparing and corrosion inhibition behaviour of quaternized polyethyleneimine for low carbon steel in sulfuric acid, Materials Chem and Phys, 108, 375–381
26. Hamman, C.H., Hamnet, A., Vielstich, W.,(1997), Electrochemistry, Wiley- VCH.
27. Piron, D.J., (1991), The Electrochemistry of Corrosion, NACE.
28. Jiang, X., Zheng Y. G., Qu, D.R., Ke, W., (2006), Effect of calcium ions on pitting corrosion and inhibition performance in CO2 corrosion of N80 steel,
Corros Sci, 48, 3091-3108.
29. Ernst, P., Newman, R.C., (2007), Explanation of the effect of high chloride concentration on the critical pitting temperature of stainless steel, Corros Sci,
LAMPIRAN A
Lampiran A.1 Hasil uji metalografi dan spektrometri sampel baja karbon
Lampiran A.2 Pengaruh konsentrasi ion klorida terhadap laju korosi baja karbon
dalam air sadah tiruan di lingkungan ion klorida pada suhu 25 ºC Konsentrasi Cl- (ppm) pH DHL (µS/cm) Icorr (µA/cm-2) Ecorr (mV) Laju Korosi (mm/thn) 22,51 9,7 680 26,0891 -731,5 0,3051 32,51 9,7 697 29,3575 -732,5 0,3433 42,51 9,7 719 35,2357 -735,7 0,4121 54,31 9,7 726 32,4119 -732,6 0,3790 64,31 9,7 751 27,2306 -732,7 0,3184 74,31 9,7 775 26,8499 -733.0 0,3140 84,31 9,7 800 25,0838 -732,5 0,2933
Lampiran A.3 Pengaruh suhu terhadap laju korosi baja karbon dalam air sadah
yang mengandung 42,5 ppm ion klorida pada suhu 25 ºC
Suhu (ºC) Icorr (µA/cm-2) Ecorr (mV) Laju Korosi (mm/thn) 25 35,2357 -735,7 0,4121 35 36,4617 -732,9 0,4264 45 42,3504 -732,4 0,4953 55 53,2445 -734,7 0,6227
Lampiran A.4 Pengaruh konsentrasi ion sulfat terhadap laju korosi baja karbon
dalam air sadah tiruan di lingkungan ion sulfat pada suhu 25 ºC
Konsentrasi SO4 2-(ppm) pH DHL (µS/cm) Icorr (µA/cm-2) Ecorr (mV) Laju korosi (mm/thn) 0,75 9,7 629 21,2936 -736 0,2490 2,5 9,7 631 24,3115 -739,8 0,2843 5 9,7 633 25,3661 -735,9 0,2966 7,5 9,7 635 21,7588 -740,7 0,2544 10 9,7 646 21,4845 -741,5 0,2512
Lampiran A.5 Pengaruh suhu terhadap laju korosi baja karbon dalam air sadah yang mengandung 5 ppm ion sulfat pada suhu 25ºC
Suhu (ºC) Icorr (µA/cm-2) Ecorr (mV) Laju Korosi (mm/thn) 25 25,3661 -735,9 0,2966 35 25,4870 -735,0 0,2981 45 28,4277 -736,1 0,3324 55 32,6028 -738,4 0,3813
Lampiran A.6 Hasil analisis kimia air sadah di industri tekstil tahun 2005
dari Laboratorium Sucopindo
Jenis Analisis Hasil (ppm)
SO42- 4,88 Cl- 54,31 Ca2+ 7,05 Mg2+ 17,62 SiO2 40,41 HCO3- 349,83
Kekerasan total sebagai CaCO3 90,13
Lampiran A.7 Pengaruh konsentrasi ion klorida terhadap laju korosi baja karbon
dalam air sadah di industri tekstil pada suhu 25 ºC
Konsentrasi penambahan ion klorida (ppm) pH DHL (µS/cm) Icorr (µA/cm-2) Ecorr (mV) Laju Korosi (mm/thn) 10 8,7 563 21,3301 -721,3 0,2494 20 8,7 588 24,5626 -725,1 0,2872 30 8,7 609 25,2089 -725,2 0,2948 40 8,7 629 26,8535 -723,6 0,3140 50 8,7 656 27,9103 -718,7 0,3264 60 8,7 679 28,4567 -723,4 0,3328 70 8,7 693 30,9778 -723,1 0,3623 80 8,7 722 32,1223 -720,3 0,3757 90 8,7 736 36,8163 -723,5 0,4306 100 8,7 756 28,0525 -723,7 0,3281 120 8,7 778 26,0355 -723,3 0,3045
Lampiran A.8 Pengaruh konsentrasi ion sulfat terhadap laju korosi baja karbon
dalam air sadah di industri tekstil pada suhu 25 ºC
Konsentrasi penambahan ion sulfat (ppm) pH DHL (µS/cm) Icorr (µA/cm-2) Ecorr (mV) Laju Korosi (mm/thn) 10 8,7 547 21,7142 -725,8 0,2539 20 8,7 565 22,6544 -724,9 0,2649 30 8,7 573 28,0600 -725,5 0,3281 40 8,7 592 25,4830 -724,4 0,2980 50 8,7 602 25,0333 -726,6 0,2927 60 8,7 624 24,4294 -725,7 0,2856 70 8,7 637 22,6704 -724,8 0,2651
Lampiran A.9 Pengaruh suhu terhadap laju korosi baja karbon dalam air sadah
di industri tekstil dengan penambahan 90 ppm ion klorida Suhu (ºC) Icorr (µA/cm-2) Ecorr (mV) Laju Korosi (mm/thn) 25 36,8163 -723,5 0,4306 35 37,3557 -740,9 0,4369 45 45,9381 -741,7 0,5373 55 50,5003 -739,1 0,5906
LAMPIRAN B
Lampiran B.1 Pengaruh konsentrasi inhibitor terhadap laju korosi baja karbon
dalam air sadah tiruan yang mengandung 42,5 ppm ion klorida dan efektifitasnya pada suhu 25 ºC
Konsentrasi inhibitor (ppm) Icorr (µA/cm-2) Ecorr (mV) Laju korosi (mm/thn) EI (%) cmc (ppm) Blanko 35,2357 -735,7 0,4121 --- --- Tiourea 10 3,6160 -652,5 0,04229 89,73 20 3,1919 -652,8 0,03733 90,94 30 2,5621 -652,8 0,02996 92,73 40 1,8688 -649,3 0,02185 94,69 50 2,5593 -664,4 0,02993 92,73 75 2,5977 -648,4 0,03038 92,63 40 Simetidin 10 13,6015 -705,6 0,15900 61,39 20 8,7390 -695,5 0,10220 75,19 25 7,8291 -691,6 0,09157 77,78 50 7,5391 -687,8 0,08817 78,60 75 7,7045 -688,6 0,09011 78,13 100 8,0438 -693,1 0,09408 77,17 50
Lampiran B.2 Pengaruh suhu terhadap efektifitas inhibitor dalam air sadah tiruan
yang mengandung 42,5 ppm ion klorida Suhu (ºC) Icorr (µA/cm-2) Ecorr (mV) Laju korosi (mm/thn) EI (%) Blanko 25 35,2357 -735,7 0,4121 --- 35 36,4617 -732,9 0,4264 --- 45 42,3504 -732,4 0,4953 --- 55 53,2445 -734,7 0,6227 --- Tiourea 25 1,8688 -649,3 0,02185 94,7 35 4,1066 -674,5 0,04803 88,7 45 5,4370 -669,5 0,06359 87,2 55 9,2688 -668,4 0,10840 82,6 Simetidin 25 7,5391 -687,8 0,0882 78,6 35 9,7810 -710,3 0,1144 73,2 45 11,4346 -714,4 0,1337 73,0 55 14,5748 -712,7 0,1704 72,6
Lampiran B.3 Pengaruh konsentrasi inhibitor terhadap laju korosi baja karbon
dalam air sadah tiruan yang mengandung 5 ppm ion sulfat dan efektifitasnya pada suhu 25 ºC
Konsentrasi inhibitor (ppm) Icorr (µA/cm-2) Ecorr (mV) Laju korosi (mm/thn) EI (%) cmc (ppm) Blanko 25,3661 -735,9 0,2966 --- --- Tiourea 5 4,7842 -681,0 0,05595 81,1 10 3,0536 -691,5 0,03571 87,9 20 1,8303 -677,8 0,02140 92,8 30 2,4868 -679,9 0,02908 90,2 40 2,6759 -675,4 0,03129 89,5 20 Simetidin 10 22,1151 -715,2 0,25900 12,8 20 19,6333 -707,7 0,22956 22,6 30 17,8323 -702,3 0,20850 29,7 40 16,1183 -693,5 0,18850 36,5 50 16,4185 -704,6 0,19200 35,3 60 16,5423 -698,2 0,19300 34,8 40
Lampiran B.4 Pengaruh suhu terhadap efektifitas inhibitor dalam air sadah tiruan
yang mengandung 5 ppm ion sulfat
Suhu ( ºC) Icorr (µA/cm-2) Ecorr (mV) Laju korosi (mm/thn) EI (%) Blanko 25 25,3661 -735,9 0,2966 --- 35 25,4870 -735,0 0,2981 --- 45 28,4277 -736,1 0,3324 --- 55 32,6028 -738,4 0,3813 --- Tiourea 25 1,8303 -677,8 0,02140 92,8 35 2,0979 -697,0 0,02453 91,8 45 3,1270 -677,7 0,03656 89,0 55 3,9675 -681,1 0,04640 87,8 Simetidin
Lampiran B.5 Pengaruh konsentrasi inhibitor terhadap laju korosi baja karbon
dalam air sadah di industri tekstil dengan penambahan 90 ppm ion klorida dan efektifitasnya pada suhu 25 ºC
Konsentrasi inhibitor (ppm) Icorr (µA/cm-2) Ecorr (mV) Laju korosi (mm/thn) EI (%) cmc (ppm) Blanko 36,8163 -723,5 0,4306 --- Tiourea 5 3,1273 -637,4 0,03657 91,5 10 2,7961 -664,1 0,03080 92,4 20 2,5501 -664,4 0,02809 93,1 30 3,1200 -660,2 0,03437 91,5 40 4,8427 -662,1 0,05664 86,9 20 Simetidin 20 21,1405 -704,7 0,247,2 42,6 30 18,4082 -702,1 0,2153 50,0 40 15,0946 -700,1 0,1765 59,0 50 16,3830 -704,8 0,1916 55,5 60 16,9797 -703,9 0,1985 53,9 40
Lampiran B.6 Pengaruh suhu terhadap efektifitas inhibitor dalam air sadah
di industri tekstil yang mengandung 90 ppm ion klorida Suhu (ºC) Icorr (µA/cm-2) Ecorr (mV) Laju korosi (mm/thn) EI (%) Blanko 25 36,8163 -723,5 0,4306 --- 35 37,3557 -740,9 0,4369 --- 45 45,9381 -741,7 0,5373 --- 55 50,5003 -739,1 0,5906 --- Tiourea 25 2,5501 -664,4 0,02809 93,1 35 3,1296 -677,0 0,03660 91,6 45 4,2852 -687,0 0,05012 90,7 55 7,2307 -686,9 0,08682 85,7 Simetidin 25 15,0946 -700,1 0,1765 59,0 35 15,5026 -708,0 0,1813 58,5 45 19,4609 -714,4 0,22760 57,6 55 21,8483 -706,3 0,25550 56,7
Lampiran B.7 Pengaruh konsentrasi inhibitor terhadap tegangan permukaan
dalam air sadah tiruan yang mengandung 42,5 ppm pada suhu 25 ºC Inhibitor Konsentrasi Inhibitor (ppm) Tegangan Permukaan (mN/m) cmc (ppm) Blanko --- 70,1 10 69,3 20 67,1 30 62,6 40 61,9 50 62,2 60 62,2 Tiourea 70 62,2 40 10 68,2 20 65,6 30 64,0 40 63,6 50 61,8 60 61,8 70 61,8 Simetidin 80 61,8 50
Lampiran B.8 Pengaruh konsentrasi inhibitor terhadap tegangan permukaan
dalam air sadah tiruan yang mengandung 5 ppm ion sulfat pada suhu 25 ºC Inhibitor Konsentrasi Inhibitor (ppm) Tegangan Permukaan (mN/m) cmc (ppm) Blanko --- 74.7 10 72.5 20 67,5 30 69,5 40 69,5 50 69,5 Tiourea 60 69,5 20 10 73,1 20 71,6 30 71,3
Lampiran B.9 Pengaruh konsentrasi inhibitor terhadap tegangan permukaan
dalam air sadah di industri tekstil dengan penambahan 90 ppm ion klorida pada suhu 25 ºC
Inhibitor Konsentrasi Inhibitor (ppm) Tegangan Permukaan (mN/m) cmc (ppm) Blanko --- 77,4 10 75,2 20 71,6 30 71,6 40 71,6 Tiourea 50 71,6 20 10 76,5 20 75,1 30 73,1 40 71,9 50 72,1 60 72,1 Simetidin 70 72,1 40