PENGARUH SUHU PIROLISIS DAN JUMLAH KATALIS SILIKA GEL TERHADAP YIELD DAN KUALITAS BAHAN BAKAR CAIR DARI LIMBAH PLASTIK JENIS POLIPROPILENA SKRIPSI

(1)

PENGARUH SUHU PIROLISIS DAN JUMLAH

KATALIS SILIKA GEL TERHADAP YIELD DAN

KUALITAS BAHAN BAKAR CAIR DARI LIMBAH

PLASTIK JENIS POLIPROPILENA

SKRIPSI

Oleh

ERLANGGA WICAKSANA

110405102

DEPARTEMEN TEKNIK KIMIA

FAKULTAS TEKNIK

UNIVERSITAS SUMATERA UTARA

JANUARI 2016

(2)

PENGARUH SUHU PIROLISIS DAN JUMLAH

KATALIS SILIKA GEL TERHADAP YIELD DAN

KUALITAS BAHAN BAKAR CAIR DARI LIMBAH

PLASTIK JENIS POLIPROPILENA

SKRIPSI

Oleh

ERLANGGA WICAKSANA

110405102

SKRIPSI INI DIAJUKAN UNTUK MELENGKAPI SEBAGIAN

PERSYARATAN MENJADI SARJANA TEKNIK

DEPARTEMEN TEKNIK KIMIA

FAKULTAS TEKNIK

(3)

i

PERNYATAAN KEASLIAN SKRIPSI

Saya menyatakan dengan sesungguhnya bahwa skripsi dengan judul :

PENGARUH SUHU PIROLISIS DAN JUMLAH KATALIS SILIKA GEL TERHADAP YIELD DAN KUALITAS BAHAN BAKAR CAIR DARI

LIMBAH PLASTIK JENIS POLIPROPILENA

yang dibuat untuk melengkapi sebagian persyaratan menjadi Sarjana Teknik pada Departemen Teknik Kimia Fakultas Teknik Universitas Sumatera Utara. Skripsi ini adalah hasil karya saya kecuali kutipan-kutipan yang telah saya sebutkan sebelumnya.

Demikian pernyataan ini diperbuat, apabila dikemudian hari terbukti bahwa karya ini bukan karya saya atau merupakan hasil jiplakan maka saya bersedia menerima sanksi sesuai dengan aturan yang berlaku.

Medan, Januari 2016

Erlangga Wicaksana NIM. 110405102

(4)

PENGESAHAN

Skripsi dengan judul :

PENGARUH SUHU PIROLISIS DAN JUMLAH KATALIS SILIKA GEL TERHADAP YIELD DAN KUALITAS BAHAN BAKAR CAIR DARI

LIMBAH PLASTIK JENIS POLIPROPILENA

Dibuat untuk melengkapi persyaratan menjadi Sarjana Teknik pada Departemen Teknik Kimia Fakultas Teknik Universitas Sumatera Utara. Skripsi ini telah diajukan pada sidang ujian skripsi pada 27 Januari 2016 dan dinyatakan memenuhi syarat/sah sebagai skripsi pada Departemen Teknik Kimia Fakultas Teknik Universitas Sumatera Utara.

Mengetahui, Medan, Januari 2016 Dosen Pembimbing

Dr. Halimatuddahliana, ST, MSc NIP. 19730408 199802 2 002 Dosen Penguji I Dosen Penguji II

Prof. Dr. Ir. M. Turmuzi, MS Dr. Ir. Taslim, Msi

(5)

iii

PRAKATA

Puji dan syukur penulis panjatkan kehadirat Allah Subhanahu Wata’ala atas limpahan rahmat dan karunia-Nya sehingga skripsi ini dapat diselesaikan. Tulisan ini merupakan Skripsi dengan judul “Pengaruh Suhu Pirolisis dan Jumlah Katalis Silika Gel terhadap Yield dan Kualitas Bahan Bakar Cair dari Limbah Plastik Jenis Polipropilena”, berdasarkan hasil penelitian yang penulis lakukan di Departemen Teknik Kimia Fakultas Teknik Universitas Sumatera Utara. Skripsi ini merupakan salah satu syarat untuk mendapatkan gelar sarjana teknik.

Hasil penelitian ini diharapkan dapat memberi gambaran kepada masyarakat bahwa energi dapat dihasilkan dari limbah salah satunya adalah limbah plastik atau polimer sejenis. Hal ini dapat berdampak baik bagi lingkungan ditengah krisis energi yang sedang kita hadapi karena menjadi salah satu solusi pencemaran limbah pastik yang kian meningkat beberapa tahun terakhir.

Selama melakukan penelitian sampai penulisan skripsi ini, penulis banyak mendapat bantuan dari berbagai pihak, untuk itu penulis mengucapkan terima kasih dan penghargaan yang sebesar-besarnya kepada :

1. Dr. Halimatuddahliana, ST, MSc selaku Dosen Pembimbing yang telah banyak memberikan ilmu dan arahan kepada penulis pada penyusunan dan penulisan skripsi ini.

2. Ir. Renita Manurung, M.T selaku Koordinator Penelitian Departemen Teknik Kimia, Fakultas Teknik, Universitas Sumatera Utara.

3. Dr. Eng. Ir. Irvan, M.Si selaku Ketua Departemen Teknik Kimia, Fakultas Teknik, Universitas Sumatera Utara.

4. Prof. Dr. Ir. Turmuzi, MS selaku Dosen Penguji I yang telah memberikan saran dan masukan yang membangun dalam penulisan skripsi ini.

5. Dr. Ir. Taslim, MSi selaku Dosen Penguji II yang telah memberikan kritik dan saran yang membangun dalam penulisan skripsi ini.

6. Dr. Iriany, MSi selaku Dosen Pembimbing Akademik yang telah membimbing penulis dalam hal akademik selama kuliah di Teknik Kimia USU.

7. Seluruh staf Dosen Teknik Kimia USU, yang telah mendidik dan membagikan ilmu kepada penulis selama perkuliahan.

(6)

8. Pegawai Departemen Teknik Kimia USU, yang telah membantu penulis dalam hal administrasi selama perkuliahan.

9. Rio Nazif selaku partner penelitian penulis.

10. Abang dan kakak senior, teman-teman stambuk 2011, dan adik-adik stambuk 2012 hingga 2015 yang tidak dapat disebutkan satu persatu.

Penulis menyadari bahwa skripsi ini masih jauh dari sempurna oleh karena itu penulis mengharapkan saran dan masukan demi kesempurnaan skripsi ini. Semoga skripsi ini memberikan manfaat bagi pengembangan ilmu pengetahuan.

Medan, Januari 2016 Penulis

(7)

v

DEDIKASI

Penulis mendedikasikan skripsi ini

kepada keluarga besar penulis atas

dukungan dan kasih sayang mereka,

terutama kepada orang tua,

Ir. Edward Wahab, MSi dan Rosdiana Rangkuti

kepada nenek Rohana Oemar,

serta adik-adikku

(8)

RIWAYAT HIDUP PENULIS

Nama : Erlangga Wicaksana NIM : 110405102

Tempat/Tgl. Lahir : Jambi / 18 Oktober 1994 Nama orang tua : Ir. Edward Wahab, MSi Rosdiana Rangkuti Alamat orang tua :

Jalan As-Shofa I Komp. Tirta Mas Blok B/10 Kota Pekanbaru - Riau

Asal Sekolah

 SD Islam As-Shofa Pekanbaru, tahun 1999-2005

 SMP Islam As-Shofa Pekanbaru, tahun 2005-2008

 SMA Islam As-Shofa Pekanbaru, tahun 2008-2011 Pengalaman Organisasi/Kerja :

1. Asisten Laboratorium Mikrobiologi Industri / Bioproses tahun 2013 - 2015 modul Fermentasi Alkohol.

2. Wakil Bendahara Umum Covalen Study Group Periode 2013 - 2014 3. Anggota Bidang Penelitian dan Pengembangan Himpunan Mahasiswa

Teknik Kimia Periode 2013 – 2014

4. Anggota Departemen Riset dan Teknologi Pemerintahan Mahasiswa FT USU Periode 2013 - 2014

5. Sekretaris Umum Himpunan Mahasiswa Teknik Kimia Periode 2014 - 2015

6. On Job Training Angkatan I Tahun 2015 di SRO (Smelter Reduction Operation) PT Inalum (Persero) Kuala Tanjung.

(9)

vii

ABSTRAK

Beberapa permasalahan besar yang muncul di beberapa negara akibat peningkatan jumlah penduduk yaitu peningkatan volume sampah dan peningkatan konsumsi energi. Penanggulangan sampah plastik dengan landfill dan insinerasi masih meninggalkan efek samping lain seperti polutan. Cadangan sumber energi tidak terbarukan juga sudah menipis untuk memenuhi kebutuhan energi. Proses pirolisis atau cracking sampah plastik dapat menjadi solusi permasalahan ini. Penelitian ini bertujuan untuk mengamati pengaruh suhu proses pirolisis dan jumlah katalis silika gel terhadap yield dan kualitas bahan bakar cair yang dihasilkan dari Plastik Bekas Kemasan Gelas (PBKG) jenis Polipropilena (PP). Suhu proses divariasikan yang dimulai dari suhu 200 °C, 250 °C, 300 °C, dan 350 °C. Rasio jumlah bahan baku : jumlah katalis divariasikan dari 10 : 0 (tanpa katalis), 10 : 1, 10 :1,5; 10 : 2, 10 : 2,5, dan 10 : 3. Pirolisis dilakukan selama 2 jam. Rangkaian alat pirolisis terdiri dari reaktor pirolisis, burner / kompor, dan kondensor. Analisis yang dilakukan yaitu analisis densitas / specific gravity / API gravity, viskositas kinematis, karakterisasi GC-MS dan FTIR, dan heating value. Hasil penelitian menunjukkan peningkatan suhu proses dapat menaikkan yield bahan bakar cair, namun suhu yang sangat tinggi dapat menurunkan yield bahan bakar cair. Penambahan katalis juga dapat menambah yield

bahan bakar cair namun dalam jumlah yang banyak akan menurunkan yield bahan bakar cair. Penambahan katalis silika gel memproduksi fraksi bahan bakar C8 – C21

lebih banyak dibandingkan tanpa penggunaan katalis silika gel. Yield bahan bakar cair tertinggi didapatkan pada pirolisis suhu 350 °C tanpa katalis yaitu 71,064 %. Namun kualitas bahan bakar terbaik didapatkan pada pirolisis suhu 300 °C dengan perbandingan jumlah bahan baku dan katalis silika gel 10 : 3.

Kata kunci : Sampah Plastik, Pirolisis, Cracking, Katalis Silika Gel, Suhu, Bahan Bakar Cair

(10)

ABSTRACT

Several major issues that arise in some countries as a result of increasing population is increase in the volume of waste and energy consumption. Reduction of plastic waste in landfills and incineration are still leaving the other side effects such as pollutants. Non-renewable energy sources supply has also been low to meet energy needs. The process of pyrolysis or cracking plastic waste can be a solution to this problem. This study aims to observe the effect of temperature catalytic pyrolysis process and the amount of silica gel to yield and quality of liquid fuels produced from Polypropylene (PP) Used Plastic Packaging Glass. Temperatures varied process that starts from a temperature of 200 ° C, 250 ° C, 300 ° C and 350 ° C. Ratio of raw materials and the amount of catalyst was varied from 10: 0 (without catalyst), 10: 1, 10: 1.5; 10: 2, 10: 2.5 and 10: 3. Pyrolysis carried out for 2 hours. Pyrolysis apparatus consists of a pyrolysis reactor, burner, and a condenser. The analysis carried out by an analysis of density/specific gravity/API gravity, kinematic viscosity, characterization of GC-MS and FTIR, and heating value. Raise the temperature of the process can increase the yield of liquid fuels, but the very high temperatures can reduce the yield of liquid fuels. The addition of the silica gel catalyst can also increase the yield of liquid fuels, but in large amounts will decrease the yield of liquid fuel. The addition of silica gel catalysts produce fuel fraction C8

- C21 more than without using silica gel catalyst. The highest yield obtained at

pyrolysis temperature of 350 ° C without a silica gel catalyst that is 71.064%. But the best fuel quality obtained at pyrolysis temperature of 300 ° C with a ratio of the amount of raw materials and silica gel catalyst 10: 3.

Keywords: Waste Plastics, Pyrolysis, Cracking, Silica Gel Catalyst, Temperature, Liquid Fuels

(11)

ix

DAFTAR ISI

Halaman PERNYATAAN KEASLIAN SKRIPSI i PENGESAHAN UNTUK UJIAN SKRIPSI ii

PRAKATA iii

DEDIKASI v

RIWAYAT HIDUP PENULIS vi

ABSTRAK vii

ABSTRACT viii

DAFTAR ISI ix

DAFTAR GAMBAR xiii

DAFTAR TABEL xv

DAFTAR SINGKATAN xvii

DAFTAR SIMBOL xviii

BAB I PENDAHULUAN 1

1.1 Latar Belakang 1

1.2 Perumusan Masalah 3

1.3 Tujuan Penelitian 3 1.4 Manfaat Penelitian 4 1.5 Ruang Lingkup Penelitian 4

BAB II TINJAUAN PUSTAKA 5

2.1 Plastik 5

2.1.1 Pembuatan Plastik 5 2.1.2 Daur Ulang Plastik 7 2.1.3 Plastik Jenis Propilena (PP) 9

2.2 Silika 10

2.2.1 Silika Kristalin 11

2.2.2 Silika Amorf 11

2.2.3 Sifat – Sifat Reaksi Silika 12

(12)

2.3 Proses Pirolisis 14 2.3.1 Thermal Cracking 15 2.3.2 Catalytic Cracking 15 2.3.3 Mekanisme Catalytic Cracking 18 2.3.4 Hydro Cracking 19 2.4 Faktor-Faktor yang Mempengaruhi Pirolisis 20

2.4.1 Temperatur 20

2.4.2 Jumlah Katalis 21

2.4.3 Waktu 21

2.4.4 Jenis dan Komposisi Plastik 22 2.5 Parameter Kualitas Bahan Bakar 22

2.5.1 Densitas 23

2.5.2 Viskositas 23

2.5.3 Nilai Kalor / Heating Value 24 BAB III METODOLOGI PENELITIAN 25

3.1 Lokasi Penelitian 25

3.2 Bahan dan Peralatan 25

3.2.1 Bahan 25

3.3.2 Peralatan 25

3.3 Prosedur Penelitian 26 3.3.1 Penyediaan Bahan Baku Utama 26 3.3.2 Proses Pirolisis Polipropilena dari PBKG 26 3.3.3 Penentuan Yield Proses Pirolisis 29 3.3.4 Pengujian Kualitas Bahan Bakar Pirolisis 29 3.3.4.1 Uji Densitas/ Specific Gravity/ API Gravity 29 3.3.4.2 Uji Viskositas Kinematik 30 3.3.4.3 Karakterisasi Fourier Transform Infra-Red (FTIR) 31 3.3.4.4 KarakterisasiGas Chromatography Mass

(13)

xi

4.2 Pengaruh Jumlah Katalis Dan Suhu Pirolisis Terhadap Yield Bahan

Bakar Cair 33

4.3 Analisis Produk Bahan Bakar Cair 37 4.3.1 Analisis Densitas / Specific Gravity / API Gravity 37 4.3.2 Analisis Viskositas Kinematis 39 4.3.3 Analisis GC-MS Produk Bahan Bakar Cair 41 4.3.4 Analisis FTIR Produk Bahan Bakar Cair 45 4.3.5 Analisis Heating Value Produk Bahan Bakar Cair 48 BAB V KESIMPULAN DAN SARAN 49

4.1 Kesimpulan 49

4.2 Saran 50

DAFTAR PUSTAKA 51

LAMPIRAN 1 DATA BAHAN BAKU 56 LAMPIRAN 2 DATA HASIL PENELITIAN 58 L2.1 Hasil Pirolisis PBKG Jenis PP Tanpa Katalis 58 L2.2 Hasil Pirolisis PBKG Jenis PP dengan Katalis Silika Gel 58 L2.3 Data Yield Produk Bahan Bakar Cair 59 L2.4 Data Hasil Analisis Densitas Bahan Bakar Cair 60 L2.5 Data Hasil Analisis Specific Gravity dan API Gravity 61 L2.6 Data Hasil Analisis Viskositas Kinematik Bahan Bakar Cair 62 LAMPIRAN 3 CONTOH PERHITUNGAN 63 L3.1 Perhitungan Densitas, Specific Gravity, dan API Gravity 63 L3.2 Perhitungan Viskositas Bahan Bakar Cair 63 L3.3 Perhitungan Yield Bahan Bakar Cair 64 LAMPIRAN 4 DOKUMENTASI PENELITIAN 65 L4.1 Bahan Baku PBKG Jenis Polipropilena 65

L4.2 Proses Pirolisis 65

L4.3 Hasil Pirolisis 66

L4.4 Penyaringan Katalis dan Pengotor 66 L4.5 Produk Akhir Bahan Bakar Cair 67 L4.6 Analisis Densitas 67 L4.7 Analisis Viskositas 68

(14)

LAMPIRAN 5 HASIL ANALISIS PRODUK BAHAN BAKAR CAIR 69 L5.1 Hasil Analisis GC-MS 69 L5.2 Hasil Analisis FTIR 72

(15)

xiii

DAFTAR GAMBAR

Halaman Gambar 2.1 Struktur Kristalin dari Sebuah Kristal Silika Tunggal 11 Gambar 2.2 Sketsa Skema Susunan Amorf dalam (a) Padatan Kristalin, (b)

Padatan Amorf, dan (c) Gas 12 Gambar 2.3 Struktur Senyawa Silika Gel 13 Gambar 2.4 Perbandingan Yield Produk Cair yang Didapat dari Pemecahan

Plastik HDPE secara termal dan dengan Katalis 16 Gambar 2.5 Tahap Pembentukan Ion Karbonium / Karbokation 18 Gambar 2.6 Tahap Interaksi Ion Karbonium dengan Reaktan 18 Gambar 2.7 Tahap Penataan Ion Karbonium Melalui Pemutusan Beta 19 Gambar 2.8 Tahap Pembentukan Katalis Kembali 19 Gambar 2.9 Pengaruh Temperatur dalam Pemecahan Termal Polietilen 20 Gambar 2.10 Yield Cairan, Padatan, dan Gas dari Cracking dengan Katalis FCC 22 Gambar 3.1 Flowchart Penyediaan Bahan Baku Pirolisis 26 Gambar 3.2 Flowchart Rangkaian Peralatan Pirolisis Limbah PBKG 27 Gambar 3.3 Flowchart Prosedur dalam Proses Pirolisis, Yaitu Polipropilena

dari PBKG 28

Gambar 4.1 Karakterisasi FTIR PBKG dan PP Murni 32 Gambar 4.2 Struktur Polipropilena 33 Gambar 4.3 Pengaruh Suhu Pirolisis dan Jumlah Katalis terhadap Yield Bahan

Bakar Cair pada Suhu Reaksi 200 – 350 °C 34 Gambar 4.4 Kromatogram Hasil Analisis GC-MS pada Sampel Bahan Bakar

Cair (T = 300 °C, Perbandingan Bahan Baku : Katalis 10 : 3) 42 Gambar 4.5 Kromatogram Hasil Analisis GC-MS pada Sampel Bahan Bakar

Cair (T = 350 °C, Tanpa Katalis) 43 Gambar 4.6 Pengaruh Penggunaan Katalis terhadap Distribusi Fraksi Bahan

Bakar 45

Gambar 4.7 Spektrum Gelombang Analisis FTIR Produk Bahan Bakar Cair

Yang Dihasilkan dari Suhu Pirolisis 350 °C Tanpa Katalis 46 Gambar 4.8 Spektrum Gelombang Analisis FTIR Produk Bahan Bakar Cair

(16)

Yang Dihasilkan dari Suhu Pirolisis 300 °C dengan Perbandingan Bahan Baku : Katalis 10 : 3 47 Gambar L1.1 Hasil Spektofotometer FTIR pada PBKG Jenis PP 56 Gambar L4.1 Bahan Baku PBKG Jenis PP 65 Gambar L4.2 Proses Pirolisis 65 Gambar L4.3 Hasil Pirolisis 66 Gambar L4.4 Penyaringan Katalis 66 Gambar L4.5 Bahan Bakar Cair yang dihasilkan dan Penyimpanannya 67 Gambar L4.6 Analisis Densitas 67 Gambar L4.7 Analisis Viskositas 68 Gambar L5.1 Kromatogram Hasil Analisis GC-MS pada Sampel Bahan Bakar

Cair (T = 350 °C, Tanpa Katalis) 69 Gambar L5.2 Kromatogram Hasil Analisis GC-MS pada Sampel Bahan Bakar

Cair (T = 300 °C, Perbandingan Bahan Baku : Katalis 10 : 3) 71 Gambar L5.3 Spektrum Gelombang Analisis FTIR Produk Bahan Bakar Cair

Yang Dihasilkan dari Suhu Pirolisis 350 °C Tanpa Katalis 72 Gambar L5.4 Spektrum Gelombang Analisis FTIR Produk Bahan Bakar Cair

Yang Dihasilkan dari Suhu Pirolisis 300 °C dengan Perbandingan Bahan Baku : Katalis 10 : 3 73

(17)

xv

DAFTAR TABEL

Halaman Tabel 2.1 Data Temperatur Transisi dan Temperatur Lebur Plastik 7 Tabel 2.2 Konsumsi Plastik Per kapita Beberapa Negara di Dunia 8 Tabel 2.3 Jenis-Jenis Limbah Plastik dan Tanda Daur Ulang 8 Tabel 2.4 Pemilihan Plastik 9 Tabel 2.5 Sifat Umum Polipropilena 10 Tabel 2.6 Reaksi Komponen Halogen dan Silika 13 Tabel 2.7 Perbandingan yield gas, cairan, dan residu dari pemecahan

secara termal dan katalitik dari limbah HDPE pada 430 °C 16 Tabel 2.8 Kualitas Bahan Bakar Diesel Komersil yang Diizinkan Pemerintah Indonesia 23 Tabel 4.1 Hasil Analisis Densitas, Specific Gravity, dan API Gravity Bahan

Bakar Cair Hasil Pirolisis PBKG 38 Tabel 4.2 Hasil Analisis Viskositas Kinematik Bahan Bakar Cair 40 Tabel 4.3 Komponen Senyawa yang Terkandung pada Produk Bahan Bakar

Cair (T = 300 °C perbandingan PP : Katalis = 10 : 3) 42 Tabel 4.4 Komponen Senyawa yang Terkandung pada Produk Bahan Bakar

Cair (T = 350 °C Tanpa Katalis) 43 Tabel 4.5 Hasil Analisis FTIR pada Bahan Bakar Cair yang dihasilkan dengan

Suhu Pirolisis 350 °C Tanpa Katalis 46 Tabel 4.6 Hasil Analisis FTIR pada Bahan Bakar Cair yang dihasilkan dengan

Suhu Pirolisis 300 °C dengan Perbandingan Jumlah Bahan Baku :

Katalis 10 : 3 47

Tabel L1.1 Komposisi Gugus Fungsi Senyawa pada PBKG Jenis PP 56 Tabel L2.1 Hasil Pirolisis PBKG Jenis PP 58 Tabel L2.2 Hasil Pirolisis PBKG Jenis PP dengan Katalis Silika Gel 58 Tabel L2.3 Hasil Yield Bahan Bakar Cair 59 Tabel L2.4 Hasil Analisa Densitas Bahan Bakar Cair 60 Tabel L2.5 Hasil Analisa Specific Gravity dan API Gravity Bahan Bakar Cair 61 Tabel L2.6 Hasil Analisa Viskositas Bahan Bakar Cair 62

(18)

Tabel L5.1 Komponen Senyawa yang Terkandung pada Produk Bahan Bakar Cair (T = 350 °C Tanpa Katalis) 69 Tabel L5.2 Komponen Senyawa yang Terkandung pada Produk Bahan Bakar

Cair (T = 300 °C perbandingan PP : Katalis = 10 : 3) 71 Tabel L5.3 Hasil Analisis FTIR pada Bahan Bakar Cair yang dihasilkan dengan

Suhu Pirolisis 350 °C Tanpa Katalis 72 Tabel L5.4 Hasil Analisis FTIR pada Bahan Bakar Cair yang dihasilkan dengan

Suhu Pirolisis 300 °C dengan Perbandingan Jumlah Bahan Baku :

(19)

xvii

DAFTAR SINGKATAN

API American Petrolium Institute

ASTM American Standard Testing Method

FCC Fluid Cracking Catalyst

FTIR Fourier Transform Infra-Red

GC-MS Gas Chromatography Mass Spectofotometry

HDPE High Density Polyethylene

LDPE Low Density Polyethylene

LPG Liquified Petrolium Gas

MCM-41 Mobil Composition of Matter No.41

PBKG Plastik Bekas Kemasan Gelas PET Polyethylene Tereftalate

PP Polypropilene

PS Polystyrene

PVC Polyvinyl Chloride

(20)

DAFTAR SIMBOL

Simbol Keterangan Dimensi

° Derajat Celcius

Ω Beban maksimum ohm