LAMPIRAN 1
ALAT DAN BAHAN PENELITIAN
1. Peralatan Penelitian
Mortar dan Alu Ayakan 100 mesh
High Energy milling (HEM) Saringan
Particle Size Analyzer (PSA)
SEM-EDX
Vacuum Furnace
Magnetizer K-Series X-Ray Diffraction
Peralatan Archimedes Dryer
Molding
piknometer
Bata tahan panas Microhardness tester
2. Bahan Penelitian
Serbuk BaFe12O19
Serbuk FeMn
LAMPIRAN 2
DATA-DATA HASIL PENGUKURAN DENSITAS
1. True Density
Mengukur true density dengan menggunakan rumus :
1.1True density eksperimen
3. True density serbuk awal BaFe12O19 dan FeMn
Sampel ρs
(g/cm3)
BaFe12O19 5,2
FeMn 7,7
1.2True density teori
Pengukuran true density teori dilakukan dengan menggunakan rumus sebagai berikut :
( )
Keterangan :
ρx, ρy = Densitas sampel (g/cm3)
2. Bulk Density
Mengukur bulk density dari sampel berbentuk pelet menggunakan rumus :
Keterangan :
ρs = bulk density sampel (g/cm3)
mk = massa kering sampel (g)
mb = massa basah sampel (g)
LAMPIRAN 3
DATA PENGUKURAN DIAMETER PARTIKEL SERBUK DENGAN
MENGGUNAKAN SOFTWARE IMAGE-J
1. BaFe12O19 milling 30 menit
Diameter rata - rata 2.508451
LAMPIRAN 4
DATA HASIL ANALISIS XRD
1. Serbuk BaFe12O19
Raw Data
General information
Analysis date 2017/03/16 13:54:07
Sample name BaO6Fe2O3 Measurement date 2017/03/14 09:31:44
File name BaO6Fe2O3.ras Operator administrator
Comment
Measurement conditions
X-Ray 40 kV , 30 mA Scan speed / Duration time 2.0000 deg/min
Goniometer SmartLab(In-plane) Step width 0.0100 deg
Attachment RxRy Scan axis Theta/2-Theta
Filter Cu_K-beta Scan range 10.0000 - 90.0000 deg
CBO selection slit BB Incident slit 2/3deg
Diffrected beam mono. None Length limiting slit 10.0mm
Detector SC-70 Receiving slit #1 2/3deg
Scan mode CONTINUOUS Receiving slit #2 0.450mm
2. Serbuk BaFe12O19 + FeMn 1% milling 15 menit
Raw Data
General information
Analysis date 2017/03/16 14:11:33
Sample name BaO6Fe2O3 99%+FeMn 1% Measurement date 2017/03/14 10:13:53
File name BaO6Fe2O3 99%+FeMn 1%.ras Operator administrator
Comment
Measurement conditions
X-Ray 40 kV , 30 mA Scan speed / Duration time 2.0000 deg/min
Goniometer SmartLab(In-plane) Step width 0.0100 deg
Attachment RxRy Scan axis Theta/2-Theta
Filter Cu_K-beta Scan range 10.0000 - 90.0000 deg
CBO selection slit BB Incident slit 2/3deg
Diffrected beam mono. None Length limiting slit 10.0mm
Detector SC-70 Receiving slit #1 2/3deg
Scan mode CONTINUOUS Receiving slit #2 0.450mm
Measurement profile
3. Serbuk BaFe12O19 + FeMn 5 % milling 15 menit
Raw Data
General information
Analysis date 2017/03/16 14:04:01
Sample name BaO6Fe2O3 95%+FeMn 5% Measurement date 2017/03/14 10:55:52
File name BaO6Fe2O3 95%+FeMn 5%.ras Operator administrator
Comment
Measurement conditions
X-Ray
40 kV , 30 mA Scan speed / Duration time 2.0000 deg/min
Goniometer SmartLab(In-plane) Step width 0.0100 deg
Attachment RxRy Scan axis Theta/2-Theta
Filter Cu_K-beta Scan range 10.0000 - 90.0000 deg
CBO selection slit BB Incident slit 2/3deg
Diffrected beam mono. None Length limiting slit 10.0mm
Detector SC-70 Receiving slit #1 2/3deg
Scan mode CONTINUOUS Receiving slit #2 0.450mm Meas. data:BaO6Fe2O3 99%+FeMn 1% Calc. data:BaO6Fe2O3 99%+FeMn 1%
Measurement profile
4. BaFe12O19 + FeMn 10% milling 15 menit
Raw Data
General information
Analysis date 2017/03/16 14:00:23
Sample name BaO6Fe2O3 90%+FeMn 10% Measurement date 2017/03/14 11:37:52
File name BaO6Fe2O3 90%+FeMn 10%.ras Operator administrator
Comment
Measurement conditions
X-Ray 40 kV , 30 mA Scan speed / Duration time 2.0000 deg/min
Goniometer SmartLab(In-plane) Step width 0.0100 deg
Attachment RxRy Scan axis Theta/2-Theta
Filter Cu_K-beta Scan range 10.0000 - 90.0000 deg
CBO selection slit BB Incident slit 2/3deg
Diffrected beam mono. None Length limiting slit 10.0mm
Detector SC-70 Receiving slit #1 2/3deg
Scan mode CONTINUOUS Receiving slit #2 0.450mm
Measurement profile
Meas. data:BaO6Fe2O3 95%+FeMn 5% Calc. data:BaO6Fe2O3 95%+FeMn 5%
Meas. data:BaO6Fe2O3 90%+FeMn 10% Calc. data:BaO6Fe2O3 90%+FeMn 10%
2-theta (deg)
Intens
ity (
count
s)
20 40 60 80
LAMPIRAN 5
DATA HASIL PENGUJIAN HARDNESS VICKERS
1. BaFe12O19 99,5 wt% + FeMn 0,5 wt% milling 15 menit.
3. BaFe12O19 99,5 wt% + FeMn 3 wt% milling 15 menit.
6. BaFe12O19 99,5 wt% + FeMn 0,5 wt% milling 30 menit.
8. BaFe12O19 97 wt% + FeMn 3 wt% milling 30 menit.
9. BaFe12O19 95 wt% + FeMn 5 wt% milling 30 menit.
LAMPIRAN 6
DATA HASIL ANALISIS VSM
1. Sampel pelet BaFe12O19 milling 15 menit.
3. Sampel pelet BaFe12O19 + FeMn 5 wt%milling 30 menit.
5. Sampel serbuk BaFe12O19 + 5 wt % FeMn milling 15 menit
7. Sampel serbuk BaFe12O19 +10 wt % FeMn milling 15 menit
9. Sampel serbuk BaFe12O19 + 5 wt % FeMn milling 30 menit
LAMPIRAN 7
DATA HASIL PENGUKURAN BH MAX
1. Sampel Serbuk
a. BaFe12O19+ FeMn 1 wt% milling 15 menit.
0 500 1000 1500 2000
15 min FeMn 1 %
0 500 1000 1500 2000
15 min FeMn 5 %
800 900 1000 1100
BH
Poly. (BH)
c. BaFe12O19 + FeMn 10 wt% milling 15 menit.
0 500 1000 1500 2000
d. BaFe12O19 + FeMn 1 wt% milling 30 menit.
0 500 1000 1500
30 min 1 % FeMn
0 500 1000 1500
BH 30 min 1 % FeMn
0 500 1000 1500
f. BaFe12O19 + FeMn 10 wt% milling 30 menit.
2. Sampel Pelet
a. BaFe12O19 milling 15 menit.
0 500 1000 1500
30 min 10 % FeMn
0 500 1000 1500
b. BaFe12O19 milling 30 menit.
0 200 400 600 800 1000 1200
BH max
BH max
Poly. (BH max)
y = -1.9714x2 + 3124.5x - 887889
0 500 1000 1500
d. BaFe12O19 + FeMn 5 wt%milling 30 menit.
Poly. (BH MAX)
0
LAMPIRAN 8
DATA HASIL ANALISIS PSA ( Particle Size Analyzer )