PRELIMINARY INVESTIGATION OF PLASTICS
JOINING PROCESS
SITI NOORAISHAH BINTI ELIES
B051010171
UNIVERSITI TEKNIKAL MALAYSIA MELAKA
UNIVERSITI TEKNIKAL MALAYSIA MELAKA
PRELIMINARY INVESTIGATION OF PLASTICS JOINING
PROCESS
This report submitted in accordance with requirement of the Universiti Teknikal Malaysia Melaka (UTeM) for the Bachelor Degree of Manufacturing Engineering
(Manufacturing Process) (Hons.)
by
SITI NOORAISHAH BINTI ELIES B051010171
900409015894
UNIVERSITI TEKNIKAL MALAYSIA MELAKA
BORANG PENGESAHAN STATUS LAPORAN PROJEK SARJANA MUDA
TAJUK: Preliminary Investigation of Plastics Joining Process
SESI PENGAJIAN: 2012/13 Semester 2
Saya SITI NOORAISHAH BINTI ELIES
mengaku membenarkan Laporan PSM ini disimpan di Perpustakaan Universiti Teknikal Malaysia Melaka (UTeM) dengan syarat-syarat kegunaan seperti berikut:
1. Laporan PSM adalah hak milik Universiti Teknikal Malaysia Melaka dan penulis.
2. Perpustakaan Universiti Teknikal Malaysia Melaka dibenarkan membuat salinan
untuk tujuan pengajian sahaja dengan izin penulis.
3. Perpustakaan dibenarkan membuat salinan laporan PSM ini sebagai bahan
pertukaran antara institusi pengajian tinggi. 4. **Sila tandakan (/)
SULIT
TERHAD
TIDAK TERHAD
(Mengandungi maklumat yang berdarjah keselamatan atau kepentingan Malaysiasebagaimana yang termaktub dalam AKTA RAHSIA RASMI 1972)
(Mengandungi maklumat TERHAD yang telah ditentukan oleh organisasi/badan di mana penyelidikan dijalankan)
Alamat Tetap:
NO. 1 Jalan KM 2,
Taman Kota Mas,
81900 Kota Tinggi, Johor.
Tarikh: _________________________
Disahkan oleh:
Cop Rasmi:
Tarikh: _______________________
DECLARATION
I hereby, declared this report entitled “Preliminary Investigation of Plastics Joining Process” is the results of my own research except as cited in references.
Signature :
Author’s Name : Siti Nooraishah Binti Elies
APPROVAL
This report is submitted to the Faculty of Manufacturing Engineering of UTeM as a partial fulfillment of the requirements for the degree of Bachelor of Manufacturing Engineering (Manufacturing Process) (Hons.). The member of the supervisory committee is as follow:
i
ABSTRAK
ii
ABSTRACT
iii
DEDICATION
iv
ACKNOWLEDGEMENT
v
List of Abbreviations, Symbols, Specialized Nomenclature ix
CHAPTER 1: INTRODUCTION 1
1.1 Project Background 1
1.2 Problem Statement 3
1.3 Scope of Project 4
1.4 Objectives 5
1.5 Theory 6
1.5.1 Laser Processing Overview 6
1.5.2 Definition of Laser 8
1.5.3 The Work Process of Laser 8
1.5.4 Laser Properties 10
1.5.5 Types of Laser 12
1.5.6 Laser Machining 14
1.5.7 Laser Processing 17
vi
1.7 Plastics Joining Processes 25
1.7.1 Fusion Welding 26
1.7.2 Types of Joint 27
CHAPTER 2: LITERATURE REVIEW 28
2.1 Laser Welding of Non-Metallic Material 28
2.1.1 Thermoplastics Material 28
CHAPTER 3: METHODOLOGY 35
3.1 Research Methodology Flowchart 35
3.2 Material Selection 37
3.3 Investigation of Process Parameters 38
3.4 Design Parameters Identification 38
3.5 Design of Experiment (DOE) 39
3.7 Experiment Setup 44
3.8 Observation & Evaluation 48
3.8.1 Non-destructive Test 48
3.8.2 Destructive Test 49
3.9 Result 52
3.10 Discussion/Conclusion 52
CHAPTER 4: RESULT & DISCUSSION 53
4.1 Joined Produced 53
vii
4.3 Flexural Result 65
4.4 Defects 70
4.5 Effect of Travel Speed and Laser Power on Joining Process 71
4.6 Effect of Gas Pressure on Joining Process 72
CHAPTER 5: CONCLUSIONS AND RECOMMENDATIONS 73
REFERENCES 75
APPENDICES 79
A 79
B 80
viii
Summarizing overview of carbon black concentration, optical penetration depth and bridged gap for the investigated flat samples while applying contour welding (U. A. Russek et al., 2003)
D.O.E Matrix for experimental work Parameters and Level
Basic specifications of the LVD Helius Hybrid 2513 Laser Cutting Machine
D.O.E Matrix
Specimen dimension
Semi crystalline and amorphous structure
Length measurement and the percentage of error (% error) Width measurement and the percentage of error (% error) Thickness dimension and the percentage of error (% error)
Maximum force, flexural strength and flexural strain of the joined plastic
ix
Classification of Laser Material Processing Flow Chart (Majumdar J. D. And Manna I., 2003)
Simple Atom Model Photon Simulation Photon Amplification
Comparison of Monochromatic Light between Fluorescent Light and Laser (Wasikowski J., 2003)
Comparison of Coherency between Normal Light and Laser (Wasikowski J., 2003)
Comparison of Radiance of Light Bulb and Laser Beam (Wasikowski J., 2003)
Schematic of One, Two and Three-Dimensional Laser Machining (Wasikowski J., 2003)
Laser Cutting Head (TRUMPF, 2000)
Focal positon (Manual of Helius 2513 Laser Machine, 2000) Stand off Distance (Manual of Helius 2513 Laser Machine, 2000) Properties of polymers
Structures of thermoplastics Joining processes
Basic weld joints
Averaged weld failure force and visual ratings for each of factor level combinations. Each colour code represents different level of visual appearance (James D. Van de Ven and Arthur G. Erdman, 2007)
Weld width as a function of velocity and laser power (James D. Van de Ven and Arthur G. Erdman, 2007)
Weld strength as a function of velocity and laser power (James D.
x
Van de Ven and Arthur G. Erdman, 2007)
Main effects plot for S/N ratios (B. Acherjee et al., 2010) Percentage distribution of each process parameter to weld strength (B. Acherjee et al., 2010)
Methodology Flowchart HDPE engine oil bottle
Helius Hybrid 2513 Laser Cutting Machine Flow chart for experimental setup
Drawing of specimen to be cut and join
Screen display where parameter values were change Laser beam movement direction
Venire Calliper
Stereo Digital Imaging Microscopy Loading diagram
Universal Testing Machine Flexural test on joined plastic
Image of two plastic sheets before subjected to laser joining process
Image of two plastic sheets after subjected to laser joining process
Close view of joining area on specimen produced from experiment number 7
Close view of ‘frame-line’ on inside part of specimen from experiment number 1
Three points at which the length were observed Three points at which the width were observed
Points at which the thickness dimensions were observed Maximum Force versus Number of Experiment
Flexural Strength versus Number of Experiment Flexural Strain versus Number of Experiment
xi
LIST OF ABBREVIATIONS, SYMBOLS, SPECIALIZED
NOMENCLATURE
angstroms - measure of length, 1 angstrom= 10E-10m ANOVA - Analysis Of Variance
ANSI - American National Standard Institute cm - centimetre
xii
ISO - International Organization for Standardization
J - Joule
K - Kelvin
k - kilo
kg - Kilogram
L - Length
LASER - Light Amplification by Stimulated Emission of Radiation
m - meter
xiii
PSM - Bachelors Degree Project (Projek Sarjana Muda)
R - Radius
TEA - Transversely Excited Atmosphere Pressure
1
Chapter 1 is basically includes the entire report content starting from Project Background up to Plastics Joining Processes. Related information regarding laser processing is included in this chapter.
1.1 Project Background
Laser machining is widely known for cutting almost any materials. The highly focus, high-density energy source melts and evaporates portions of the workpiece in a controlled manner. Laser cutting which is one laser machining process could be referred as a material removal process accomplished by laser material interaction. Besides machining, laser also is been used in processing such as welding. Laser welding is a non-contact process and involves localized heat treating of materials to modify the surface mechanical and tribological properties (Kalpakjian, 2010).
Used products with plastics based are usually recycled. When the material is recycled, the properties of the material will not remain the same. Usually the properties are reduced and qualities of secondary products are low. Instead of re-melt or recycle the material, the used product is reused. In addition, due to high investment cost needed to setup a laser machine, optimization of existing laser cutting machine is the main goal of this study. For experimental, laser joining process will be performed by laser cutting machine instead of laser welding machine. In laser processing, the controllable process parameters are quite same for any process.
INTRODUCTION
2
The challenge in conducting this study is to identify the most suitable parameters to be applied in laser welding. This preliminary investigation will determined the capability of CO2 laser to produce join between materials by varying
some of process parameters. A laser cutting machine with rated power 3kW is used in this experimentation work.
The join is evaluated through visual inspection and destructive tests. Throughout this study, CO2 laser cutting machine has proved its ability to melt and
3
1.2 Problem Statement
Huge wastage of plastic bottle has become a big problem faced by the country. In average, one Malaysian citizen has produced abut 0.8kg waste per day. It is expected that in 2020, 30 000 tonne waste will be produced since only 5% of the total waste is recycled. This is a hug number for a small country like Malaysia. Due to this problem, waste plastic (HDPE) is chosen as the main material to be used in experimentation. The plastic is used in order to maintain its properties since re-meting will just reduce it. Besides, high cost is required to setup recycling equipment.
4
1.3 Scope of Project
The aim of this project is to identify the best controllable process parameters that have big impact in laser processing. In order to produce good join, a set of process variables is developed and recommended. The values of each three chosen parameters which are laser power, travel speed and gas pressure are varied within the range of experiment while other controllable parameters are fixed. The model of laser cutting machine to perform joining process is Helius 2513 hybrid series that was made in Belgium. The laser machine is equipped with nitrogen and oxygen as laser assisted gas and carbon dioxide (CO2) laser beam with rated power of 3kW. The
5
1.4 Objectives
The main objectives of this project are:
i. To investigate the ability to form stack joining of HDPE by CO2 laser.