LAMPIRAN I
Nama Nim
Material : Pasir Tanggal
0 0 0 0.00 0 100
23 21 44 2.20 2.2 97.8
43 56 99 4.95 7.15 92.85
128 132 260 13.00 20.15 79.85
335 342 677 33.85 54 46
265 260 525 26.25 80.25 19.75
187 175 362 18.10 98.35 1.65
19 14 33 1.65 100 0
1000 1000 2000 100
262.1 100
Halus Sedang Kasar
ANALISA AYAKAN PASIR UNTUK
MATERIAL BETON
Mengetahui, : 2.2 < FM < 2.6
: 2.6 < FM < 2.9 : 2.9 < FM < 3.2
Berat Fraksi Tertahan
9.50 (3/8 - in) 4.75 (No.4) 2.36 (No.8) 1.18 (No.16) 0.60 (No.30) 0.30 (No.50)
Berat Total (gram) Diameter Ayakan.
(mm) (No.) %
Kumulatif
Asisten Lab. Beton USU
Muhammad Fauzi 0.15 (No.100)
Pan Total
= 2.62
Fineness Modulus (FM) =
Klasifikasi pasir yang baik :
(ASTM C 136 - 84a)
: Rumanto
Berat Sampel 1
(gram)
Berat Sampel 2
Nama Nim
Material : Pasir
Tanggal
kg/m3 996.77
539.96
mm 5
Net Weight (G)
Muhammad Fauzi
Total Rata-rata
BERAT ISI AGREGAT HALUS UNTUK
MATERIAL BETON
ASTM C 29/C 29M - 90
: Rumanto : 08 0404 153
Berat
Cara Merojok Cara Longgar Berat Air
Berat Isi Air Faktor Koreksi, C=(B/A) Diameter Agregat Maksimum 1. Calibration Of Measure
3.01 2.97
Sampel 1 Sampel 2
Berat Isi (G*K), kg/m3
Mengetahui, Asisten Lab.Beton USU 5.97
Suhu Ruangan Suhu Air Berat Bejana
2.3
2. Hasil Pemeriksaan
: 12 Maret 2014
Nama Nim
Material : Pasir
Tanggal
Sampel 1 Sampel 2 Rata-rata
500 500 500
494 493 493.5
676 676 676
A
Berat Jenis Semu
BERAT JENIS DAN ABSORBSI AGREGAT
HALUS UNTUK MATERIAL BETON
ASTM C 128 - 88
Berat agregat dalam keadaan SSD di udara, g (S)
974 : 08 0404 153
=
Berat Jenis SSD =
Berat piknometer + agregat + air yang dikalibrasi, g ( C )
: 12 Maret 2014
Mengetahui, Asisten Lab.Beton USU
Muhammad Fauzi 2.44
Berat piknometer yang terisi air, g (B)
Berat Jenis Kering
: Rumanto
=
Nama Nim
Material : Pasir
Tanggal
Sample 1 Sample 2 Average
500 500 500
490 491 490
: 08 0404 153
: 12 Maret 2014
Asisten Lab.Beton USU
Muhammad Fauzi 9
1.8
9.5
1.9
Mengetahui,
Berat agregat mula-mula, g
Berat kering agregat setelah dicuci, g
Berat lumpur yang telah dicuci dengan ayakan No.200, g
Kadar lumpur pada agregat yang telah dicuci dengan ayakan No.200, %
10
2
PEMERIKSAAN KADAR LUMPUR
AGREGAT HALUS UNTUK MATERIAL
BETON
ASTM C 117 - 90
Nama Nim
Material : Pasir
Tanggal
Kontrol
OK OK OK OK OK
Mengetahui, Asisten Lab.Beton
Muhammad Fauzi
Spesifikasi
2.20 - 3.20 Kering<SSD<Semu
>1125 kg/m3
< 5% < 5%
Hasil
FM = 2.62 SSD = 2.48
UW = 1241.11 kg/m3
1.90% 1.32%
Pemeriksaan Analisa Ayakan
Berat Jenis Berat Isi Kadar Lumpur
: 08 0404 153
: 12 Maret 2014
Absorbsi
: Rumanto
ASTM C 136 - 84a & ASTM D 448 - 86
Nama Nim
Material : Batu pecah
Tanggal
0 0 0 0.00 0 100.00
1006 1112 2118 52.95 52.95 47.05
757 657 1414 35.35 88.30 11.70
230 227 457 11.43 99.73 0.28
0 0 0 0.00 99.73 0.28
2000 2000 4000 100
= 7.4
: 12 Maret 2014
Kumulatif
38.1 mm
Muhammad Fauzi
0.15 mm Pan Total
Fineness Modulus
Mengetahui, Asisten lab.Beton
Tertahan
(%) Lolos %) Diameter Ayakan.
(mm) (No.)
Berat Fraksi Tertahan
%
ANALISA AYAKAN AGREGAT KASAR
UNTUK MATERIAL BETON
Berat
Nama Nim
Material : Batu pecah
Tanggal
o
C 28
o
C 26
kg 5
kg 8.1
kg/m3 996.77
123.058
mm 25
: 08 0404 153
: 12 Maret 2014
Mengetahui, Asisten Lab.Beton
Net Weight (G) 14.15 13.3
Berat Isi (G*K), kg/m3 1741.28 1636.68
Total 38.3 36.6
Rata-rata 19.15 18.3
Sampel 1 19.1 18.4
Sampel 2 19.2 18.2
1. Calibration Of Measure Suhu Ruangan
Suhu Air Berat Bejana Berat Air (A) Berat Isi Air (B) Faktor Koreksi, C=(B/A) Diameter Maksimum Agregat
Berat
Cara Merojok Cara Longgar
BERAT ISI AGREGAT KASAR UNTUK
MATERIAL BETON
ASTM C 29/C 29 M - 90
: Rumanto
Nama Nim
Material : Batu pecah
Tanggal
Sample 1 Sample 2 Average
753 751 752
1232 1230 1231
A (B-C)
B (B-C)
A (A-C) (B-A)x100
A
Mengetahui. Asisten Lab.Beton
Muhammad Fauzi
=
Absorbsi, % =
2.57 2.57
1.54
Berat Jenis Semu =
2.52 2.51 2.51
: 08 0404 153
: 12 Maret 2014
1250 1250 1250
2.48 2.46 2.47
Berat agregat dalam keadaan SSD di udara, g (B)
Berat agregat dalam air, g (C )
Berat kering oven agregat di udara, g (A)
Berat Jenis Kering =
Berat Jenis SSD
2.57
1.46 1.63
ASTM C 127 - 88
BERAT JENIS DAN ABSORBSI AGREGAT
KASAR UNTUK MATERIAL BETON
Nama Nim
Material : Batu pecah
Tanggal
Sampel 1 Sampel 2 Rata-rata
1000 1000 1000
993 992 992.5
Muhammad Fauzi 7.5
Kadar lumpur pada agregat yang telah dicuci dengan
ayakan No.200, % 0.7 0.8 0.75
: 08 0404 153
: 12 Maret 2014
PEMERIKSAAN KADAR LUMPUR
AGREGAT KASAR UNTUK MATERIAL
BETON
ASTM C 117 - 90
Berat agregat mula-mula, g
Berat kering agregat setelah dicuci, g
Mengetahui, Asisten Lab.Beton USU
Berat lumpur yang telah dicuci dengan ayakan No.200,
g 7 8
Nama Nim
Material : Pasir
Tanggal
Kontrol
OK OK
OK OK OK
Mengetahui, Asisten Lab.Beton USU
Muhammad Fauzi
Kadar Lumpur 0.75% < 1%
Absorbsi 1.54% < 5%
Berat Jenis SSD = 2.51 Kering<SSD<Semu
Berat Isi UW = 1636.68 kg/m3
>1250 kg/m3
: 12 Maret 2014
Pemeriksaan Hasil Spesifikasi Analisa Ayakan FM = 7.41 5.5 - 7.5
: 08 0404 153 : Rumanto
Nama Nim
Material : Potongan Bambu Betung Tanggal
Kontrol OK OK
-Mengetahui, Asisten Lab.Beton USU
Muhammad Fauzi
Absorbsi 45.80%
-Berat Isi UW = 379.21 kg/m3
-Analisa Ayakan FM = 7.26 5.5 - 7.5
Berat Jenis SSD = 1.14 Kering<SSD<Semu : 12 Maret 2014
Pemeriksaan Hasil Spesifikasi
KESIMPULAN PEMERIKSAAN AGREGAT
KASAR (BAMBU)
Nama Nim
Material : Potongan bambu betung
Tanggal
0 0 0 0.00 0.00 100.00
475 553.5 1028.5 25.71 25.71 74.29
1525 1446.5 2971.5 74.29 100.00 0.00
0 0 0 0.00 100.00 0.00
2000 2000 4000 100
= 7.3
Mengetahui, Asisten lab.Beton
Muhammad Fauzi
0.30 mm 0.15 mm
Pan Total
Fineness Modulus
ANALISA AYAKAN AGREGAT KASAR (BAMBU)
UNTUK MATERIAL BETON
ASTM C 136 - 84a & ASTM D 448 - 86
: Rumanto : 08 0404 153 Berat Fraksi Tertahan
4.76 mm 2.38 mm 1.19 mm 0.60 mm Diameter Ayakan.
(mm) (No.)
Nama Nim
Material : Potongan bambu betung
Tanggal
o
C 28
o
C 26
kg 5
kg 9.2
kg/m3 996.77
108.3446
mm 20
Mengetahui, Asisten Lab.Beton
Muhammad Fauzi
BERAT ISI AGREGAT KASAR (BAMBU)
UNTUK MATERIAL BETON
ASTM C 29/C 29 M - 90
: Rumanto
Suhu Ruangan Suhu Air
: 08 0404 153
: 12 Maret 2014
1. Calibration Of Measure
Faktor Koreksi, C=(B/A) Diameter Maksimum Agregat
Berat Bejana Berat Air (A) Berat Isi Air (B)
Sampel 1 2. Hasil Pemeriksaan
Berat Cara Longgar
8.5
Net Weight (G) 3.5
Nama Nim
Material : Potongan bambu betung Tanggal
Sample 1 Sample 2 Average
125 115 120
536 548 542
A
(B-C)
B
(B-C)
A (A-C)
(B-A)x100
B
Mengetahui. Asisten Lab.Beton
Muhammad Fauzi
88.5 88
1.13 1.14
Berat Jenis Semu = 1.30 1.27 1.28
Berat Jenis SSD = 1.14
Absorbsi, % = 87.5
Berat agregat dalam air, g (C)
Berat Jenis Kering =
Berat kering oven agregat di udara, g (A)
Berat agregat dalam keadaan SSD di udara, g (B) 1000 1000 1000 : Rumanto
: 08 0404 153
: 12 Maret 2014
0.61 0.62 0.62
ASTM C 127 - 88
BERAT JENIS DAN ABSORBSI AGREGAT
KASAR (BAMBU) UNTUK MATERIAL
LAMPIRAN II
Nama Semen
Ag. Halus : Pasir Ag. Kasar
Air : PDAM
Slump : 6-18 cm
: 55
Faktor Air Semen Standar : 0.5
Kerikil 170 230 330 400
: 0.57
Koefisien koreksi laboratorium 0,95 : 0.54
: 0.6
: 0.54
Ø max 0-1 cm 1-3 cm 3-6 cm 6-18 cm
150 180 205 225
180 205 230 250
135 160 180 195
170 190 210 225
115 140 160 175
155 175 190 205
: 341,6 kg/m3 beton
MIX DESIGN BETON (f'c = 17 MPa)
: Rumanto
: f'c 17 Mpa Deviasi
Rencana pelaksanaan di lokasi : 259.82 kg/cm2
Jenis Agregat
Kasar
Batu Pecah
3 7 28 91
Umur Beton Pada Saat Diuji (hari)
190 270 370 450
Berdasarkan grafik faktor air semen
Direncanakan faktor air semen 1. Perencanaan Faktor Air Semen
2. Perencanaan air bebas untuk campuran beton (1lt/m3)
Tidak pecah Pecah
Jenis
Faktor air semen maksimum : Semen Padang Type 1
: Batu Pecah
Mutu Rencana
Tidak pecah Pecah Tidak pecah
Pecah
Agregat Slump
10 mm
20 mm
30 mm
Direncanakan memakai air sebanyak
Pemakaian semen sebanyak
: 185 lt/m3 beton
Zona I Zona II Zona III Zona IV
9.5 100 100 100 100 100 0
4.75 90-100 90-100 90-100 95-100 97.8 2.2
2.36 60-95 75-100 85-100 95-100 92.85 7.2
1.18 30-70 55-90 75-100 90-100 79.85 20.2
0.6 15-34 35-59 60-79 80-100 46 54
0.3 5--20 8--30 12--40 15-50 19.75 80.3
0.15 0-10 0-10 0-10 0-15 1.65 98.4
I II III IV
%min 40.0 32.0 26.5 22.0
%max 48.0 40.0 32.0 26.5
86 57
40
diperlukan pasir antara : 32% - 40% dari total agregat
3. Klasifikasi agregat halus
Diameter ayakan
(mm)
Persentase lolos ayakan
Agregat
Klasifikasi daerah perbutiran
Ø agregat max
Faktor zona pasir
(%) 71 100
Diameter Ayakan
Zona I
Diameter Ayakan
Zona II
0
Diameter Ayakan
Zona III
0
Diameter Ayakan
Pasir Ag.kasar Fineness Modulus
4. Klasifikasi agregat campuran
Komposisi agregat campuran yang digunakan
Diameter ayakan
(mm)
Komposisi rencana
Kumulatif lolos
Kumulatif tertahan Komposisi
Fraksi
1 kg/m3
342,6 kg/m3
295,4 liter 704,6 liter koreksi penggunaan semen
semen yang digunakan volume pasta
volume agregat
0
Diameter Ayakan
Ag.halus Ag.kasar
2.481 2.51
40 60
0.993 1.506
673.3 1010
Semen 1.00
Pasir 1.97
Ag.Kasar 2.95
Air 0.54
Koreksi Air, Pasir, dan Ag.kasar
1.32% 1.54% 1.00% 1.00%
Komposisi Adukan Beton Rencana dengan Agregat
Semen 1.00
Pasir 1.96
Ag.kasar 2.94
Air 0.55
Semen 40 liter
Pasir 97,8 kg 78,8 liter
Ag.kasar 147,2 kg 90,0 liter
Air 27,7 kg 27,7 liter
Ag.campuran
2.5
1683.3 Berat jenis SSD
Komposisi agregat, %
Berat jenis untuk agregat campuran Berat total agregat, kg
Berat total tiap agregat, kg
109,8 liter
271,3 liter
402,4 liter
185,5 liter
342,6 kg/m3
673,3 kg/m3
50 kg (1 zak)
189,7 kg/m3
109,8 liter
270,1 liter
402,0 liter
189,7 liter
Komposisi beton untuk 1 zak semen: Komposisi agregat
Komposisi Akhir Beton dalam Keadaan SSD
1010,0 kg/m3
185,5 kg/m3
Absorbsi air pada agregat halus (Ca) Absorsi air pada agregat kasar (Da) Kandungan air pada agregat halus (Ck) Kandungan air pada agregat kasar (Dk)
342,6 kg/m3
670,1 kg/m3
LAMPIRAN III
Variasi Benda uji Berat basah Berat kering Absorbsi Rata-rata
(%) (kg) (kg) (%) (%)
7 12.80 12.64 1.27 8 13.01 12.85 1.25 9 12.80 12.64 1.27 10 13.05 12.89 1.24 11 12.78 12.62 1.27 12 12.75 12.60 1.19 7 12.54 12.36 1.46 8 12.51 12.32 1.54 9 12.31 12.15 1.32 10 12.44 12.27 1.39 11 12.25 12.09 1.32 12 12.30 12.11 1.57 7 12.18 11.98 1.67 8 12.11 11.94 1.42 9 12.02 11.88 1.18 10 12.18 12.00 1.50 11 12.16 11.94 1.84 12 12.14 11.90 2.02 7 11.83 11.60 1.98 8 11.59 11.46 1.13 9 11.74 11.54 1.73 10 11.57 11.40 1.49 11 11.77 11.59 1.55 12 11.66 11.46 1.75 7 11.37 11.18 1.70 8 11.42 11.20 1.96 9 11.37 11.19 1.61 10 11.26 11.10 1.44 11 11.22 11.06 1.45 12 11.24 11.04 1.81
LEMBAR DATA
Mengetahui, Asisten Lab.Beton USU
Muhammad Fauzi
PENGUJIAN ABSORBSI BETON
Variasi Benda uji Diameter Panjang Volume Berat kering Berat jenis Berat jenis Rata-rata (%) (cm) (cm) (m3) (kg) (kg/m3) (kg/m3)
1 15 30 0.0053 12.64 2385.47
2 15 30 0.0053 12.83 2421.33
3 15 30 0.0053 12.76 2408.12
4 15 30 0.0053 12.68 2393.02
5 15 30 0.0053 12.75 2406.23
6 15 30 0.0053 12.64 2385.47
7 15 30 0.0053 12.64 2385.47
8 15 30 0.0053 12.85 2425.10
9 15 30 0.0053 12.64 2385.47
10 15 30 0.0053 12.89 2432.65
11 15 30 0.0053 12.62 2381.69
12 15 30 0.0053 12.60 2377.92
1 15 30 0.0053 12.18 2298.66
2 15 30 0.0053 12.15 2292.99
3 15 30 0.0053 12.38 2336.40
4 15 30 0.0053 12.11 2285.44
5 15 30 0.0053 12.42 2343.95
6 15 30 0.0053 12.18 2298.66
7 15 30 0.0053 12.36 2332.63
8 15 30 0.0053 12.32 2325.08
9 15 30 0.0053 12.15 2292.99
10 15 30 0.0053 12.27 2315.64
11 15 30 0.0053 12.09 2281.67
12 15 30 0.0053 12.11 2285.44
1 15 30 0.0053 12.00 2264.69
2 15 30 0.0053 12.02 2268.46
3 15 30 0.0053 11.96 2257.14
4 15 30 0.0053 11.90 2245.81
5 15 30 0.0053 11.84 2234.49
6 15 30 0.0053 11.92 2249.59
7 15 30 0.0053 11.98 2260.91
8 15 30 0.0053 11.94 2253.36
9 15 30 0.0053 11.88 2242.04
10 15 30 0.0053 12.00 2264.69
11 15 30 0.0053 11.94 2253.36
12 15 30 0.0053 11.90 2245.81
1 15 30 0.0053 11.42 2155.23
2 15 30 0.0053 11.78 2223.17
3 15 30 0.0053 11.54 2177.87
4 15 30 0.0053 11.44 2159.00
5 15 30 0.0053 11.53 2175.98
6 15 30 0.0053 11.46 2162.77
7 15 30 0.0053 11.60 2189.20
8 15 30 0.0053 11.46 2162.77
LEMBAR DATA
PENGUJIAN BERAT JENIS BETON
60% 2173.78
0% 2398.99
20% 2307.46
Variasi Benda uji Diameter Panjang Volume Berat kering Berat jenis Berat jenis Rata-rata
9 15 30 0.0053 11.54 2177.87
10 15 30 0.0053 11.40 2151.45
11 15 30 0.0053 11.59 2187.31
12 15 30 0.0053 11.46 2162.77
1 15 30 0.0053 11.08 2091.06
2 15 30 0.0053 11.18 2109.93
3 15 30 0.0053 10.86 2049.54
4 15 30 0.0053 10.60 2000.47
5 15 30 0.0053 11.16 2106.16
6 15 30 0.0053 11.00 2075.96
7 15 30 0.0053 11.18 2109.93
8 15 30 0.0053 11.20 2113.71
9 15 30 0.0053 11.19 2111.82
10 15 30 0.0053 11.10 2094.83
11 15 30 0.0053 11.06 2087.28
12 15 30 0.0053 11.04 2083.51
Muhammad Fauzi Mengetahui, Asisten Lab.Beton USU
Variasi Umur Benda uji Berat Beban Tekan Luas Penampang
Kuat tekan
beton Rata-rata
(%) (kg) (kN) (mm2) (MPa) (MPa)
1 12.64 384 17662.5 21.74 2 12.83 450 17662.5 25.48 3 12.76 368 17662.5 20.84 4 12.68 374 17662.5 21.17 5 12.75 428 17662.5 24.23 6 12.64 328 17662.5 18.57 1 12.18 280 17662.5 15.85 2 12.15 244 17662.5 13.81 3 12.38 324 17662.5 18.34 4 12.11 348 17662.5 19.70 5 12.42 270 17662.5 15.29 6 12.18 344 17662.5 19.48 1 12.00 198 17662.5 11.21 2 12.02 176 17662.5 9.96 3 11.96 186 17662.5 10.53 4 11.90 206 17662.5 11.66 5 11.84 148 17662.5 8.38 6 11.92 224 17662.5 12.68 1 11.42 136 17662.5 7.70 2 11.78 148 17662.5 8.38 3 11.54 166 17662.5 9.40
4 11.44 114 17662.5 6.45
5 11.53 100 17662.5 5.66
6 11.46 128 17662.5 7.25
1 11.08 128 17662.5 7.25
2 11.18 96 17662.5 5.44
3 10.86 84 17662.5 4.76
4 10.60 122 17662.5 6.91
5 11.16 118 17662.5 6.68
6 11.00 68 17662.5 3.85
22.01
LEMBAR DATA
PENGUJIAN KUAT TEKAN BETON
Mengetahui, Asisten Lab.Beton USU
Muhammad Fauzi
5.81 40%
60%
80%
Variasi Benda Uji Umur Diameter Panjang Beban tekan Kuat Tarik Belah Rata - rata
LEMBAR DATA
PENGUJIAN KUAT TARIK BELAH BETON
Mengetahui, Asisten Lab.Beton USU
Variasi Umur Benda Uji Regangan Tegangan Elastisitas Rata-rata
(%) (MPa) (MPa) (MPa)
1 0.00020 21.741 62842.843
2 0.00023 25.478 62823.807
3 0.00020 20.835 62574.328
4 0.00019 21.175 65522.158
5 0.00023 24.232 61915.032
6 0.00018 18.570 62601.641
1 0.00036 15.853 47426.435
2 0.00013 13.815 67401.764
3 0.00018 18.344 63652.428
4 0.00019 19.703 63227.487
5 0.00016 15.287 66646.059
6 0.00018 19.476 66873.779
1 0.00026 11.210 33501.662
2 0.00029 9.965 63270.252
3 0.00027 10.531 36013.747
4 0.00018 11.663 47532.575
5 0.00014 8.379 45469.110
6 0.00018 12.682 48008.315
1 0.00012 7.700 45698.109
2 0.00010 8.379 53220.099
3 0.00012 9.398 55742.727
4 0.00013 6.454 39131.374
5 0.00012 5.662 35204.239
6 0.00025 7.247 29961.518
1 0.00052 7.247 10041.723
2 0.00051 5.435 8701.477
3 0.00056 4.756 7629.832
4 0.00050 6.907 10217.200
5 0.00049 6.681 10231.326
6 0.00030 3.850 12054.743
Muhammad Fauzi 28 hari
LEMBAR DATA
PENGUJIAN ELASTISITAS BETON
Mengetahui, Asisten Lab.Beton USU 0%
20%
40%
60%
80% 9812.717
LEMBAR DATA PENGUJIAN ELASITISITAS BETON
P Pembacaan
dial ∆L σ ε P
Pembacaan
dial ∆L σ ε P
Pembacaan
dial ∆L σ ε P
Pembacaan
dial ∆L σ ε P
Pembacaan
dial ∆L σ ε P
Pembacaan
dial ∆L σ ε (%) (kN) (mm) (mm) (MPa) (mm) (kN) (mm) (mm) (MPa) (mm) (kN) (mm) (mm) (MPa) (mm) (kN) (mm) (mm) (MPa) (mm) (kN) (mm) (mm) (MPa) (mm) (kN) (mm) (mm) (MPa) (mm)
0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0
50 16 0.16 2.83086 0.00053 50 13 0.13 2.83086 0.00043 50 14 0.14 2.83086 0.00047 50 13 0.13 2.83086 0.00043 50 15 0.15 2.83086 0.0005 50 15 0.15 2.83086 0.0005
100 30 0.3 5.66171 0.001 100 25 0.25 5.66171 0.00083 100 28 0.28 5.66171 0.00093 100 27 0.27 5.66171 0.0009 100 28 0.28 5.66171 0.00093 100 28 0.28 5.66171 0.00093
150 42 0.42 8.49257 0.0014 150 40 0.4 8.49257 0.00133 150 40 0.4 8.49257 0.00133 150 39 0.39 8.49257 0.0013 150 39 0.39 8.49257 0.0013 150 39 0.39 8.49257 0.0013
200 50 0.5 11.3234 0.00167 200 55 0.55 11.3234 0.00183 200 51 0.51 11.3234 0.0017 200 49 0.49 11.3234 0.00163 200 50 0.5 11.3234 0.00167 200 50 0.5 11.3234 0.00167
250 63 0.63 14.1543 0.0021 250 68 0.68 14.1543 0.00227 250 67 0.67 14.1543 0.00223 250 64 0.64 14.1543 0.00213 250 65 0.65 14.1543 0.00217 250 65 0.65 14.1543 0.00217
300 76 0.76 16.9851 0.00253 300 83 0.83 16.9851 0.00277 300 82 0.82 16.9851 0.00273 300 74 0.74 16.9851 0.00247 300 80 0.8 16.9851 0.00267 300 80 0.8 16.9851 0.00267
350 90 0.9 19.816 0.003 350 99 0.99 19.816 0.0033 350 93 0.93 19.816 0.0031 350 87 0.87 19.816 0.0029 350 95 0.95 19.816 0.00317 328 95 0.95 18.5704 0.00317
384 102 1.02 21.741 0.0034 400 112 1.12 22.6469 0.00373 368 105 1.05 20.8351 0.0035 374 110 1.1 21.1748 0.00367 400 114 1.14 22.6469 0.0038 - - - - -- - - 450 123 1.23 25.4777 0.0041 - - - 428 131 1.31 24.2321 0.00437 - - - -
-0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0
50 9 0.09 2.83086 0.0003 50 11 0.11 2.83086 0.00037 50 13 0.13 2.83086 0.00043 50 12 0.12 2.83086 0.0004 50 11 0.11 2.83086 0.00037 50 11 0.11 2.83086 0.00037
100 23 0.23 5.66171 0.00077 100 30 0.3 5.66171 0.001 100 23 0.23 5.66171 0.00077 100 25 0.25 5.66171 0.00083 100 20 0.2 5.66171 0.00067 100 20 0.2 5.66171 0.00067
150 38 0.38 8.49257 0.00127 150 38 0.38 8.49257 0.00127 150 39 0.39 8.49257 0.0013 150 35 0.35 8.49257 0.00117 150 38 0.38 8.49257 0.00127 150 38 0.38 8.49257 0.00127
200 55 0.55 11.3234 0.00183 200 42 0.42 11.3234 0.0014 200 52 0.52 11.3234 0.00173 200 55 0.55 11.3234 0.00183 200 55 0.55 11.3234 0.00183 200 55 0.55 11.3234 0.00183
250 86 0.86 14.1543 0.00287 244 75 0.75 13.8146 0.0025 250 67 0.67 14.1543 0.00223 250 73 0.73 14.1543 0.00243 250 70 0.7 14.1543 0.00233 250 70 0.7 14.1543 0.00233
280 94 0.94 15.8528 0.00313 - - - 300 85 0.85 16.9851 0.00283 300 88 0.88 16.9851 0.00293 270 95 0.95 15.2866 0.00317 300 83 0.83 16.9851 0.00277 - - - 324 105 1.05 18.3439 0.0035 348 111 1.11 19.7028 0.0037 - - - 344 106 1.06 19.4763 0.00353 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0
50 10 0.1 2.83086 0.00033 50 9 0.09 2.83086 0.0003 50 9 0.09 2.83086 0.0003 50 10 0.1 2.83086 0.00033 50 11 0.11 2.83086 0.00037 50 10 0.1 2.83086 0.00033
100 18 0.18 5.66171 0.0006 100 18 0.18 5.66171 0.0006 100 25 0.25 5.66171 0.00083 100 20 0.2 5.66171 0.00067 100 26 0.26 5.66171 0.00087 100 23 0.23 5.66171 0.00077
150 75 0.75 8.49257 0.0025 150 68 0.68 8.49257 0.00227 150 66 0.66 8.49257 0.0022 150 58 0.58 8.49257 0.00193 148 60 0.6 8.37933 0.002 150 65 0.65 8.49257 0.00217
198 100 1 11.2102 0.00333 176 84 0.84 9.96461 0.0028 186 98 0.98 10.5308 0.00327 200 90 0.9 11.3234 0.003 - - - 200 92 0.92 11.3234 0.00307
- - - 206 105 1.05 11.6631 0.0035 - - - 224 115 1.15 12.6822 0.00383
0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0
50 21 0.21 2.83086 0.0007 50 18 0.18 2.83086 0.0006 50 15 0.15 2.83086 0.0005 50 26 0.26 2.83086 0.00087 50 20 0.2 2.83086 0.00067 50 25 0.25 2.83086 0.00083
100 75 0.75 5.66171 0.0025 100 77 0.77 5.66171 0.00257 100 68 0.68 5.66171 0.00227 100 80 0.8 5.66171 0.00267 100 95 0.95 5.66171 0.00317 100 90 0.9 5.66171 0.003
136 146 1.46 7.69993 0.00487 148 165 1.65 8.37933 0.0055 150 150 1.5 8.49257 0.005 114 121 1.21 6.45435 0.00403 - - - 128 150 1.5 7.24699 0.005
- - - 166 182 1.82 9.39844 0.00607 - - -
-0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0
50 88 0.88 2.83086 0.00293 50 85 0.85 2.83086 0.00283 50 90 0.9 2.83086 0.003 50 84 0.84 2.83086 0.0028 50 89 0.89 2.83086 0.00297 50 58 0.58 2.83086 0.00193
100 167 1.67 5.66171 0.00557 96 220 2.2 5.43524 0.00733 84 245 2.45 4.75584 0.00817 100 166 1.66 5.66171 0.00553 100 154 1.54 5.66171 0.00513 68 122 1.22 3.84996 0.00407
128 211 2.11 7.24699 0.00703 - - - 122 201 2.01 6.90729 0.0067 118 198 1.98 6.68082 0.0066 - - - -
-40
60
80
Sampel 1 Sampel 2 Sampel 5 Sampel 6
Substitusi
0
20
GRAFIK HUBUNGAN TEGANGAN-REGANGAN
0 0.001 0.002 0.003 0.004
σ
0 0.001 0.002 0.003 0.004 0.005
σ
0 0.001 0.002 0.003 0.004
σ
0 0.001 0.002 0.003 0.004
σ
0 0.001 0.002 0.003 0.004 0.005
σ
0 0.001 0.002 0.003 0.004
-
Substitusi 20%
0 0.001 0.002 0.003 0.004
σ
0 0.001 0.002 0.003 0.004
σ
0 0.001 0.002 0.003 0.004
σ
0 0.001 0.002 0.003 0.004
σ
0 0.001 0.002 0.003 0.004
σ
0 0.001 0.002 0.003 0.004
-
Substitusi 40%
0 0.001 0.002 0.003
σ
0 0.001 0.002 0.003 0.004
σ
0 0.001 0.002 0.003 0.004
σ
0 0.001 0.002 0.003 0.004
σ
0 0.0005 0.001 0.0015 0.002
σ
0 0.001 0.002 0.003 0.004 0.005
-
Substitusi 60%
0 0.002 0.004 0.006
σ
0 0.002 0.004 0.006
σ
0 0.002 0.004 0.006 0.008
σ
0 0.002 0.004 0.006
σ
0 0.001 0.002 0.003 0.004
σ
0 0.002 0.004 0.006
-
Substitusi 80%
0 0.002 0.004 0.006 0.008
σ
0 0.002 0.004 0.006 0.008
σ
0 0.002 0.004 0.006 0.008 0.01
σ
0 0.002 0.004 0.006 0.008
σ
0 0.002 0.004 0.006
σ
0 0.002 0.004 0.006