PEMBUATAN KOMPOSIT BIODEGRADABEL DARI
α
-SELULOSA
AMPAS TEBU Bz 132 (Saccharum officinarum) DAN POLIPROPILENA
DENGAN MENGGUNAKAN POLIPROPILENA TERGRAFTING
MALEAT ANHIDRIDA DAN DIVINIL BENZENA
SEBAGAI AGEN PENGIKAT SILANG
TESIS
Oleh
Tengku Rachmi Hidayani
107006002/KIM
FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
UNIVERSITAS SUMATERA UTARA
PEMBUATAN KOMPOSIT BIODEGRADABEL DARI
α
-SELULOSA
AMPAS TEBU Bz 132 (Saccharum officinarum) DAN POLIPROPILENA
DENGAN MENGGUNAKAN POLIPROPILENA TERGRAFTING
MALEAT ANHIDRIDA DAN DIVINIL BENZENA
SEBAGAI AGEN PENGIKAT SILANG
TESIS
Diajukan Sebagai Salah Satu Syarat Untuk Memperoleh Gelar Magister Sains Dalam Program Studi Ilmu Kimia Pada Fakultas Matematika Dan Ilmu
Pengetahuan Alam Universitas Sumatera Utara
Oleh
Tengku Rachmi Hidayani
107006002/KIM
FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
UNIVERSITAS SUMATERA UTARA
Judul Tesis :
PEMBUATAN KOMPOSIT BIODEGRADABEL
DARI
α
-SELULOSA AMPAS TEBU Bz 132
(
Saccharum officinarum
) DAN POLIPROPILENA
DENGAN MENGGUNAKAN POLIPROPILENA
TERGRAFTING MALEAT ANHIDRIDA DAN
DIVINIL BENZENA SEBAGAI AGEN
PENGIKAT SILANG
Nama Mahasiswa : Tengku Rachmi Hidayani Nomor Pokok : 107006002
Program Studi : Magister Ilmu Kimia
Menyetujui Komisi Pembimbing
(Dr. Darwin Yunus Nasution, MS) (Dr.Yugia Muis, MS) Ketua Anggota
Ketua Program Studi Dekan
(Prof. Basuki Wirjosentono, MS, Ph.D) (Dr. Sutarman, MSc)
PERNYATAAN ORISINALITAS
PEMBUATAN KOMPOSIT BIODEGRADABEL DARI
α
-SELULOSA
AMPAS TEBU Bz 132 (Saccharum officinarum) DAN POLIPROPILENA
DENGAN MENGGUNAKAN POLIPROPILENA TERGRAFTING
MALEAT ANHIDRIDA DAN DIVINIL BENZENA
SEBAGAI AGEN PENGIKAT SILANG
TESIS
Dengan ini saya menyatakan bahwa saya mengakui semua karya Tesis ini adalah hasil kerja saya sendiri kecuali kutipan dan ringkasan yang tiap satunya telah dijelaskan sumbernya dengan benar.
Medan, 4 Mei 2012
PERNYATAAN PERSETUJUAN PUBLIKASI KARYA ILMIAH
UNTUK KEPENTINGAN AKADEMIS
Sebagai Sivitas Akademika Universitas Sumatera Utara, saya yang bertanda tangan di bawah ini:
Nama : Tengku Rachmi Hidayani Nomor Pokok : 107006002
Program Studi : Magister Ilmu Kimia Jenis Karya Ilmiah : Tesis
Demi pengembangan ilmu pengetahuan, menyetujui untuk memberikan kepada Universitas Sumatera Utara Hak Bebas Royalti Non-Eksklusif (Non-Exclusif Royalty
Free Right) atas Tesis saya yang berjudul:
PEMBUATAN KOMPOSIT BIODEGRADABEL DARI
α
-SELULOSA
AMPAS TEBU Bz 132 (Saccharum officinarum) DAN POLIPROPILENA
DENGAN MENGGUNAKAN POLIPROPILENA TERGRAFTING
MALEAT ANHIDRIDA DAN DIVINIL BENZENA
SEBAGAI AGEN PENGIKAT SILANG
beserta perangkat yang ada (jika diperlukan). Dengan Hak Bebas Royalti Non-Eksklusif ini, Universitas Sumatera Utara berhak menyimpan, mengalih media, memformat, mengelola dalam bentuk data-base, merawat dan mempublikasikan Tesis saya tanpa meminta izin dari saya selama tetap mencantumkan nama saya sebagai penulis dan sebagai pemegang dan atau sebagai pemilik hak cipta.
Demikian pernyataan ini dibuat dengan sebenarnya.
Medan, 4 Mei 2012
Telah diuji pada
Tanggal : 4 Mei 2012
PANITIA PENGUJI TESIS
KETUA : Dr. Darwin Yunus Nasution, MS
Anggota : 1. Dr. Yugia Muis, MS
2. Prof. Basuki Wirjosentono, MS, Ph.D
3. Dr. Hamonangan Nainggolan, MSc
RIWAYAT HIDUP
Penulis lahir di Medan,Sumatera Utara pada tanggal 15 Maret 1988, anak
pertama dan terakhir dari Bapak H.T.Syahril SH dan Ibu Hj.Dra.Nurtizar,Apt.
Penulis menimba ilmu di TK Perwanis Medan pada tahun 1992-1994.
Melanjutkan pendidikan di SD Percobaan negeri Medan pada Tahun 1994-2000,
SLTP Negeri I Medan pada tahun 2000-2003, dan di SMA Negeri I Medan pada
tahun 2003-2006. Kemudian melanjutkan jenjang perkuliahan dengan menjadi
mahasiswa Departemen Kimia Fakultas Matematika Universitas Sumater Utara pada
tahun 2006-2010. Lalu melanjutkan kembali pendidikan pada program Magister Ilmu
KATA PENGANTAR
Puji syukur atas limpahan rezeki dan Rahmat dari Allah SWT. Salawat dan
salam untuk Rasulullah Muhammad SAW karena jika bukan karena-Nya,saya tidak
akan mampu mengerjakan penelitian serta tesis ini dengan baik.
Tesis berjudul “PEMBUATAN KOMPOSIT BIODEGRADABEL DARI α
-SELULOSA AMPAS TEBU Bz 132 (Saccharum officinarum) DAN POLIPROPILENA DENGAN MENGGUNAKAN POLIPROPILENA
TERGRAFTING MALEAT ANHIDRIDA DAN DIVINIL BENZENA SEBAGAI AGEN PENGIKAT SILANG” ini dibuat sebagai salah satu syarat mendapatkan gelar Magister Sains pada bidang ilmu Kimia Fakultas Matematika Dan Ilmu Pengetahuan
Alam Universitas Sumatera Utara. Pada kesempatan ini penulis ingin memberikan
penghargaan yang setinggi-tingginya serta mengucapkan terima kasih yang tidak
terhingga kepada berbagai pihak yang terlibat secara langsung maupun tidak
langsung dan telah memberikan dukungan baik moril maupun materil. Dengan segala
kerendahan hati dan rasa hormat yang mendalam penulis ingin menyampaikan terima
kasih yang tulus kepada:
Orang tua tercinta, Ayahanda H.T.Syahril SH dan Ibunda Hj.Dra.Nurtizar,Apt
yang selalu memberikan limpahan kasih sayang,ketulusan dan keikhlasan dalam
mendidik dan membesarkan penulis. Memberikan semangat terbesar yang tidak ada
henti-hentinya kepada penulis. Semoga mama dan papa selalu dalam lindungan Allah
SWT.
Bapak Prof. Dr. dr. Syahril Pasaribu, DMTH, MSc, CTM SpA (K) dan Dr.
Sutarman, MSc selaku Rektor Universitas Sumatera Utara dan Dekan Fakultas
Matematika dan Ilmu Pengetahuan Alam Universitas Sumatera Utara.
Bapak Dr.Darwin Yunus Nst, MS selaku dosen pembimbing I dan Ibu
meluangkan waktu,tenaga dan pikirannya serta memberikan masukan, saran, dan
petunjuk kepada penulis dalam melakukan penelitian dan penyusunan tesis ini.
Bapak Prof. Basuki Wirjosentono, MS, Ph.D dan Dr. Hamonangan
Nainggolan, MSc selaku ketua program studi dan sekretaris Pascasarjana Ilmu Kimia.
Bapak/Ibu dosen Pascasarjana Ilmu Kimia yang telah membimbing dan
memotivasi serta memberi disiplin ilmu selama penulis menjalani studi.
Seluruh staf laboratorium Kimia Polimer dan Laboratorium Ilmu Dasar
FMIPA USU, kak Ayu, serta seluruh adik-adik assisten kimia fisika dan kimia
polimer, terima kasih atas bantuannya dalam penelitian.
Kak Leli selaku tata usaha Pascasarjana Ilmu Kimia dan bang Edi teknisi
Laboratorium Kimia Polimer FMIPA-USU. Kakak tempat berbagi suka dan duka
selama di Program Magister. Teman-teman Pascasarjana Ilmu Kimia USU Stambuk
2010 semester ganjil (kak Mawar, kak Efi, Kak Sari, Kak Angel, Bang Mulia, Bang
Irwan, Bang Ridwan) dan juga stambuk 2010 semester genap.
Sahabat terbaik yang pernah penulis miliki, Rizki FitriYani,Reni Silvia
Nasution,Widia Susanti. Sahabat lama yang tak pernah tergantikan : Uli, Kiki, Lia,
Diah, Putri, Nanda, Ramadhani, Leila. Teman berbagi cerita dan melepas lelah : adik
Dwi Ramadhani dan Wendy Syahfitri. Seluruh keluarga besar (sepupu,ponakan,om
dan tante) yang selalu mendoakan yang terbaik kepada penulis. Seluruh teman-teman
baik dari dunia maya,maupun dunia nyata yang tidak dapat disebutkan satu persatu.
Semangat dari kalian semua sangat berharga.
Hanya Allah yang dapat membalas segala kebaikan,ketulusan dan keikhlasan
yang telah kalian berikan kepada penulis. Penulis berharap limpahan Rahmat Allah
selalu mengalir untuk kita semua. Terima kasih.
Penulis menyadari bahwa tesis ini tidak terlepas dari kekurangan. Oleh karena
itu penulis mengharapkan kritik dan saran yang dapat membangun dan
Akhirnya penulis berharap tesis ini memberikan manfaat bagi setiap pembaca
maupun kemajuan penelitian dan ilmu pengetahuan yang akan datang.
Medan, Mei 2012 Hormat Penulis
PEMBUATAN KOMPOSIT BIODEGRADABEL DARI α-SELULOSA AMPAS TEBU Bz 132 (Saccharum officinarum) DAN POLIPROPILENA DENGAN
MENGGUNAKAN POLIPROPILENA TERGRAFTING MALEAT ANHIDRIDA DAN DIVINIL BENZENA SEBAGAI
AGEN PENGIKAT SILANG
ABSTRAK
Telah dilakukan penelitian tentang penggunaan polipropilena tergrafting maleat anhidrida dan divinil benzene sebagai agen pengikat silang dalam pembuatan komposit biodegradabel dari α-selulosa yang bersumber dari ampas tebu dan polipropilena. Penelitian ini terdiri dari tiga tahapan. Tahap pertama yaitu pembuatan PP-g-MA dari polipropilena murni. Tahap kedua yaitu pemisahan α-selulosa dari ampas tebu yang dilakukan dengan metode Okhamafe. Tahapan yang terakhir adalah pencampuran antara polipropilena dan α-selulosa dari ampas tebu dengan agen pengikat silang dengan berbagai variasi massa. Proses pembuatan PP-g-MA dilakukan dengan mendegradasi polipropilena terlebih dahulu dengan BPO dalam internal mixer dengan perbandingan 90:10 (%berat/berat). Kemudian digrafting dengan maleat anhidrida dengan perbandingan PPd:MA:BPO 92:6:2 (%berat/berat). Hasil PP-g-Ma yang diperoleh dimurnikan dengan cara direfluks dengan pelarut xilena. Proses pemisahan α-selulosa dilakukan dengan metode Okhamafe yaitu dilakukan dengan perendaman dalam asam HNO 3,5%, pemutihan dengan Natrium Hipoklorit 1,75% dan pemurnian dengan NaOH 17,5%. Proses pencampuran α -selulosa dengan polipropilena dan agen pengikat silangnya dilakukan dengan metode kempa tekan pada suhu 160oC. Variasi komposisi dan massa dalam pembentukan komposit biodegradabel adalah PP:α-Selulosa (95:5), PP:α-Selulosa:PP-g-MA (95:5:1), PP:α-Selulosa:PP-g-MA:BPO (95:5:1:1), PP:α -Selulosa:PP-g-MA:BPO:DVB (95:5:1:1:1), PP:α-Selulosa:PP-g-MA:BPO:DVB (95:5:0,5:0,5:1), dan PP:α-Selulosa:BPO:DVB (95:5:1:1). Karakterisasi hasil komposit yang diperoleh dianalisa gugus fungsi dengan uji FTIR, analisa sifat morfologi dengan uji SEM, analisa sifat thermal dengan uji DTA, analisa sifat mekanis dengan uji tarik, analisa ketahanan terhadap air dengan uji daya serap air dan analisa kemampuannya terurai di alam dengan uji biodegradabel. Hasil penelitian menunjukan bahwa komposit biodegradabel yang memiliki sifat terbaik dan sesuai dengan SNI 7188.7:2011 adalah dengan perbandingan PP: α-Selulosa:PP-g-MA:BPO:DVB (95:5:0,5:0,5:1) dengan nilai tegangan hasil uji tarik yaitu 50,031N/m2, daya serap air yang rendah yaitu 0,791%, hasil foto permukaan yang rata dan interaksi gugus yang kuat serta memiliki sifat biodegradabel yang baik.
ABSTRACT
PREPARATION OF COMPOSITE BIODEGRADABLE FROM BAGGASE α -CELLULOSE Bz 132 (Saccharum officinarum) AND POLYPROPYLENE
USING POLYPROPYLENE GRAFTED MALEIC ANHYDRADE AND DIVINIL BENZENE AS CROSSLINKING AGENTS
Research about use of polypropylene grafted maleic anhydride and divinyl benzene as a crosslinking agent in the manufacture of composite biodegradable and
α-cellulose from bagasse and polypropylene. The study consisted of three stages. The
first stage of the manufacture of PP-g-MA of pure polypropylene. The second stage of
the separation of α-cellulose from bagasse is performed by the Okhamafe methode.
The last stage of the mixing between the polypropylene and α-cellulose from bagasse by crosslinking with various binding agents of mass variation. The process of making PP-g-MA polypropylene degrades done by BPO in advance in an internal mixer with a ratio of 90:10 (% w / w). Then PPd grafted with maleic anhydride in the ratio PPd : MA: BPO 92:6:2 (% w / w). The results of PP-g-ma obtained was purified by
solvent refluxed with xylene. α-cellulose separation process performed by the
Okhamafe methode that is done by immersion in 3.5% HNO3 acid, bleaching with
sodium hypochlorite 1.75% and 17.5%, purification with NaOH. Α-mixing process
with polypropylene and cellulose binding agents is done by cross-clamp method at a
temperature of 1500C press. Variations in composition and mass of the formation of
polymer composites is a PP: α-Cellulose (95:5), PP: α-Cellulose: PP-g-MA (95:5:1),
PP:α-Cellulose:PP-g-MA:BPO (95:5:1:1), PP:α-Cellulose:PP-g-MA: BPO:DVB
(95:5:1:1:1), PP:α-Cellulose:PP-g-MA:BPO:DVB (95:5:0,5:0,5:1), PP:α -Cellulose:BPO:DVB (95:5:1:1).
Characterization of the composites obtained were analyzed with a functional group FTIR testing, analysis of morphology by SEM, analysis of thermal properties by DTA test, analysis of mechanical properties with tensile stress test, analysis of resistance to water with a water absorption test and analysis of its ability to decompose in
nature to the test biodegradable.
The results showed that the polymer composite that has the best properties and in
accordance with ISO 7188.7:2011 is the ratio of PP: α-Cellulose: PP-g-MA: BPO:
DVB (95:5:0,5:0,5:1) with the test results of tensile stress is 50.031 N/m2, low water absorption, namely 0.791%, the images on a flat surface and a strong group
interactions as well as having good biodegradable properties.
DAFTAR ISI
2.1.2 Komposit biodegradabel dengan bahan dasar selulosa 8
2.2 Kemasan 9
2.2.1 Fungsi kemasan 10
2.2.2 Kemasan Biodegradabel 10
2.3 Tebu 12
2.3.1 Botani Tebu (Saccharum Officinarum) 12
2.4 Selulosa 14
2.4.1 Sifat-Sifat Selulosa 14 2.4.2 Pembagian Selulosa 16
2.4.3 α-Selulosa 16
2.4.4 Selulosa dari serat alam 17 2.4.5 Metode Pemisahan Selulosa 18
2.5 Polipropilena 19
2.5.1 Struktur Polipropilena 20 2.5.2 Pembentukan Radikal Bebas Pada Bahan Polimer 21 2.5.2.1 Radikal Bebas pada Polimerisasi 21
2.6 Degradasi dengan Inisiator Peroksida 23
2.7 Proses Grafting 23
2.8 Karakterisasi Komposit Biodegradabel 24
2.8.1 Analisa Sifat Thermal Komposit Biodegradabel 25 2.8.2 Spektofotometer FT-IR 27 2.8.3 Analisa Sifat Permukaan dengan Pengujian SEM 28 2.8.4 Analisa Sifat Mekanik dengan uji kekuatan tarik dan kemulura 29 2.8.5 Analisa Ketahanannya Terhadap Air dengan Uji serapan air 29 2.8.6 Analisa Kemampuan Terurai dialam dengan uji biodegradabel 30
Reaksi Penelitian 34
3.2.1 Proses Degradasi Polipropilena dengan Benzoil Peroksida 38 3.2.2 Proses Grafting MA kedalam PP Terdegradasi 38 3.2.3 Pemurnian PP-g-MA 39 3.2.4 Preparasi Pembentukan Serbuk Polipropilena 39 3.2.5 Preparasi Serbuk Ampas Tebu 39 3.2.6 Ekstraksi α-Selulosa Dari Serbuk Ampas Tebu 39 3.2.7 Pembentukan komposit biodegradabel PP Murni dan 40
α-Selulosa
3.2.8 Pembentukan Komposit biodegradabel PP Murni, α-Selulosa 40 Dan PP-g-MA
3.2.9 Pembentukan Komposit biodegradabel PP Murni, α-Selulosa, 41 PP-g-MA dan BPO
3.2.10 Pembentukan Komposit biodegradabel PP Murni, α-Selulosa, 41 BPO dan DVB
3.2.11 Pembentukan Komposit biodegradabel PP Murni, α-Selulosa, 41 PP-g-MA, BPO dan DVB
3.2.12 Karakterisasi Komposit Biodegradabel 42 3.2.12.1 Analisa Gugus Fungsi Dengan FTIR 42 3.2.12.2 Analisa Sifat Thermal dengan Uji DTA 42 3.2.12.3 Analisa Sifat Mekanik dengan Uji Tarik 42 3.2.12.4 Analisa Sifat Morfologi dengan uji SEM 43 3.2.12.5 Analisa Sifat Ketahanan Terhadap Air dengan 43 Uji Serap Air
3.2.12.6 Analisa Kemampuan Terurai di Alam dengan 44 Uji Biodegradabel
3.3 Bagan Penelitian 44
3.3.1 Proses Degradasi Polipropilena dengan Benzoil Peroksida 44 3.3.2 Proses Grafting MA kedalam PP Terdegradasi 45 3.3.3 Pemurnian PP-g-MA 46 3.3.4 Preparasi Pembentukan Serbuk Polipropilena 47 3.3.5 Preparasi Serbuk Ampas Tebu 47 3.3.6 Ekstraksi α-Selulosa Dari Serbuk Ampas Tebu 48 3.3.7 Pembentukan komposit biodegradabel PP Murni dan 49
α-Selulosa
3.3.8 Pembentukan Komposit biodegradabel PP Murni, α-Selulosa 49 dan PP-g-MA
3.3.9 Pembentukan Komposit biodegradabel PP Murni, α-Selulosa, 50 PP-g-MA dan BPO
3.3.10 Pembentukan Komposit biodegradabel PP Murni, α-Selulosa, 50 BPO dan DVB
3.3.11 Pembentukan Komposit biodegradabel PP Murni, α-Selulosa, 51 PP-g-MA, BPO dan DVB
3.3.12 Uji Serap Air 51
3.3.13 Uji Biodegradabel 52
BAB 4 HASIL DAN PEMBAHASAN 53
4.1 Karakterisasi Berdasarkan Analisa Sifat Mekanik dengan Uji Traik 53
4.2 Analisa Sifat Thermal dengan Uji DTA 55
4.5 Analisa Gugus Fungsi dengan Uji FTIR 61
4.5.1 Komposit biodegradabel PP:α-Selulosa:PP-g-MA (95:5:1) 64 4.5.2 Komposit biodegradabel PP:α-Selulosa:BPO:DVB (95:5:1:1) 64 4.5.3 Komposit biodegradabel PP:α-Selulosa:PP-g-MA:BPO:DVB 64 (95:5:0,5:0,5:1)
4.6 Analisa Kemampuan Terurai di Alam dengan Uji Biodegradasi 65
BAB 5 KESIMPULAN DAN SARAN 71
5.1 Kesimpulan 71
5.2 Saran 72
DAFTAR PUSTAKA 73
DAFTAR TABEL
Nomor Judul Halaman
2.1 Persyaratan Kemasan Biodegradabel menurut SNI 7188.7:2011 11
2.2 Komposisi Kimia Ampas Tebu 13
3.1 Perbandingan Pembentukan Komposit Biodegradabel PP murni, 42 α-selulosa, PP-g-MA, BPO dan DVB
4.1 Hasil Perhitungan Kekuatan Tarik dan kemuluran Komposit 53 Biodegradabel
4.2 Hasil Uji DTA Polipropilena Murni dan Komposit Biodegradabel 56
4.3 Data Hasil Uji Serapan Air 61
4.4 Bilangan Gelombang Polipropilena Murni 62
4.5 Bilangan Gelombang PP: α-selulosa:PP-g-MA (95:5:1) 62
4.6 Bilangan Gelombang PP: α-selulosa:BPO:DVB (95:5:1:1) 63
4.7 Bilangan Gelombang PP: α-selulosa: 63 PP-g-MA:BPO:DVB (95:5:0,5:0,5:1)
4.8 Data Hasil Penurunan Massa (%) Spesimen Komposit Biodegradebel 65 setelah Penguburan dalam Tanah
4.9 Bilangan Gelombang PP: α-selulosa:PP-g-MA (95:5:1) 66 setelah Penguburan
4.10 Bilangan Gelombang PP: α-selulosa:BPO:DVB (95:5:1:1) 67 setelah Penguburan
DAFTAR GAMBAR
Nomor Judul Halaman
2.1 Rumus Bangun Selulosa 15
2.2 Struktur Polipropilena 19
2.3 Polipropilena Isotatik, Sindiotaktik, Ataktik 21
2.4 Grafik (b) hasil dari set up yang diperlihatkan pada gambar 27 (a), Grafik (d) merupakan jejak DTA yang umum yang merupakan
dari pengaturan yang diperlihatkan pada Gambar (c)
2.5 Reaksi Penelitian 36
3.1 Spesimen Uji Kekuatan Tarik Berdasarkan ASTM D-638-72 TypeIV 42
3.2 Proses Degradasi Polipropilena dengan Benzoil Peroksida 44
3.3 Proses Grafting Maleat Anhidrida kedalam Polipropilena Terdegradasi 45
3.4 Pemurnian Polipropilena Tergrafting Maleat Anhidrida 46
3.5 Preparasi Pembentukan Serbuk Polipropilena 47
3.6 Preparasi Serbuk Ampas Tebu 47
3.7 Ekstraksi α-Selulosa Dari Serbuk Ampas Tebu 48
3.8 Pembentukan Komposit biodegradabel Polipropilena Murni 49 dan α-Selulosa
3.9 Pembentukan Komposit biodegradabel Polipropilena Murni, 49 α-Selulosa, dan PP-g-MA
3.10 Pembentukan Komposit biodegradabel PP murni, α-Selulosa, 50 PP-g-MA, dan BPO
3.11 Pembentukan Komposit biodegradabel PP murni, 50 α-Selulosa, BPO, dan DVB
3.12 Pembentukan Komposit biodegradabel PP murni, PP-g-MA, BPO, 51 DVB, dan α-Selulosa
3.14 Uji Biodegradabel 52
4.1 Grafik Kekuatan Tarik (N/m2) dari Komposit Biodegradabel 54
4.2 Grafik Kemuluran (%) Dari Komposit Biodegradabel 54
4.3 Hasil Uji SEM dari Polipropilen Murni Pembesaran 1000 kali 57
4.4 Hasil Uji PP:α-Selulosa:PP-g-MA (95:5:1) Pembesaran 1000 kali 58
4.5 Hasil Uji Komposit biodegradabel PP:α-Selulosa: BPO:DVB (95:5:1:1) 59 Pembesaran 1000 kali
4.6 Hasil Uji Komposit biodegradabel PP:α-Selulosa: 60 PP-g-MA:BPO:DVB (95:5:0,5:0,5:1) Pembesaran 1000 kali
4.7 Mekanisme Reaksi Penguraian di Alam 69
4.8 Permukaan Komposit biodegradabel PP:α-Selulosa:PP-g-MA (95:5:1) 69
4.9 Permukaan Komposit biodegradabel PP:α-selulosa:BPO:DVB (95:5:1:1) 70
DAFTAR LAMPIRAN
Nomor Judul Halaman
1 Rumus perhitungan kekuatan tarik dan kemuluran 81 2 Cara membaca data termogram uji DTA 81 3 Gambar Grafik Hasil Uji Tarik 82 4 Gambar Kromatogram Hasil Uji DTA Untuk Polipropilena murni 83 5 Gambar Kromatogram Hasil Uji DTA Untuk 84
PP:α-Selulosa: PP-g-MA (95:5:1)
6 Gambar Kromatogram Hasil Uji DTA Untuk
PP:α-Selulosa:PP-g-MA:BPO:DVB (95:5:0,5:0,5:1) 85 7 Gambar Kromatogram Hasil Uji DTA Untuk
PP:α-Selulosa:BPO:DVB (95:5:1:1) 86 8 Gambar Hasil Spektrum FTIR Polipropilena Murni 87 9 Gambar Hasil Spektrum FTIR Untuk 87 α-Selulosa:PP-g-MA (95:5:1) setelah ditanam pada tanah sampah
selama 1 bulan
13 Gambar Hasil Spektrum FTIR Untuk PP:α-Selulosa: 89 BPO:DVB (95:5:1:1) setelah ditanam pada tanah sampah selama
1 bulan
14 Gambar Hasil Spektrum FTIR Untuk 90 PP:α-Selulosa:PP-g-M:BPO:DVB (95:5:0,5:0,5:1) setelah ditanam pada tanah sampah selama 1 bulan
15 Gambar Spesimen Hasil Uji Tarik 90 16 Gambar Wadah Penguburan Spesimen 92 17 Gambar Bahan Baku Pembuatan Komposit Biodegradabel 93 18 Tabel Perbandingan Karakterisasi Dari Komposit Biodegradabel 95
DAFTAR SINGKATAN
PP = Polipropilena
PPd = Polipropilena terdegradasi MA = Maleat Anhidrida
PP-g-MA = Polipropilena tergrafting maleat anhidrida FTIR = Fourier Transform Infrared Spectroscopy SEM = Spectra Electro magnetic
BPO = Benzoil Peroksida DVB = Divinilbenzena