STUDI KARAKTERISTIK MARSHALL CAMPURAN LATASIR B MENGGUNAKAN ABU CANGKANG KELAPA SAWIT SEBAGAI FILLER

(1)

STUDI KARAKTERISTIK MARSHALL CAMPURAN LATASIR B MENGGUNAKAN ABU CANGKANG

KELAPA SAWIT SEBAGAI FILLER

HALAMAN JUDUL

SKRIPSI

Diajukan Kepada Universitas Muhammadiyah Malang Untuk Memenuhi Salah Satu Persyaratan Akademik

Dalam Menyelesaikan Program Sarjana Teknik

Disusun Oleh :

MUHAMMAD EDY WIRAWAN

201710340311033

JURUSAN TEKNIK SIPIL FAKULTAS TEKNIK

UNIVERSITAS MUHAMMADIYAH MALANG

2022

(2)

ii

LEMBAR PENGESAHAN

JUDUL : STUDI KARAKTERISTIK MARSHALL CAMPURAN LATASIR B MENGGUNAKAN ABU CANGKANG KELAPA SAWIT SEBAGAI FILLER

NAMA : MUHAMMAD EDY WIRAWAN

NIM : 201710340311033

Pada hari Jum’at 8 April 2022, tugas akhir ini telah diuji oleh tim penguji :

1. Dr. Abdul Samad, ST., MT. Dosen Penguji I ………

2. Lintang Satiti Mahabella, ST., MT. Dosen Penguji II ………

Menyetujui :

Dosen Pembimbing I Dosen Pembimbing II

Ir. Khoirul Abadi, MT., Ir. Andi Syaiful Amal, MT.,

Mengetahui :

Ketua Jurusan Teknik Sipil

Dr. Ir. Sulianto, MT.,

(3)

iii

SURAT PERNYATAAN

Yang bertanda tangan di bawah ini:

Nama : Muhammad Edy Wirawan NIM : 201710340311033

Jurusan : Teknik Sipil Fakultas : Teknik

UNIVERSITAS MUHAMMADIYAH MALANG

Dengan ini menyatakan dengan sebenar – benarnya bahwa Tugas Akhir dengan judul “Studi Karakteristik Marshall Campuran Latasir B Menggunakan Abu Cangkang Kelapa Sawit Sebagai Filler” adalah hasil karya saya dan bukan karya tulis orang lain. Dalam naskah Tugas Akhir ini tidak terdapat karya ilmiah yang pernah diajukan oleh orang lain untuk memperoleh gelar akademik di suatu Perguruan Tinggi, dan tidak terdapat karya atau pendapat yang pernah ditulis atau diterbitkan oleh orang lain, baik sebagian maupun seluruhnya, kecuali yang secara tertulis dikutip dalam naskah ini dan di disebutkan dalam sumber kutipan atau daftar pustaka.

Demikian pernyataan ini saya buat dengan sebenarnya dan apabila penyataan ini tidak benar saya bersedia mendapat sangsi akademis.

Malang, 16 Mei 2022

Yang Menyatakan,

Muhammad Edy Wirawan

(4)

iv

SURAT KETERANGAN LOLOS PLAGIASI

Mahasiswa/i atas nama,

Nama : MUHAMMAD EDY WIRAWAN

NIM :

Telah dinyatakan memenuhi standar maksimum plagiasi dengan hasil,

BAB 1 3 % ≤ 10%

BAB 2 8 % ≤ 25%

BAB 3 17 % ≤ 35%

BAB 4 5 % ≤ 15%

BAB 5 4 % ≤ 5%

Naskah Publikasi 7 % ≤ 20% Malang, 22 April 2022

Amalia Nur Adibah SURAT KETERANGAN LOLOS PLAGIASI

201710340311033

(5)

v

KATA PENGANTAR

Puji syukur penulis panjatkan kehadirat Allah SWT yang telah melimpahkan rahmat dan hidayahnya, sehingga penulis dapat menyelesaikan skripsi yang berjudul “Studi Karakteristik Marshall Campuran Latasir B Menggunakan Abu Cangkang Kelapa Sawit Sebagai Filler”.

Skripsi ini merupakan tugas akhir yang diajukan untuk memenuhi syarat dalam memperoleh gelar Sarjana Teknik (ST) pada Fakultas Teknik Universitas Muhammadiyah Malang.

Penulis menyadari bahwa penulisan skripsi ini tidak akan terwujud tanpa adanya bantuan dan dorongan dari berbagai pihak. Oleh karena itu pada kesempatan ini penulis menyampaikan banyak terima kasih kepada :

1. Ayah dan Ibu, yang sangat saya hormati dan saya sayangi, atas cinta dan dukungan mereka seumur hidup saya.

2. Bapak Dr. Fauzan, M.Pd., selaku Rektor Universitas Muhammadiyah Malang.

3. Bapak Prof. Ilyas Masudin, ST., MLogSCM., PhD., IPM., ASEAN Eng.

selaku Dekan Fakultas Teknik Universitas Muhammadiyah Malang.

4. Bapak Dr. Ir. Sulianto, MT., selaku Ketua Jurusan Teknik Sipil Universitas Muhammadiyah Malang.

5. Ir. Khoirul Abadi, MT., selaku Dosen Pembimbing I yang telah meluangkan waktu untuk membimbing dan mengarahkan penulis dalam menyelesaikan tugas akhir ini.

6. Ir. Andi Syaiful Amal, MT., IPM., ASEAN Eng. selaku Dosen Pembimbing II yang telah meluangkan waktu untuk membimbing dan mengarahkan penulis dalam menyelesaikan tugas akhir ini.

7. Seluruh jajaran Dosen dan Staff Teknik Sipil Universitas Muhammadiyah Malang yang telah memberikan ilmu dan pengetahuan yang luar biasa bermanfaat untuk kita semua.

(6)

vi

8. Perkontenan Duniawi, Ahmad Nurfikri, Diandra Romadhona Putra, Fadillah Ramadhani dan Muhammad Kurnia Rahman yang telah memberikan tenaga dan dukungan dalam menyelesaikan tugas akhir ini.

9. Nadia Rahmah, yang selalu memberikan semangat dan dukungan dalam menyelesaikan tugas akhir ini.

10. Teman-teman seperjuangan Teknik Sipil Angkatan 2017 kelas A yang telah saling menghibur dan berbagi cerita di perantauan selama proses perkuliahan.

Demi kesempurnaan skripsi ini, saran dan kritik yang sifatnya membangun sangat penulis harapkan. Semoga karya skripsi ini bermanfaat dan dapat memberikan sumbangan yang berarti bagi pihak yang membutuhkan.

Malang, 16 Mei 2022

Penulis

(7)

vii

STUDI KARAKTERISTIK MARSHALL CAMPURAN LATASIR B MENGGUNAKAN ABU CANGKANG

KELAPA SAWIT SEBAGAI FILLER

Muhammad Edy Wirawan¹⁾, Khoirul Abadi²⁾, Andi Syaiful Amal³⁾

1,2,3Jurusan Teknik Sipil, Fakultas Teknik, Universitas Muhammadiyah Malang Jl. Tlogomas No.246 Tlp. (0341) 464318-319 Pes. 130 Fax (0341) 460435

email: wan.wira30@gmail.com ABSTRAK

Kebutuhan perkerasan lentur yang semakin meningkat membuat kebutuhan bahan perkerasan lentur semakin besar. Bahan penyusun perkerasan lentur salah satunya yaitu filler yang berfungsi sebagai pengisi rongga pada campuran aspal.

Bahan filler yang umumnya digunakan meliputi portland cement, abu batu, dan kapur, merupakan bahan alam yang tidak dapat diperbaharui. Alternatif lain bahan filler campuran aspal berupa penggunaan limbah abu cangkang kelapa sawit.

Tujuan studi untuk mengetahui karakteristik marshall campuran Latasir B dengan filler abu cangkang kelapa sawit berdasarkan KAO dan mengetahui perbandingan karakteristik marshall campuran menggunakan filler portland cement dengan abu cangkang kelapa sawit. Metode studi yang digunakan yaitu metode eksperimen di laboratorium dengan menggunakan perencanaan campuran metode Bina Marga.

Hasil studi diketahui campuran Latasir B dengan filler abu cangkang kelapa sawit pada KAO 9,98% dengan kadar filler 8,14% nilai karakteristik marshall yaitu, Marshall Stability 2410,00 kg, Marshall Quotient 5,60 Kn/mm, Volume Air Void 5,57% dan Film Thickness 7,39 μm. Perbedaan karakteristik marshall campuran Latasir B menggunakan filler abu cangkang kelapa sawit terhadap campuran Latasir B filler portland cement pada kadar aspal 9,88% yaitu, nilai Marshall Stability lebih besar 12,97%, nilai Marshall quotient lebih besar 7,14%, nilai Volume Air Void lebih besar 46,55%, dan nilai Film Thickness lebih kecil 10,39%.

Kata Kunci : Latasir B, Filler, Abu Cangkang Kelapa Sawit

(8)

viii

STUDY OF CHARACTERISTICS OF MARSHALL LATASIR B MIXED USING SHELL ASH PALM OIL AS A FILLER

Muhammad Edy Wirawan¹⁾, Khoirul Abadi²⁾, Andi Syaiful Amal³⁾

1,2,3Department of Civil Engineering, Faculty of Engineering, University of Muhammadiyah Malang

Jl. Tlogomas No.246 Tlp. (0341) 464318-319 Pes. 130 Fax (0341) 460435 email: wan.wira30@gmail.com

ABSTRACT

The increasing demand for flexible pavement makes the need for flexible pavement materials getting bigger. One of the constituent materials for flexible pavement is filler which functions as a cavity filler in the asphalt mixture. Filler materials that are commonly used include portland cement, rock ash, and lime, which are non- renewable natural materials. Another alternative for asphalt mixture filler material is the use of palm shell ash waste. The purpose of the study was to determine the characteristics of the mixed marshall Latasir B with palm shell ash filler based on KAO and to compare the characteristics of the mixed marshall using portland cement filler with palm shell ash. The study method used is the experimental method in the laboratory using a mixed planning method of Bina Marga. The results of the study found the value of Marshall characteristics that the mixture of Latasir B with palm shell ash filler at KAO 9.98% with a filler content of 8.14%, Marshall Stability 2410.00 kg, Marshall Quotient 5.60 Kn/mm, Volume Air Void 5 .57% and Film Thickness 7.39 m. The difference in the characteristics of the marshall mixture of Latasir B using palm shell ash filler against the Latasir B mixture of portland cement filler at an asphalt content of 9.88%, the value of Marshall Stability is 12.97% greater, the value of Marshall quotient is 7.14% greater, the value of Volume Air Void is 46.55% bigger, and the value of Film Thickness is 10.39%

smaller.

Keywords: Latasir B, Filler, Palm Oil Shell Ash

(9)

ix

DAFTAR ISI

HALAMAN JUDUL ... i

LEMBAR PENGESAHAN ... ii

SURAT PERNYATAAN ... iii

SURAT KETERANGAN LOLOS PLAGIASI ... iv

KATA PENGANTAR ... v

ABSTRAK ... vii

DAFTAR ISI ... ix

DAFTAR TABEL ... xii

DAFTAR GAMBAR ... xiii

BAB I PENDAHULUAN ... 1

1.1 Latar Belakang ... 1

1.2 Identifikasi Masalah ... 3

1.3 Rumusan Masalah ... 3

1.4 Batasan Masalah ... 3

1.5 Tujuan Studi ... 3

1.6 Manfaat Studi ... 3

BAB II LANDASAN TEORI ... 4

2.1 Perkerasan Jalan ... 4

2.2 Konstruksi Perkerasan Jalan ... 5

2.3 Lapis Tipis Aspal Pasir (LATASIR) ... 11

2.4 Bahan Penyusun ... 12

2.4.1 Agregat ... 12

2.4.2 Macam-Macam Agregat... 15

2.4.3 Bahan Pengisi (Filler) ... 16

2.4.4 Berat Jenis Agregat ... 17

2.5 Aspal ... 18

2.6 Abu Cangkang Kelapa Sawit ... 21

2.7 Penentuan Campuran Nominal ... 22

2.8 Perencanaan dan Pembuatan Campuran ... 23

(10)

x

2.9 Pengujian Campuran Dengan Marshall Test ... 24

2.10 Karakteristik Campuran ... 25

BAB III METODE STUDI ... 29

3.1 Tahapan Studi ... 29

3.2 Pemeriksaan Bahan ... 29

3.2.1 Pemeriksaan Agregat Kasar ... 31

3.2.2 Pemeriksaan Agregat Halus ... 31

3.2.3 Pemeriksaan Filler ... 31

3.2.4 Pemeriksaan Aspal ... 32

3.3 Campuran Latasir B dengan Filler PC ... 32

3.3.1 Perencanaan Campuran Latasir B Filler PC ... 32

3.3.2 Pembuatan Campuran Latasir B Filler PC... 33

3.3.3 Pengujian Campuran Latasir B Filler PC ... 33

3.4 Campuran Latasir B dengan Filler ACKS ... 33

3.4.1 Perencanaan Campuran Latasir B Filler ACKS ... 34

3.4.2 Pembuatan Campuran Latasir B Filler ACKS ... 34

3.4.3 Pengujian Campuran Latasir B Filler ACKS ... 34

3.5 Pembahasan ... 35

BAB IV HASIL DAN PEMBAHASAN ... 36

4.1 Bahan ... 36

4.2 Campuran Latasir B Filler PC ... 37

4.2.1 Proporsi Campuran Latasir B Filler PC... 37

4.2.2 Karakteristik Campuran Latasir B Filler PC ... 39

4.2.3 KAO Campuran Latasir B Filler PC ... 41

4.3 Campuran Latasir B Filler ACKS ... 43

4.3.1 Proporsi Campuran Latasir B Filler ACKS ... 43

4.3.2 Karakteristik Campuran Latasir B Filler ACKS ... 44

4.3.3 KAO Campuran Latasir B Filler ACKS ... 46

4.4 Pembahasan ... 48

4.4.1 Karakteristik Benda Uji Campuran dengan Filler PC dan ACKS .. 48

(11)

xi

4.4.2 Perbandingan Karakteristik Marshall Campuran Latasir B Filler PC

& Campuran Latasir B Filler ACKS ... 51 BAB V KESIMPULAN ... 59 DAFTAR PUSTAKA ... 60 LAMPIRAN

(12)

xii

DAFTAR TABEL

Tabel 2.1 Perbedaan Antara Perkerasan Lentur dan Perkerasan Kaku…………...6

Tabel 2.2 Ketentuan sifat–sifat campuran Latasir……… 11

Tabel 2.3 Gradasi Agregat Kasar……….. 15

Tabel 2.4 Persyaratan Agregat Kasar………... 15

Tabel 2.5 Gradasi Agregat Halus………. 16

Tabel 2.6 Persyaratan Agregat Halus………... 16

Tabel 2.7 Persyaratan Filler ……….…17

Tabel 2.8 Ketentuan untuk aspal keras pen 60/70……… 20

Tabel 2.9 Komposisi Campuran………... 23

Tabel 2.10 Angka Korelasi Stabilitas………... 25

Tabel 4.1 Hasil Pemeriksaan Agregat Kasar………... 36

Tabel 4.2 Hasil Pemeriksaan Agregat Halus……… 36

Tabel 4.3 Hasil Pemeriksaan Filler……….. 37

Tabel 4.4 Hasil Pemeriksaan Aspal……….. 37

Tabel 4.5 Ringkasan Sifat-sifat Agregat……….. 37

Tabel 4.6 Penentuan Campuran Nominal……… 38

Tabel 4.7 Proporsi Rancangan Campuran Nominal………. 38

Tabel 4.8 Penyesuaian Proporsi Campuran Nominal………... 38

Tabel 4.9 Hasil Pengukuran Benda Uji Campuran Latasir B Filler PC ………. 39

Tabel 4.10 Hasil Pengujian Marshall Campuran Latasir B Filler PC…………. 40

Tabel 4.11 Karakteristik Marshall Campuran Latasir B Filler PC …….……… 41

Tabel 4.12 Hasil Pengukuran Benda Uji Campuran Latasir B Filler ACKS ….. 44

Tabel 4.13 Hasil Pengujian Marshall Campuran Latasir B Filler ACKS …..… 45

Tabel 4.14 Karakteristik Marshall Campuran Latasir B Filler ACKS ………… 46

Tabel 4.15 Berat Jenis bulk Campuran Latasir B Filler PC & Campuran Latasir B Filler ACKS ……… 49

(13)

xiii

DAFTAR GAMBAR

Gambar 3.1 Diagram Alir……… 30 Gambar 4.1 Penentuan Kadar Aspal Optimum Filler PC………... 42 Gambar 4.2 Penentuan Kadar Aspal Optimum Filler ACKS……….. 47 Gambar 4.3 Grafik BJ. Bulk Campuran Latasir B Filler PC & Campuran

Latasir B Filler ACKS ………….………….………….…………. 50 Gambar 4.4 Grafik Marshall Stability Campuran Latasir B Filler PC &

Campuran Latasir B Filler ACKS ……….. 51 Gambar 4.5 Grafik Marshall Question Campuran Latasir B Filler PC &

Campuran Latasir B Filler ACKS ……….. 52 Gambar 4.6 Grafik Volume Air Void Campuran Latasir B Filler PC & Campuran Latasir B Filler ACKS ……….. 53 Gambar 4.7 Grafik Film Thickness Campuran Latasir B Filler PC & Campuran

Latasir B Filler ACKS ……….….. 54 Gambar 4.8 Tinjauan Kadar Aspal dalam Grafik Superposisi ………... 56 Gambar 4.9 Nilai Marshall Campuran Latasir B Filler PC & Campuran Latasir

B Filler ACKS pada Kadar Aspal 9,88 %………... 57

(14)

60

DAFTAR PUSTAKA

Direktorat Jenderal Bina Marga, 1976, Manual Pemeriksaan Bahan Jalan.

Direktorat Jenderal Bina Marga, 2018. Spesifikasi Umum Bina Marga untuk Pekerjaan Konstruksi Jalan dan Jembatan.

Agusmaniza Roni, Saleh M. Sofyan, Anggraini Renni, 2018. Uji Durabilitas campuran AC-WC Menggunakan Kombinasi Limbah Plastik dan Abu Cangkang Kelapa Sawit. Jurnal Teknik Sipil Universitas Suiah Kuala Vol 1 Special Issue, No.3, Januari 2018, pp.725-736.

Alamsyah,A.A. 2001. Rekayasa Jalan Raya. Malang: UMM Press.

Fauziah M, Febriansyah H, 2013, Pemanfaatan Limbah Cangkang Kelapa Sawit Sebagai Bahan Tambah Untuk Meningkatkan Kekuatan Dan Keawetan Campuran Asphal Concrete Binder Course (AC-BC), Jurnal Teknik Sipil, Universitas Islam Indonesia, Yogyakarta

Hardiyatmo,H.C. 2019. Perencanaan Perkerasan Jalan dan Penyelidikan Tanah.

Yogyakarta: Gajah Mada University Press.

Munawarah Fajri, AR Sulaiman, Fitri Gustina, 2019. Subtitusi Abu Cangkang Kelapa Sawit Sebagai Material Pengisi Pada Campuran AC-WC.

Proceeding Seminar Nasional Politeknik Negri Lhokseumawe, Vol.3 No.1 Oktober 2019.

Nisumanti, Sartika, & Yusuf, Muhammad, 2019. Pengaruh Arang Cangkang Kelapa Sawit Sebagai Pengganti Filler Aspal Penetrasi 60/70. Jurnal Ilmiah Tekno Global Vol 8 No. 2 Desember 2019.

Nuswantoro, Waluyo, Desriantomy, & Edwin, 2003. Penggunaan Abu Cangkang Kelapa Sawit Sebagai Tambahan Filler Pada Campuran Aspal Panas Jenis Hot Rolled Sheet (HRS). Jurnal Rekayasa Rancang Bangun, Vol. 4 No.2 Desember 2003: 75-82.

Puri, Anas., 2016. Pengaruh Penambahan Abu Sawit Sebagai bahan Pengisi Terhadap Karakteristik Marshall Material Beton Aspal. Jurnal Saintis Vol.

9 No. 2, Oktober 2006, pp. 103-112.

(15)

61

Sentosa, L. 2005. Kinerja Laboratorium Campuran Hot Rolled Asphalt dengan Abu Sawit sebagai Filler. Simposium VIII Forum Studi Transportasi Antar- Perguruan Tinggi (FSTPT). Palembang: Universitas Sriwijaya

Sukirman, Silvia, 1999, Perkerasan Lentur Jalan Raya. Bandung: Nova.

Sukirman, Silvia, 2003, Beton Aspal Campuran Panas. Jakarta: Granit.

Suparma, Latif Budi, Panggabean, Tunggul W Mude, Sandra, 2014. Potensi Penggunaan Limbah Kelapa Sawit Sebagai Agregat Pengisi Pada Campuran Hot Rolled Sheet-Base. Jurnal Transportasi Vol. 14 No. 2 Agustus 2014: 87-96.

Suprapto Tm, M,Sc. 2004. Bahan dan Struktur Jalan Raya. Yogyakarta: Teknik Sipil Universitas Gajah Mada.

Tohir Musrufah & Findia, 2020. Analisis Penambahan Abu Cangkang Kelapa Sawit pada Campuran Lapis Aspal Beton (Lataston). Jurnal Riset Pembangunan Vol. 3 No. 1 2020.