PENGARUH PANJANG SERAT TERHADAP SIFAT MEKANIK DAN FISIK KOMPOSIT POLIPROPILENA-POLIPROPILENA

TERGRAFTING MALEAT ANHIDRAT- SERAT DAUN NENAS YANG TELAH

DIALKALISASI

ABSTRAK

Telah dilakukan penelitian untuk mengetahui sifat mekanik dan fisik dari polipropilena, polipropilena tergrafting maleat anhidrat (PP-g-MA) dan serat daun nenas dengan variasi berat polipropilena, PP-g-MA, serta panjang serat. Kekuatan tarik diuji berdasarkan ASTM D-638. Serat nenas telah direndam dalam NaOH 5% selama 1 jam, dan penyusunan serat dilakukan searah dengan panjang spesimen. Variasi berat PP:PP-g-MA:serat nenas yang digunakan 8:1:1, 7:2:1, 6:3:1, 5:4:1, 4:5:1. Hasil kekuatan tarik yang paling tinggi didapatkan dengan perbandingan 8:1:1 yaitu 34,57 Mpa dan nilai kemulurannya 4,15%. Dari hasil uji kerapatan perbandingan 8:1:1 memiliki kerapatan yang paling tinggi dan daya serap air yang paling rendah yaitu 0,95 gr/cm3 dan 1,32% (2jam), 1,33% (24 jam). Pada variasi panjang serat 1, 2, 3, 4, 5 cm perbandingan berat polipropilena, PP-g-MA yang digunakan merupakan hasil kuat tarik maksimum dari variasi berat polipropilena dan PP-g-MA yaitu 8:1:1. Kekuatan tarik yang paling tinggi didapatkan dengan panjang serat 3 cm yaitu 36,98 Mpa dengan nilai kemuluran 5,15%. Dari hasil uji kerapatan, panjang serat 3 cm memiliki kerapatan yang paling tinggi yaitu sebesar 0,96 gr/cm3 dan daya serap air sebesar 1,28 % (2 jam), 2,63% (24 jam).

Kata Kunci : Polipropilena, PP-g-MA, Serat daun nenas, Sifat mekanik dan fisik

(2)

THE INFLUENCE OF FIBER LENGTH ON MECHANICAL AND PHYSICAL PROPERTIES OF COMPOSITE POLYPROPYLENE

-POLYPROPILENE GRAFTED MALEIC ANHYDRIDE- PINEAPPLE LEAF FIBER THAT

HAS BEEN ALKALIZED

ABSTRACT

The research about determined the mechanical and physical properties of polypropylene, polypropylene grafted maleic ahydride (PP-g-MA), and pineapple leaf fibre with weight variation polypropylene, PP-g-MA and fiber length. Tensile strength tested based on ASTM D-638. Pineapple leaf fiber has been soaked in 5% NaOH for 1 hour, and the arranged pinneapple fiber was same direction of the specimen. Variations of weight PP: PP-g-MA: pineapple fibers used such as 8:1:1, 7:2:1, 6:3:1, 5:4:1, 4:5:1. The highest tensile strength obtained on ratio 8:1:1 was 34.57 Mpa and strain value 4.15%. The density test ratio 8:1:1 has the highest and the lowest of water absorption test was 0,95 gr/cm3 and 1,32% (2 hours), 1,33% (24 hours). On variation of fiber length 1, 2, 3, 4, 5 cm weight ratio polypropylene, PP-g-MA was used a maximum tensile strength of variation polypropylene and PP-g-MA was 8:1:1. The highest tensile strength was obtained by fiber length 3 cm was 36.98 MPa with strain value 5.15%. The density test, fiber length 3 cm has the highest density was 0,96 gr/cm3 and the water absorption was 1,28% (2 hours) and 2,63% (24 hours).

Keywords : Mechanical and Physical properties, Pineapple leaf fibre, Polypropylene, PP-g-MA,

Referensi

Dokumen terkait

2.Melafalkan huruf hijaiyah berharakat secara berulang sampai pengucapannya benar secara individu,kelompok maupun klasikal,. 3.Mendemonstrasikan pelafalan huruf

[r]

• DALAM BENTUK LISAN, TULISAN, DIAGRAM, BAGAN, GAMBAR ATAU

Alamat : Mancagahar Ds.Mancagahar Kec.Pameungpeuk Kab.garut Telah mengajukan pindah ke salah satu sekolah:. Nama : Sekolah Dasar Negeri

FNNs (one for source language and the other for target language) to learn bilingual word embeddings so as to make sure that a source word is close to its correct translation in

Dari fenomena-fenomena tersebut peneliti akan melakukan penelitian yang lebih dalam tentang Perilaku Pro-Sosial Mahasiswa Psikologi UNNES ditinjau dari tipe kepribadian introvert

Dalam usaha untuk memperlancar arus barang atau jasa dari produsen ke konsumen, maka salah satu faktor penting yang tidak boleh diabaikan adalah memilih secara

Tujuan penelitian ini adalah untuk mengetahui apakah ada pengaruh dukungan sosial keluarga terhadap craving pada mantan pengguna narkoba.. Populasi penelitian ini adalah mantan