3
ABSTRACT
CHRISTINE ANASTASIA TARIGAN: Variation of Particle Size and
Composition of Urea Formaldehyde - Styrofoam against the Quality of Particle Board Made from Waste Oil Palm Trunks. Supervised by TITO SUCIPTO and RUDI HARTONO.
The waste of oil palm trunks could be used as raw materials for particleboards. The purpose of these study were to evaluate the physical and mechanical properties, the resistance of particle board against termite attack and evaluate the best composition of UF – styrofoam. The treatment variation were particle size (20, 35 and 50 mesh) and comparison of adhesive content between urea formaldehyde and styrofoam (60:40 ; 70:30 : 80:20 : 90:10). Board were made with size 25 cm x 25 cm x 1 cm with a target density of 0.7 gr/cm2 and press 25 kg/cm2 for 10 minute. The results would be compared by SNI 03-2105-2006. It showed that density, moisture content, water absorption, thickness swelling, modulus of elasticity, modulus of rupture and internal bond, were 0.52-0.60 g/cm3;10.04-11.19%;51.0-175.1%;8.6-24.3%;2005-4235kg/cm2;13-41kg/cm2 ;0.6-2.1 kg/cm2 respectively. Physical properties (density and moisture content) fullfilled the standard SNI 03-2105-2006, the thickness swelling were not fullfilled the standard. All of MOE and MOR properties didn’t fullfill the standard, and for Internal Bond only 2 board that fullfilled standard that is board with comparison of UF: SF = 90:10 by 20 mesh particle size, and comparison 90:10 by 35 mesh particle size. The best combination of particle size is 20 mesh and comparison of UF adhesive: styrofoam is 90:10.
Keywords: oil palm trunks, particleboard, particle size, urea formaldehyde, styrofoam
4
ABSTRAK
CHRISTINE ANASTASIA TARIGAN: Variasi Ukuran Partikel dan Komposisi Perekat Urea Formaldehida – Styrofoam terhadap Kualitas Papan Partikel dari Limbah Batang Kelapa Sawit. Di bawah bimbingan TITO SUCIPTO dan RUDI HARTONO.
Limbah batang kelapa sawit dapat digunakan sebagai bahan baku papan partikel. Tujuan dari penelitian ini adalah untuk mengevaluasi pengaruh ukuran partikel dan komposisi UF - styrofoam terhadap sifat fisis, mekanis dan ketahanan papan partikel terhadap serangan rayap tanah dan untuk memperoleh komposisi UF – styrofoam terbaik. Variasi perlakuan adalah ukuran partikel (20, 35 dan 50 mesh) dan perbandingan perekat urea formaldehida : styrofoam (60:40 ; 70:30 : 80:20 : 90:10). Papan dibuat berukuran 25 cm x 25 cm x 1 cm dengan target kerapatan 0,7 gr/cm3 dan tekanan 25 kg/cm2 selama 10 menit. Hasil penelitian akan dibandingkan dengan SNI 03-2105-2006. Hasil penelitian menunjukkan bahwa nilai kerapatan, kadar air, daya serapan air, pengembangan tebal, modulus elastis, modulus patah dan keteguhan rekat internal berturut-turut ialah 0,52-0,60 g/cm3 ; 10,04-11,19% ; 51,0-175,1% ; 8,6-24,3% ; 2005–4235 kg/cm2 ; 13–41 kg/cm2, 0,6-2,1 kg/cm2. Sifat fisis (kerapatan, kadar air) telah memenuhi standar SNI 03-2105-2006, pengembangan tebal tidak satupun memenuhi standar. Seluruh pengujian MOE dan MOR belum memenuhi standar dan untuk keteguhan rekat internal hanya 2 papan saja yang memenuhi standar yaitu papan dengan perlakuan perbandingan UF:SF = 90:10 dengan ukuran partikel 20 mesh dan perbandingan 90:10 dengan ukuran partikel 35 mesh. Kombinasi terbaik antara ukuran partikel adalah 20 mesh dan perbandingan komposisi perekat dengan styrofoam adalah 90: 10.
Kata kunci: batang kelapa sawit, papan partikel, ukuran partikel, urea formaldehida, styrofoam